Method for producing steel for high-efficiency alloy welding wires through continuous billet casting

A technology of billet continuous casting and alloy welding wire, which is applied in the direction of welding medium, welding equipment, metal processing equipment, etc., to achieve the effect of improving the yield, inhibiting the agglomeration of mold slag, and stabilizing the absorption rate of the alloy

Active Publication Date: 2011-10-12
BEIJING SHOUGANG CO LTD
View PDF1 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the titanium content increases above 0.17%, the above-mentioned defects will still occur frequently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing steel for high-efficiency alloy welding wires through continuous billet casting
  • Method for producing steel for high-efficiency alloy welding wires through continuous billet casting
  • Method for producing steel for high-efficiency alloy welding wires through continuous billet casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The present invention can be implemented in iron and steel production plants with LF, RH external refining equipment and full protection casting conditions. The following table 2 to table 6 have listed the time when Shougang Qiangang Company adopts the present invention to produce titanium-containing high-efficiency alloy welding wire steel Examples of key parameters of the production process.

[0028] Table 2 Key parameters of converter process

[0029]

[0030] Table 3 Key parameters of LF refining process

[0031]

[0032] Table 4 Key parameters of RH refining process

[0033]

[0034] Table 5 Key parameters of continuous casting process

[0035]

[0036] Table 6 Control level of finished product ingredients

[0037]

[0038]High-efficiency alloy welding wire is mainly used for automatic gas shielded welding, especially for robotic automatic welding. Therefore, the surface quality of the welding wire is required to be excellent, and the production p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for producing steel for high-efficiency alloy welding wires through continuous billet casting, belonging to the technical field of steel making. The method comprises the following processes: providing low-sulfur molten iron and scrap steel; smelting in a top / bottom blowing converter; pulling off slag and tapping; deoxidizing the ladle; alloying the molten steel; carrying out LF (Ladle Furnace) refining; carrying out RH (Ruhrstahl Heraeus) refining; carrying out fully-protected continuous casting by a continuous billet casting machine; and checking the cast billets, wherein the key processes comprise the end point control during converter smelting, the dose of deoxidizer, the control on the oxygen activity of the molten steel in the production process, the control on the top slag during LF refining, the denitriding effect during RH refining, the regulation of sulfur and titanium contents in the refining process, the effect of protected casting and the like. The method is characterized by controlling oxygen and nitrogen contents in the molten steel through various process measures in the smelting process, thereby achieving the purpose of controlling the reaction of titanium with oxygen and nitrogen, and reducing the possibilities that a submerged nozzle is blocked and crystallizer protecting slag is agglomerated. By using the method, the steel for high-efficiency alloy welding wires, of which the titanium content is 0.15-0.22%, can be stably produced.

Description

technical field [0001] The invention belongs to the technical field of steelmaking, and in particular provides a production method of billet continuous casting high-efficiency alloy welding wire steel, which is suitable for the production of a class of titanium-containing high-efficiency alloy welding wire steel, and can replace die casting and bloom Production method of continuous casting. Background technique [0002] At present, the technology of various industries is developing towards high energy efficiency and high efficiency, and the welding technology widely used in various industries plays an important role in promoting the development of the industry, the technological progress of products and the development of the national economy. . In the field of welding materials, Japanese researchers have developed a low-splash gas shielded arc welding wire containing an appropriate amount of titanium. The titanium content of the finished product ranges from 0.12-0.25%, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/14C22C33/04B23K35/32
Inventor 朱殷翔靳伟李明王立峰陈涛魏建全
Owner BEIJING SHOUGANG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com