Composite structured colored contact lens

A contact lens and composite structure technology, applied in the directions of glasses/goggles, optics, instruments, etc., can solve the problems of uneven surface, foreign body sensation when the patient is wearing, low biocompatibility of contact lenses, etc., to achieve biocompatibility Good, high safety performance, good practical effect

Inactive Publication Date: 2011-09-28
SOUTHEAST UNIV
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a composite structural color contact lens, which solves the problems of low biocompatibility of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite structured colored contact lens
  • Composite structured colored contact lens
  • Composite structured colored contact lens

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The preparation of embodiment 1 composite structural color contact lens

[0041] Such as figure 1 and figure 2As shown, the composite structural color contact lens includes a contact lens body 1, and the outside of the contact lens body 1 is uniformly solidified with a structural color colloidal crystal solution polymer of a single color or a mixed color as a structural color region. The structural color area includes the pupil area 11 and the iris area 12 formed by the outward protrusion of the contact lens body 1; the pupil area 11 is a colorless and transparent area; the iris area 12 is a uniform single color or mixed color structure Structural colored regions formed by solidification of chromatic colloidal crystal solution polymers. The structural color colloidal crystal polymer solution is methyl methacrylate, polyhydroxyethyl methacrylate, cellulose acetate butyrate, siloxane methacrylate, fluorosilicon methacrylate, perfluoroether, N - Any mixture of one or m...

Embodiment 2

[0051] The preparation of embodiment 2 composite structural colored contact lenses

[0052] The raw material formula is as follows:

[0053]

[0054] 1. Preparation of structural color colloid solution:

[0055] Configure two kinds of structural color colloidal solutions, and add monodisperse colloidal silica nanoparticles with a diameter of 200 nanometers into a mixed solution of hydroxyethyl methacrylate (HEMA) and ethylene glycol dimethacrylate (EGDMA), adjust The mass percent of silicon dioxide is 40% and 60%, ultrasonic dispersion, all produces bright and bright structural color until two kinds of colloidal particle solutions; In this solution, add initiator azoisodibutylcyanide (0.1%, mass volume ratio), after fully mixing, pass through nitrogen gas for 5 minutes, and seal the structural color colloid solution for later use.

[0056] 2. Curing treatment of structural color solution in the mold:

[0057] Firstly, a 100 microliter volume of structural color colloid s...

Embodiment 3

[0060] The preparation of embodiment 3 composite structural colored contact lenses

[0061] The raw material formula is as follows:

[0062]

[0063] 1. Preparation of structural color colloid solution:

[0064] Configure two kinds of structural color colloidal solutions, and add monodisperse silica colloidal nanoparticles with a diameter of 200 nanometers into a mixed solution of siloxane methacrylate (SMA) and ethylene glycol dimethacrylate (EGDMA), Regulate the mass percent of silicon dioxide to be 40% and 60% respectively, and ultrasonically disperse until the two colloidal particle solutions all produce bright and bright structural colors; add initiator azoisodibutylcyanide (0.1%, Mass to volume ratio), after fully mixing, pass through nitrogen gas for 5 minutes, and seal the structural color colloid solution for later use.

[0065] 2. Curing treatment of structural color solution in the mold:

[0066] Firstly, a 100 microliter volume of structural color colloid sol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite structured colored contact lens which comprises a contact lens body (1); and the composite structured colored contact lens is characterized in that a uniform single-colored or mixed-colored structural colour colloidal crystal solution polymer serving as a structural colour area is cured at the outside of the contact lens body (1). Compared with other contact lenses, the composite structured colored contact lens disclosed by the invention is more beautiful, good in biocompatibility and good in practicability.

Description

technical field [0001] The invention belongs to the technical field of contact lens material research, in particular to a compound structural colored contact lens. Background technique [0002] In the past 30 years, the total number of people wearing contact lenses in the world has increased by 35 times, and colored contact lenses have gradually become popular due to the drive of the global fashion industry. According to incomplete statistics, my country's colored contact lenses currently account for more than 35% of the contact lens market. [0003] Colored contact lenses can be divided into two categories: the first category is a contact lens with transparent or opaque colored patterns only in the iris area of ​​the contact lens, which can reveal special colors and patterns in the iris area of ​​the contact lens; the second category Colored contact lenses use transparent colors to enhance the color of contact lenses. This basically transparent coloring material is evenly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G02C7/04C08F230/08C08J9/26C08F220/28
Inventor 顾忠泽赵远锦金露谢卓颖叶宝芬
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap