Synthesis method of monoclinic crystal phase rare-earth iso-oxy-sulfur superfine nanowire and wire-based superstructure

A technology of ultra-fine nanometer and synthesis method, which is applied in the direction of chemical instruments and methods, single crystal growth, single crystal growth, etc. It can solve the problems of weak S affinity, difficulty in obtaining Ln, and reduced lattice symmetry, etc., and achieve good results. Luminous performance, good universality, efficient development and application effects

Inactive Publication Date: 2012-10-24
NANJING NORMAL UNIVERSITY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The reason may be that the ionic radii of O and S are different. Rare earth ions have a strong affinity for O, but a relatively weak affinity for S. It is easy to obtain Ln2 in water system or oxygen-rich environment. O3 or Ln2O2S, it is more difficult to get Ln2OS 2
Compared to Ln2O2S, the proportion of S atoms in Ln2OS2 increases, resulting in Its lattice symmetry is drastically reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthesis method of monoclinic crystal phase rare-earth iso-oxy-sulfur superfine nanowire and wire-based superstructure
  • Synthesis method of monoclinic crystal phase rare-earth iso-oxy-sulfur superfine nanowire and wire-based superstructure
  • Synthesis method of monoclinic crystal phase rare-earth iso-oxy-sulfur superfine nanowire and wire-based superstructure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Add 0.20~6.0g Y(NO 3 ) 3 6H 2 O solid, 0.10-4.50 g thiourea solid, 2-10 mL oleic acid (Aldrich, 90%), 2-10 mL dodecylamine (Alfa Aesar, 98%), and 5-20 mL octadecene (Alfa Aesar , 90%), sealed the reactor and transferred it to an oven, and raised it from room temperature to 180 °C at a rate of 4 °C / min. After 24 h of reaction, the temperature was naturally cooled to room temperature. To obtain a light brown jelly, add n-heptane, heat slightly, then add ethanol to precipitate, and centrifuge to separate the solid. Then the initial product was washed with a mixed solvent of n-heptane / absolute ethanol (volume ratio: 2 / 1), and a precipitate was obtained after centrifugation. Washing was repeated 3-5 times to obtain a light yellow-green solid product, and finally the washed product was vacuum-dried at 60°C for 4 h.

[0034] The dried product was collected, and its composition and phase were tested by X-Ray powder diffractometer (XRD). The results showed that the obta...

Embodiment 2

[0036] Add 0.2-6.0 g Gd(NO 3 ) 3 6H 2 O solid, 0.10-4.50g thiourea solid, 2-10 mL oleic acid, 2-10 mL dodecylamine and 5-20 mL octadecene, seal the reaction kettle and transfer it to an oven at 4 ℃ / min The rate was increased from room temperature to 180 °C. After 24 h of reaction, the temperature was naturally cooled to room temperature, and a light brown jelly was obtained. Add n-heptane, heat slightly, then add ethanol, and centrifuge to separate the solid. Then, the obtained primary product was washed with a mixed solvent of n-heptane / absolute ethanol (volume ratio: 2 / 1), and a precipitate was obtained after centrifugation. Washing was repeated 3-5 times to obtain a light yellow-green solid product, and finally the washed product was vacuum-dried at 60°C for 4 h. .

[0037] The dried product was collected, and its composition and phase were tested by X-Ray powder diffractometer (XRD), which showed that the obtained product was pure monoclinic crystal phase structu...

Embodiment 3

[0039] In a clean and dry reaction kettle (volume 50 mL) with polytetrafluoroethylene liner, add 0.2-6.0 g Dy(NO 3 ) 3 6H 2 O solid, 0.10-4.50g thiourea solid, 2-10 mL oleic acid, 2-10 mL dodecylamine and 5-20 mL octadecene, seal the reaction kettle and transfer it to an oven at 4 ℃ / min The rate was increased from room temperature to 200 °C, and after 24 h of reaction, the temperature was naturally cooled to room temperature. A light brown gum was obtained. Add n-heptane, heat slightly, then add ethanol, and centrifuge to separate the solid. Then, the obtained product was washed with a mixed solvent of n-heptane / absolute ethanol (volume ratio: 2 / 1), and a precipitate was obtained after centrifugation. The washing operation was repeated 3-5 times to obtain a light yellow-green solid product, and finally the washed product was vacuum-dried at 60 °C for 4 h.

[0040] The dried product was collected, and its composition and phase were tested by X-Ray powder diffractometer (XR...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lattice spacingaaaaaaaaaa
aspect ratioaaaaaaaaaa
Login to View More

Abstract

The invention discloses a synthesis method of monoclinic crystal phase rare-earth iso-oxy-sulfur Ln2OS2 (Ln=Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Dy, Ho, Er and Yb) superfine nanowire and nanowire-based superstructure, comprising the following steps of: heating rare-earth metal nitrate solid and thiourea solid to 180-200 DEG C for solid-liquid phase reaction in the mixed solvent consisting of fatty acid, fatty amine and octadecene, and separating out reaction products to prepare target products. The method adopts a solid-liquid phase chemical reaction route and replaces an organic metal compound with rare-earth nitrate solid, thereby controllably synthesizing a series of rare-earth iso-oxy-sulfur superfine nanowires and nano wire-based superstructures with high efficiency. The synthesis method has a simple and safe operation process and universality, and can implement large-scale preparation of the product.

Description

Technical field [0001] The present invention involves a synthesis method of a rare earth isoportonal sulfur nanoma, which specializes in a novel single -diaphragm -phase phase rare earthy oxygen sulfur (LN 2 OS 2 , LN = Y, LA, CE, PR, ND, SM, EU, GD, DY, HO, ER, YB) Ultra -fine nano -nano -line and nan navile base super structure. Background technique [0002] Dimensions and dimensions are two important geometric parameters that affect the physical and chemical properties of nanomaterials.Among various nano -structures, 1D nano wires (cylindrical structures with less diameter less than 100 nanometers) Due to the priority growth of radial height limit and axial priority, its electronic density is different from 0D, 2D and 3D nano structures, so it has it to haveDifferent from the unique physical and chemical properties of other nano structures, there are potential application prospects in the fields of electronics, catalytic, sensing, and environmental degradation. [0003] In rec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C30B29/46C30B29/62
Inventor 包建春韩敏郭培戴志晖许兰全袁丹
Owner NANJING NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com