Method for self-lubricating treatment of laser micro-texture of bearing

Abstract

The invention discloses a method for self-lubricating treatment of laser micro-texture of bearings. The invention comprises the following steps: firstly performing laser micro-processing technology of micro recessed cavities or micro grooves on a bearing surface, and then performing molding and bonding technology by a self-lubricating composite material on the bearing surface; the self-lubricating composite material comprises the following components by mass: 10-15% of polyimide (PI); 8-13% of graphite powder; 40-50% of polytetrafluoroethylene; 25-29% of MoS2; 0-5% of additives. By the self-lubricating treatment of laser micro-texture of a bearing, the invention guarantees the bearing capacity and the fitting accuracy of the bearing, realizes an optimized distribution of the lubricant on the bearing working surface, and improves comprehensive performance of antifriction and wear resistance of the bearing under complicated working conditions.

Description

technical field [0001] The invention relates to self-lubricating bearing technology, in particular to a self-lubricating compound treatment technology for bearing laser micro-modeling, which is used to solve the problem of bearing lubrication under special and complicated working conditions. Background technique [0002] At present, most metallurgical enterprises use traditional mechanical bearings lubricated by lubricating oil and grease. Due to long-term exposure to harsh environments such as high temperature, heavy load, impact, and dust, lubricating oil and grease are prone to failure. It requires a large amount of cooling water and lubricating grease during use, which not only causes great energy waste and pollutes the environment, Moreover, the use stability of the bearing is poor, and it is often damaged, so it is difficult to meet the normal requirements of production. At the same time, the grease-lubricated joint sliding bearings widely used in construction machine...

AI Technical Summary

Problems solved by technology

The whole layer coating and sintering method is adopted, and the thickness of the lubricating coating reaches 0.5-2.5 mm, which affects the matching accuracy and support rigidity of the bearing.

The patent published in 2009 (application number: 200810235590.0) discloses a three-layer self-lubricating sliding bearing structure. Due to the addition of a layer of porous copper powder sintering layer, the difficulty and cost of the process are greatly improved, and the improvement of machining accuracy is also limited.

This patent uses laser micromachining small holes to form silver...