Natural rubber composite with electromagnetic shielding property and preparation method thereof
A technology of natural rubber and composite materials, applied in the field of electromagnetic shielding materials, can solve problems such as unsuitable for large-scale popularization and application, high manufacturing cost, complicated process, etc., and achieve excellent electromagnetic wave absorption performance, low manufacturing cost, and simple preparation method.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0017] Example 1
[0018] Fully disperse the chopped carbon fiber in a beating machine, filter the dispersion and fully dry it to obtain a chopped dispersed carbon fiber monofilament with a fiber diameter of 3μm and a length of 1mm; in an internal mixer or mill, first 100 parts by weight of natural rubber are masticated for 5 minutes, and then 2 parts stearic acid, 5 parts zinc oxide, 1 part antioxidant, 60 parts carbon black, 3 parts chopped carbon fiber, 3 parts paraffin oil, 1 part Parts accelerator and 2.5 parts sulfur, then mix for 8 minutes, mix evenly and press tablets to obtain a rubber mixture; park the rubber mixture at room temperature for 24 hours, and then vulcanize and shape on a 50T flat vulcanizer under a vulcanization condition of 140 ℃×30min, get the product.
[0019] After performance testing, the tensile strength of the electromagnetic shielding natural rubber composite material is 14MPa, and the electromagnetic shielding efficiency is 62.3-75.6dB under the con...
Example Embodiment
[0020] Example 2
[0021] Fully disperse the chopped carbon fiber in a beating machine, filter the dispersion and fully dry it to obtain a chopped carbon fiber monofilament with a fiber diameter of 6μm and a length of 3mm; in an internal mixer or mill, first 100 parts by weight of natural rubber are masticated for 5 minutes, and then 2 parts by weight of stearic acid, 5 parts of zinc oxide, 1 part of antioxidant, 60 parts of carbon black, 7 parts of chopped carbon fiber, 3 parts of paraffin oil, 1 part Parts accelerator and 2.5 parts sulfur, then mix for 8 minutes, mix evenly and press tablets to obtain a rubber mixture; park the rubber mixture at room temperature for 24 hours, and then vulcanize and shape on a 50T flat vulcanizer under a vulcanization condition of 140 ℃×30min, get the product.
[0022] After performance test, the tensile strength of the electromagnetic shielding natural rubber composite material is 15MPa, and the electromagnetic shielding efficiency is 68.2-82.4d...
Example Embodiment
[0023] Example 3
[0024] Fully disperse the chopped carbon fiber in a beating machine, filter the dispersion and fully dry it to obtain a chopped dispersed carbon fiber monofilament with a fiber diameter of 10μm and a length of 5mm; in an internal mixer or mill, first 100 parts by weight of natural rubber is masticated for 5 minutes, and then 2 parts by weight of stearic acid, 5 parts of zinc oxide, 1 part of antioxidant, 60 parts of carbon black, 11 parts of chopped carbon fiber, 3 parts of paraffin oil, 1 part Parts accelerator and 2.5 parts sulfur, then mix for 8 minutes, mix evenly and press tablets to obtain a rubber mixture; park the rubber mixture at room temperature for 24 hours, and then vulcanize and shape on a 50T flat vulcanizer under a vulcanization condition of 140 ℃×30min, get the product.
[0025] After performance test, the tensile strength of the electromagnetic shielding natural rubber composite material is 16MPa, and the electromagnetic shielding efficiency is...
PUM
Property | Measurement | Unit |
---|---|---|
Tensile strength | aaaaa | aaaaa |
Electromagnetic shielding effectiveness | aaaaa | aaaaa |
Tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap