Colorless transparent conductive ink as well as preparation method and application thereof

A transparent conductive ink technology, applied in applications, inks, household utensils, etc., can solve the problems of high cost of etching process, harsh requirements of magnetron sputtering environment, etc., and achieve good sprayability, short preparation cycle and good conductivity sexual effect

Active Publication Date: 2011-12-21
宁波森利电子材料有限公司
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Magnetron sputtering has strict requirements on the environment, and the cost of multiple etching processes is very high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colorless transparent conductive ink as well as preparation method and application thereof
  • Colorless transparent conductive ink as well as preparation method and application thereof
  • Colorless transparent conductive ink as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] (1) 9.27g of silver nitrate is added to the mixed solution of 10g of deionized water and 8g of ethanol. After sealing the beaker containing the solution with plastic wrap, the solution is placed in an ultrasonic cleaner for 3 minutes of ultrasonic oscillation to make the silver nitrate completely dissolved in the solvent;

[0047] (2) Under the condition of magnetic stirring, add ammonia water (NH 3 , analytically pure AR, Sinopharm Group Chemical Reagent Co., Ltd.) 18.5g, to obtain a clear solution, then add 1g of sodium potassium tartrate, and carry out magnetic stirring for 5min to obtain a solution;

[0048] (3) 0.5g polyacrylic acid [(C 3 h 4 o 2 ) n , the average molecular weight is 3000, Aladdin Reagent (Shanghai) Co., Ltd.] was added to the solution, magnetically stirred for 30 minutes, and the solution was filtered to obtain a colorless and transparent conductive ink. The viscosity of the colorless and transparent conductive ink at 20°C was 15mPa ·s, the s...

Embodiment 2

[0052] (1) Add 8.56g of silver nitrate to a mixture of 10g of deionized water and 4.8g of ethylene glycol methyl ether, seal the beaker containing the solution with plastic wrap, place the solution in an ultrasonic cleaner for 1 minute of ultrasonic Shake to completely dissolve the silver nitrate in the solvent;

[0053] (2) Under the condition of magnetic stirring, add ammonia water (NH 3 , analytically pure AR, Sinopharm Chemical Reagent Co., Ltd.) 17g to obtain a clear solution, then add 0.75g of glucose, and magnetically stir for 20min to obtain a solution;

[0054] (3) 0.15g polyvinylpyrrolidone k-30 [(C 6 h 9 NO) n , the average molecular weight is 58000, Sinopharm Group Chemical Reagent Co., Ltd.] was added to the solution, magnetically stirred for 20 minutes, and the solution was filtered to obtain a colorless and transparent conductive ink. The viscosity of the colorless and transparent conductive ink at 20°C was 25mPa·s , the surface tension at 20°C is 28.9mN / m, ...

Embodiment 3

[0058] (1) 4.26g silver nitrate was added to the mixed solution of 10g deionized water and 2.4g diethylene glycol, after sealing the beaker containing the solution with plastic wrap, the solution was placed in an ultrasonic cleaner for 3 minutes Ultrasonic vibration, so that the silver nitrate is completely dissolved in the solvent;

[0059] (2) Under the condition of magnetic stirring, add ammonia water (NH 3 , Analytical pure AR, Sinopharm Chemical Reagent Co., Ltd.) 7.5g to obtain a clear solution, then add 0.5g sucrose, and magnetically stir for 20min to obtain a solution;

[0060] (3) 0.25g polyvinylpyrrolidone k-90 [(C 6 h 9 NO) n , the average molecular weight is 1300000, Sinopharm Group Chemical Reagent Co., Ltd.] was added to the solution, magnetically stirred for 5 minutes, and the solution was filtered to obtain a colorless and transparent conductive ink. The viscosity of the colorless and transparent conductive ink at 20°C was 25mPa·s , the surface tension at 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Surface tensionaaaaaaaaaa
Graininessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a colorless transparent conductive ink. The ink is prepared from the following raw materials by weight percent: 12%-21% of silver salt, 36%-53% of solvent, 27%-43% of additive and 0.1%-2.1% of dispersant. The ink has the advantages of good spraying property, good reliability, good image quality and good safety and can be used in the common home piezoelectric ink jet printer to prepare an electric circuit; and the common flat-plate printer can be utilized to prepare silver conductive patterns on different substrates. The invention also discloses a preparation method of the colorless transparent conductive ink. The method comprises the following steps: placing the silver salt in the organic solvent, performing ultrasonic vibration for 1-5 minutes; and adding the additive under stirring, stirring for 5-20 minutes, then adding the dispersant, stirring for 5-30 minutes and filtering to obtain the colorless transparent conductive ink. The method has the advantages ofsimple preparation technology, mild reaction conditions, good controllability, short preparation period, low production cost and the like.

Description

technical field [0001] The invention relates to the field of conductive ink and its preparation, in particular to a colorless and transparent conductive ink and its preparation method and application. Background technique [0002] At present, the fabrication of conductive circuits by inkjet printing technology is a relatively popular and important application. In the process of using inkjet printing technology to prepare conductive circuits, the key technology is to prepare conductive ink suitable for inkjet printing. The performance indicators of conductive ink suitable for inkjet printing mainly include: (1) Sprayability: it is expressed as three indicators of ink particle size, viscosity and surface tension. Generally speaking, the particle size in the ink should be less than 1 μm, the viscosity should be 5-35 mPa·S, and the surface tension should be 10-50 mN / m. For different printers, these indicators of ink are also slightly different. (2) Reliability: no clogging of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D11/02H05K1/09C09D11/52
Inventor 宋伟杰黄琦金沈文锋
Owner 宁波森利电子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com