Method for preparing organic single crystal particle two-dimensional ordered structure and its patterned arrangement
A technology of single crystal particles and ordered structure, which is applied in the field of preparation of two-dimensional ordered structure of organic single crystal particles and its patterned arrangement, to achieve the effect of reversible, reversible repeatability and high repeatability of two-dimensional ordered structure
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0042] (1) Use a key to take a certain amount of 2,5,8,11-tetra-tert-butylperylene single crystal particles with a diameter of 2.5um orthorhombic dodecahedron into a serum bottle, and add a certain amount of deionized water;
[0043] (2) Place the serum bottle in an ultrasonic instrument and sonicate for 5 minutes to form a monodisperse system;
[0044] (3) Inject the dispersion system obtained in step (2) into a capacitor made of another two parallel conductive glass placed horizontally;
[0045] (4) Apply an electric field strength of 4.5×10 on the electrode 4 V / m, AC electric field with a frequency of 500Hz, placed for 5 minutes.
[0046] (5) While removing the AC electric field, apply a DC voltage of 10V to the electrode, remove the DC power after 2 seconds, and turn on the capacitor. The microscope dark field picture of the obtained structure is attached figure 1 shown.
Embodiment 2
[0048] According to the method of embodiment 1, the difference is that in this embodiment, in step 5, the alternating current electric field is withdrawn and the direct current is not applied at the same time, as figure 2 (a) shows the results obtained under the conditions of Example 1, such as figure 2 (b) shows the situation after maintaining no electric field for 10 seconds, such as figure 2 (c) is the case of applying an AC electric field for 30 seconds.
Embodiment 3
[0050] According to the method of Embodiment 1, the difference is that in this embodiment, the frequency of the AC electric field is changed to 500 Hz, 900 Hz and 1300 Hz respectively. The results obtained are as follows image 3 (a)- image 3 (c) shown.
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap