Novel potassium perchlorate paper firing line for firecrackers

A technology of potassium perchlorate and fuse, applied in fuzes, inorganic oxyhalogen salt explosive compositions, offensive equipment, etc., can solve problems such as explosions and paper fuse safety hazards, and achieve simple manufacturing process, convenient material acquisition, and fast moisture dissipation Effect

Inactive Publication Date: 2011-02-16
陕西省蒲城县新型花炮技术推广中心
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since potassium chlorate itself has the characteristics of high friction sensitivity and high impact sensitivity, the impact sensitivity and friction sensitivity are both as high as 95%, and some even reach 100%, which leads to a large safety hazard in the prod

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel potassium perchlorate paper firing line for firecrackers
  • Novel potassium perchlorate paper firing line for firecrackers
  • Novel potassium perchlorate paper firing line for firecrackers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] In this embodiment, the ignition powder in the paper fuse is composed of the following raw materials in mass percentage: 58% potassium perchlorate, 29% hemp charcoal, and 13% magnesium oxide.

[0024] The manufacturing process includes the following steps:

[0025] (1) The hemp stalk charcoal and magnesium oxide are uniformly mixed by a drug mixer according to the above mass percentage, and then uniformly mixed together with potassium perchlorate to obtain pyrophoric powder.

[0026] (2) Twist the igniting powder in step (1) into a semi-finished paper igniting wire with a rubbing machine and lead paper, and the consumption of igniting powder is 0.8 jin to 1.2 jin of igniting powder / 1 kilometer of igniting paper.

[0027] (3) The semi-finished paper fuse in the step (2) is pulp drawn, after the pulp is drawn, it is air-dried, cut and drawn, and inverted to obtain the finished paper fuse.

[0028] In the present embodiment, the consumption of igniting powder is 1 jin of ...

Embodiment 2

[0030] In this embodiment, the ignition powder in the paper fuse is composed of the following raw materials in mass percentage: 53% potassium perchlorate, 34% hemp charcoal, and 13% magnesium oxide.

[0031] In the present embodiment, the consumption of igniting powder is 0.8 jin of igniting powder / 1 kilometer of wire paper. The glue used in the pulping process is made of resin glue and water after being uniformly stirred, and the mass percentages of the resin glue and water are: 0.8% of resin glue and 99.2% of water.

[0032] The manufacturing process of the novel potassium perchlorate paper fuse for firecrackers in the present embodiment is identical with embodiment 1.

Embodiment 3

[0034] In this embodiment, the ignition powder in the paper fuse is composed of the following raw materials in mass percentage: 63% potassium perchlorate, 24% hemp charcoal, and 13% magnesium oxide.

[0035] In the present embodiment, the consumption of igniting powder is 1.2 jin of igniting powder / 1 kilometer of wire paper. The glue used in the pulping process is made of resin glue and water after being uniformly stirred, and the mass percentages of the resin glue and water are: resin glue 1.2%, water 98.8%.

[0036] The manufacturing process of the novel potassium perchlorate paper fuse for firecrackers in the present embodiment is identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel potassium perchlorate paper firing line for firecrackers. Firing powders of the paper firing line are made of potassium perchlorate, hemp stem carbon and magnesium oxide by mass percent. The production process comprises the following steps of: uniformly mixing the hemp stem carbon with the magnesium oxide by adopting a mixing machine by mass percent, and then uniformly mixing with the potassium perchlorate to obtain the firing powders; twisting the firing powders in the step one with firing line paper into a semi-finished paper firing line by adopting a firing line twisting machine, wherein the usage of the firing powders is 0.8 catty to 1.2 catties firing powders/1 kilometer firing lines; and starching the semi-finished paper firing line of the step 2, and air drying, cutting and pouring disks after starching to prepare the finished paper firing line. The invention has the advantages of stable performance, safe and reliable production and transport, simple production process, high burning rate, low rate of moisture absorption, low friction sensitivity and low impact sensitivity, and the performance and the selected materials are all in line with standards in China.

Description

technical field [0001] The invention belongs to the technical field of fireworks and firecrackers, in particular to a novel potassium perchlorate paper fuse for firecrackers. Background technique [0002] The production of firecrackers has a history of hundreds of years in my country, and the production of paper fuses has long been in the manual production of family workshops, and it has only developed into mechanical production without isolation and close-range operation in recent years. The paper fuse in the prior art is usually prepared by mixing potassium chlorate and miscellaneous charcoal according to a certain ratio, and the glue used during pulping is polyvinyl alcohol resin. Since potassium chlorate itself has the characteristics of high friction sensitivity and high impact sensitivity, the impact sensitivity and friction sensitivity are both as high as 95%, and some even reach 100%, which leads to a large safety hazard in the production and transportation of paper ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C06B29/12C06C5/00
Inventor 王余粮杨世均
Owner 陕西省蒲城县新型花炮技术推广中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap