Method for preparing autoclaved aerated building block with high tensile strength and low shrinking by using waste spinning flax materials

An autoclaved aerated, low-shrinkage technology, which is applied in the direction of manufacturing tools, solid waste management, and climate sustainability, can solve the problems of low tensile strength and large drying shrinkage of autoclaved aerated concrete blocks, and achieves Improvement of compressive strength, improvement of splitting strength and splitting ratio, and small shrinkage value

Inactive Publication Date: 2011-11-16
TONGLING FENGZE BUILDING MATERIALS TECH
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the autoclaved aerated concrete block itself has a large drying shrinkage value and a low tensile strength, which will easily cause a lot of inconvenience in practical applications.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The method for making high splitting pressure ratio and low shrinkage value autoclaved aerated block from textile waste hemp material of the present invention is characterized in that it comprises the following production steps:

[0010] (1) The raw materials are prepared for use first, and the SiO 2 %≥45%, fineness≤25%, loss≤10% fly ash (78%--90%), bottom slag (8-20%) and SO 3 ≥35% phosphogypsum (0.2-0.5%) is mixed to make a slurry and stored in a storage tank for use; the quicklime is ball-milled to 80 μm and the sieve residue is 8%--15%, and then input into the steel bin for use; the PI42. 5. The cement is transported into the factory by bulk truck and then pumped into the steel silo for use; the ramie waste with L≤2cm, good dispersion and no agglomeration phenomenon is processed by cutting and separation and stored in the silo for use; the aluminum powder paste On-site metering in bags;

[0011] (2) The prepared fly ash, bottom slag, phosphogypsum, ramie waste, ce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing an autoclaved aerated block with high tensile strength and low shrinking by using waste spinning flax materials. The method comprises the following steps: (1) preparing raw materials for standby, wherein the prepared raw materials comprises coal ash, furnace dregs, ardealite, waste ramie, concrete, lime, aluminum powder paste, additives and the like; (2) utilizing a PLC (programmable logic controller) system to add the prepared materials into a mixing blender for pouring, wherein the ratio of coal ash to furnace dregs to ardealite to concrete to lime is 59.67:10.53:3:5.5:21.3, the aluminum powder is 0.06%-0.07% of the total weight of dry materials and the waste ramie is 0.025%-0.04% of the total weight of dry materials; and stirring the raw materials, pouring the mixture into a mould, standing in a procuring chamber, cutting and forming by using a PLC turning cutter set, processing in an autoclaved kettle which takes pressure saturated steam as a medium to produce an environment-friendly autoclaved aerated block with high tensile strength and low shrinking.

Description

technical field [0001] The invention relates to a production method of building material aerated blocks. Background technique [0002] At present, most of the wall materials used in buildings are brick masonry, and clay bricks account for more than 80% of the total wall materials, occupying a large amount of cultivated land every year, and destroying the ecological balance. There are more than 100,000 brick and tile enterprises in the country, covering an area of ​​about 5 million mu, and destroying nearly 100,000 mu of land every year. The development of new wall materials is already a major issue involving the national economy and people's livelihood. [0003] In order to promote the in-depth development of the circular economy in our city, our company is actively based on local resources, and effectively utilizes local fly ash, slag, phosphogypsum, waste hemp and other waste residues to replace clay solid bricks and products at the cost of destroying land resources. It h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B28B1/00
CPCC04B28/18Y02W30/91C04B7/02C04B18/08C04B18/141C04B20/0048C04B20/0076C04B20/008C04B22/04C04B22/144C04B40/0071C04B40/024
Inventor 王东
Owner TONGLING FENGZE BUILDING MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products