High-temperature colloid protecting anticaving fluid loss additive for drilling fluid and preparation method thereof

A technology of fluid loss control agent and drilling fluid, which is applied in the direction of chemical instruments and methods, drilling compositions, etc.

Inactive Publication Date: 2012-05-02
CHINA UNIV OF PETROLEUM (EAST CHINA)
View PDF6 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, foreign high-temperature colloidal stabilizers cannot meet the requirements of high-temperature rubber protection, and domestic high-temperature colloidal stabilizers have not been reported. Therefore, it is very important to develop a new type of water-based drilling fluid protection agent suitable for use under high-temperature conditions in deep wells. practical significance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature colloid protecting anticaving fluid loss additive for drilling fluid and preparation method thereof
  • High-temperature colloid protecting anticaving fluid loss additive for drilling fluid and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] An anti-slump and fluid loss reducing agent for high-temperature drilling fluid protection glue, the preparation method of which is as follows:

[0016] 1) Add 250 parts by weight of water into the reaction kettle, add 5 parts by weight of acrylamide and 40 parts by weight of 2-acrylamido-2-methylpropanesulfonic acid into the kettle, stir and dissolve so that the mass percentage concentration is 15% (two The sum of the solute concentrations, the same below), then add 3 parts by weight of acrylic acid and fully stir and dissolve;

[0017] 2) adding an aqueous potassium hydroxide solution with a mass percentage concentration of 20%, and adjusting the pH value to 7;

[0018] 3) Nitrogen protection for 20 minutes;

[0019] 4) The above solution is heated to 50° C., adding 4 parts by weight of dimethyl diallyl ammonium chloride, 1 part by weight of an initiator with a mass percent concentration of 10% -- ammonium persulfate aqueous solution and 2 parts by weight of relative...

Embodiment 2

[0035] An anti-slump and fluid loss reducing agent for high-temperature drilling fluid protection glue, the preparation method of which is as follows:

[0036] 1) Add 300 parts by weight of water into the reaction kettle, add 10 parts by weight of acrylamide and 60 parts by weight of 2-acrylamido-2-methylpropanesulfonic acid into the kettle and stir to dissolve into a 19% aqueous solution, then add 5 Parts by weight of acrylic acid are fully stirred and dissolved;

[0037] 2) adding a potassium hydroxide aqueous solution with a concentration of 20%, and adjusting the pH value to 8;

[0038] 3) Nitrogen protection for 30 minutes;

[0039] 4) The above solution is heated to 60° C., adding 7 parts by weight of dimethyl diallyl ammonium chloride, 2 parts by weight of an initiator with a concentration of 15%—ammonium persulfate aqueous solution and 3 parts by weight of a relative molecular quality control agent ——Mercaptan, constant temperature 5h, obtain colloidal product;

[0...

Embodiment 3

[0043] An anti-slump and fluid loss reducing agent for high-temperature drilling fluid protection glue, the preparation method of which is as follows:

[0044] 1) Add 350 parts by weight of water into the reaction kettle, add 8 parts by weight of acrylamide and 50 parts by weight of 2-acrylamido-2-methylpropanesulfonic acid into the kettle and stir to dissolve into a 14% aqueous solution, then add 4 Parts by weight of acrylic acid are fully stirred and dissolved;

[0045] 2) adding a potassium hydroxide aqueous solution with a concentration of 20%, and adjusting the pH value to 7.5;

[0046] 3) Nitrogen protection for 30 minutes;

[0047] 4) The above solution is heated to 55° C., adding 6 parts by weight of dimethyl diallyl ammonium chloride, 2 parts by weight of a concentration of 13% initiator—ammonium persulfate and 2 parts by weight of relative molecular mass control agent— -Mercaptan, constant temperature 3h, obtain colloidal product;

[0048] 5) Precipitate and wash ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-temperature colloid protecting anticaving fluid loss additive for a drilling fluid. A preparation method of the high-temperature colloid protecting anticaving fluid loss additive comprises the following steps of: dissolving acrylamide and 2-acrylamido-2-methylpropanesulfonic acid into 10-25 percent mixed aqueous solution; adding acrylic acid, fully stirring and dissolving and then adding a potassium hydroxide aqueous solution; adjusting the pH value to be 7-8; introducing nitrogen gas for protecting for 20-30 minutes; heating to be 50-60DEG C; adding dimethyldiallyl-ammonium chloride, ammonium persulfate and thiol and keeping the contant temperature for 2-5 hours to obtain a colloidal product; washing the colloidal product with acetone; removing an unreacted substance, keeping the constant temperature of about 105DEG C and drying for 2-4 hours; and crushing and sieving the crushed substance by a sieve with 60 meshes to obtain a white powdery product, namely the high-temperature colloid protecting anticaving fluid loss additive for the drilling fluid. According to the high-temperature colloid protecting anticaving fluid loss additive, the stability of high-temperature colloid in a waste-based drilling fluid system can be effectively improved.

Description

technical field [0001] The invention relates to an anti-slump and fluid loss agent for high-temperature drilling fluid protective glue and a preparation method thereof. Background technique [0002] Drilling fluid must have good high-temperature colloidal stability under high-temperature deep well and ultra-deep well drilling conditions, so as to ensure that the drilling fluid has good rheology and fluid loss wall-building properties under high-temperature conditions at the bottom of the well. Filtration wall-building property refers to the formation of a filter cake with good compactness, thin thickness, high strength and good lubricity on the wellbore wall while the drilling fluid is filtering out free water from the wellbore to the near-borehole wall, thereby preventing the drilling fluid from Further filtration or leakage to the formation, to avoid the occurrence of downhole complex accidents such as shrinkage, sticking, and well collapse. The formation of high-quality ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F220/58C08F220/56C08F220/06C08F226/02C09K8/035
Inventor 王富华王瑞和王力王成文
Owner CHINA UNIV OF PETROLEUM (EAST CHINA)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com