Water-based printing ink emulsion for plastic foil, and preparation method thereof

A water-based ink and plastic film technology, applied in inks, applications, household appliances, etc., can solve the problems of technical capability limitations, water-based ink emulsions cannot achieve plastic film bonding, and limit the development of water-based inks, etc. Good leveling effect

Inactive Publication Date: 2011-09-21
上海奇想青晨新材料科技股份有限公司
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, due to the limitation of technical capabilities, many water-based ink emulsions cannot achieve good bonding with plastic films, and water-based inks are mostly used for paper
Limit the development of water-based ink

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Embodiment 1 (unit: kilogram)

[0032] formula:

[0033] Reactor:

[0034] 1. Demineralized water 180 Alcohol ether succinate sodium salt 2 Ammonium bicarbonate 0.2

[0035] Sodium bicarbonate 0.3

[0036] 2. Demineralized water 17 Sodium thiosulfate 4

[0037] Pre-emulsification kettle:

[0038] 3. Demineralized water 115 Alcohol ether succinate sodium salt 5 Ammonium bicarbonate 0.2

[0039] 4. Butyl methacrylate 108 Ethyl acrylate 140 Methyl methacrylate 150

[0040] Diacetone acrylamide 10

[0041] 5. Demineralized water 8 Diacetone acrylamide 2

[0042] 6. Demineralized water 18 Sodium thiosulfate 4

[0043] 7. Mineral oil 1

[0044] 8. OT-75 3

[0045] 9. Water-soluble acrylic resin 10

[0046] 10. Ammonia 8

[0047] Steps:

[0048] Prepare the bottom liquid 1 in the reaction kettle in order, then start stirring to raise the temperature to 88°C; start the stirring in the pre-emulsification kettle, prepare the bottom liquid 3 in the pre-emulsification ...

Embodiment 2

[0049] Embodiment 2 (unit: kilogram)

[0050] formula:

[0051] Reactor:

[0052] 1. Demineralized water 200 Alcohol ether succinate sodium salt 2 Ammonium bicarbonate 0.2

[0053] Sodium bicarbonate 0.3

[0054] 2. Demineralized water 17 Sodium thiosulfate 4

[0055] Pre-emulsification kettle:

[0056] 3. Demineralized water 95 Alcohol ether succinate sodium salt 5 Ammonium bicarbonate 0.2

[0057] 4. Butyl methacrylate 113 Ethyl acrylate 140 Methyl methacrylate 160

[0058] Diacetone acrylamide 9

[0059] 5. Demineralized water 8 Diacetone acrylamide 2

[0060] 6. Demineralized water 18 Sodium thiosulfate 4

[0061] 7. Mineral oil 1

[0062] 8. OT75 3

[0063] 9. Water-soluble acrylic resin 10

[0064] Steps

[0065] Prepare the bottom liquid 1 in the reaction kettle in order, then start stirring to raise the temperature to 88°C; start the stirring in the pre-emulsification kettle, prepare the bottom liquid 3 in the pre-emulsification kettle; then add monomer 4 i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-based printing ink emulsion for a plastic foil. The emulsion is prepared by the reaction among butyl methacrylate, ethyl acrylate, methyl methacrylate, diacetone-acryloamide, sodium hyposulfite, alcohol ether sodium succinate, a buffering agent, a functional auxiliary agent, ammoniacal liquor and softened water. A preparation method in the invention is also disclosed. According to the invention, the water-based printing ink emulsion enables a large bonding intensity for the plastic foil, and has the advantages of good levelability, aging resistance, no poison, no smell, safety and reliability.

Description

technical field [0001] The invention relates to a water-based ink emulsion used for plastic films and a preparation method thereof. Background technique [0002] Water-based ink emulsion for plastic film is used to prepare water-based ink. It acts as a binder in the ink, bonding the pigments in the ink to each other as a whole, and tightly bonding with the plastic film. [0003] In the past, inks were mostly oily systems, which were easy to bond with plastic films, but a large amount of solvent volatilized, on the one hand, it caused great environmental pollution and harm to the health of operators, and on the other hand, it was very easy to cause fire. With the improvement of human health awareness. Water-based systems are getting more and more attention, but water is a polar material, and it is difficult to bond with non-polar plastic films. Therefore, the adhesion between water-based ink emulsions and plastic films is the key to the use of water-based inks. [0004] At ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/10C09J133/08C09J133/12C09D11/10C09D11/107
Inventor 刘国富赵永旗夏宇正戚向东
Owner 上海奇想青晨新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More