Surface sizing agent for corrugated paper as well as preparation method and application thereof

A surface sizing agent and corrugated paper technology, applied in the direction of water repellent addition, etc., can solve the problems of large amount of sizing agent, difficult to improve the grade, poor paper strength, etc., to improve the surface ring compressive strength, improve the Cobb value, The effect of accelerating the ripening speed

Active Publication Date: 2011-04-13
SHANGHAI DONGSHENG NEW MATERIALS
View PDF7 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 2) Use waste paper instead of wood pulp, but the strength of the paper is poor and the water absorption value is high
[0005] 3) Due to the many variable factors of internal sizing, the paper quality is unstable and the grade is difficult to improve, which makes manufacturers use less or give up internal sizing and use surface sizing to make up for it has become a popular t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surface sizing agent for corrugated paper as well as preparation method and application thereof
  • Surface sizing agent for corrugated paper as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0042] Example 1

[0043] 1. Preparation of surface sizing agent base material for corrugated paper:

[0044] In a 1000ml four-necked flask equipped with a condenser, a dripping device, a stirrer and a thermometer, add 20 grams of gelatin with a molecular weight of 10000g / mol and 214.5 grams of deionized water. The temperature is raised to 85°C to dissolve, and the temperature is lowered to 45°C. Add 2 g of 25wt% octadecyl polyoxyethylene (15) trimethylammonium chloride aqueous solution, heat to 95°C, add 1.5 g of 20wt% ammonium persulfate aqueous solution, and add dropwise the following mixed monomers: 100 g of styrene, 3 grams of dimethylaminoethyl acrylate monochloromethane quaternary ammonium, 1 gram of N-butoxymethacrylic acid, and 20 grams of n-butyl acrylate. The addition is completed in 1 hour. The reaction was maintained at 95°C for 1 hour, cooled to 35°C, and pH=2.0. It was filtered through a 100-mesh filter to obtain a surface sizing agent b...

Example Embodiment

[0051] Example 2

[0052] 1. Preparation of surface sizing agent base material for corrugated paper:

[0053] In a 2000ml four-necked flask equipped with a condenser, a dripping device, a stirrer and a thermometer, add 50 grams of gelatin with a molecular weight of 100000 g / mol and 808 grams of deionized water. The temperature is raised to 85°C to dissolve, and the temperature is reduced to 45°C. Add 20g of 10wt% dodecylpolyoxyethylene (20) trimethylammonium chloride aqueous solution, 4g of 50wt% potassium persulfate aqueous solution, and drop the following mixed monomers: 100g methyl styrene, methacrylic acid 8 grams of acyloxyethyl trimethyl ammonium chloride, 5 grams of divinylbenzene, 40 grams of isooctyl methacrylate, the addition is completed in 6 hours. The reaction was maintained at 40°C for 2 hours, then cooled to 25°C, pH=5.85. Filtered through a 100-mesh filter to obtain a surface sizing agent base material for corrugated paper with a solid ...

Example Embodiment

[0060] Example 3

[0061] 1. Preparation of surface sizing agent base material for corrugated paper:

[0062] In a 1000ml four-necked flask equipped with a condenser, a dripping device, a stirrer and a thermometer, 35 grams of gelatin with a molecular weight of 80,000 g / mol and 395.3 grams of distilled water were added, and the temperature was raised to 85°C to dissolve. Cool down to 45°C. Add 10g of 10wt% tetradecyl polyoxyethylene (8) trimethylammonium chloride aqueous solution, heat to 60°C, add 5g of 20wt% sodium persulfate aqueous solution, drop the following mixed monomers: 100g styrene, 5 grams of diallyl dimethyl ammonium chloride, 3 grams of amino ethyl acrylate, and 30 grams of methyl methacrylate. Add up in 4 hours. The reaction was maintained at 60°C for 2 hours, cooled to 35°C, and pH=3.5. It is filtered through a 100-mesh filter to obtain a surface sizing agent base material for corrugated paper with a solid content of 30.2 wt%.

[0063] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a surface sizing agent for corrugated paper as well as a preparation method and application thereof. The surface sizing agent for the corrugated paper comprises the following components in parts by weight: 100 parts of base stocks of the surface sizing agent for the corrugated paper and 5-10 parts of cationic additives, wherein the cationic additives are emulsified materials formed by stearic acids and cationic emulsifiers. The surface sizing agent for the corrugated paper is a high-performance environmental-friendly product which can meet the requirements for surface sizing of paper sheets; the product carries out the surface sizing on raw corrugated paper with starch together, thereby not only improving the Cobb value of the corrugated paper and accelerating the curing speed, but also greatly enhancing the surface ring crush strength of the corrugated paper and reducing the using amount of the starch; and in addition, the invention can be suitable for the need of the development of the high-strength corrugated paper.

Description

technical field [0001] The invention relates to a surface sizing agent for corrugated paper and a preparation method thereof. Background technique [0002] The development trend of paper, especially corrugated paper and cardboard is as follows: [0003] 1) It is developing from high grammage to low grammage. [0004] 2) Use waste paper instead of wood pulp, but the strength of the paper is poor and the water absorption value is high. [0005] 3) Due to the unstable quality of paper caused by many variable factors in internal sizing, and the difficulty of improving the grade, it has become a popular trend for manufacturers to use less or abandon internal sizing and use surface sizing to make up for it. [0006] Requirements for the sizing agent used for the above-mentioned surface sizing: a) increase the ring compressive strength; b) greatly reduce the Cobb value (water absorption value); c) fast curing speed, and it is required to be cooked immediately after getting off th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H21/16
Inventor 施晓旦尹东华王养臣
Owner SHANGHAI DONGSHENG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap