Preparation method of germanium and barium activated lithium iron phosphate as cathode material

A technology of lithium iron phosphate and cathode material, applied in chemical instruments and methods, phosphorus compounds, inorganic chemistry, etc., can solve problems such as poor conductivity and low tap density, and achieve improved conductivity, electronic conductivity, electrochemical The effect of performance improvement

Inactive Publication Date: 2012-05-02
浙江远志新材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there is a consensus that lithium iron phosphate has the advantages of good safety, no pollution, stable cycle performance, high specific capacity and low price, but it also has poor conductivity and the disadvantage of lower tap density

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Li2CO3 (99.73%), GeO2 (99.8%), BaCO3 (99.8%), FeC2O4.2H2O (99.06%), NH4H2PO4 (98%) raw materials, according to 1mol Li: 0.00002mol Ge: 0.0003mol Ba: 1mol Fe: 1mol P After proportional mixing, high-speed ball milling (rotating speed 200r / min) in absolute ethanol (AR) medium for 20h. After drying at 105-120°C, the precursor is obtained, and the dried precursor is placed in a high-temperature furnace, and calcined at 500-750°C for 24 hours in an ordinary pure nitrogen (>99.5%) atmosphere. That is, the germanium and barium activated lithium iron phosphate cathode material of the present invention is obtained.

Embodiment 2

[0027] Li2CO3 (99.73%), GeO2 (99.8%), BaCO3 (99.8%), FeC2O4.2H2O (99.06%), NH4H2PO4 (98%) raw materials, according to 1mol Li: 0.00004mol Ge: 0.001mol Ba: 1mol Fe: 1mol P After proportional mixing, high-speed ball milling (rotating speed 200r / min) in absolute ethanol (AR) medium for 20h. After drying at 105-120°C, the precursor is obtained, and the dried precursor is placed in a high-temperature furnace, and calcined at 500-750°C for 24 hours in an ordinary pure nitrogen (>99.5%) atmosphere. That is, the germanium and barium activated lithium iron phosphate cathode material of the present invention is obtained.

Embodiment 3

[0029] Li2CO3 (99.73%), GeO2 (99.8%), BaCO3 (99.8%), FeC2O4.2H2O (99.06%), NH4H2PO4 (98%) raw materials, according to 1mol Li: 0.00005mol Ge: 0.003mol Ba: 1mol Fe: 1mol P After proportional mixing, high-speed ball milling (rotating speed 200r / min) in absolute ethanol (AR) medium for 20h. After drying at 105-120°C, the precursor is obtained, and the dried precursor is placed in a high-temperature furnace, and calcined at 500-750°C for 24 hours in an ordinary pure nitrogen (>99.5%) atmosphere. That is, the germanium and barium activated lithium iron phosphate cathode material of the present invention is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of germanium and barium activated lithium iron phosphate as a cathode material. The preparation method comprises the steps of: mixing raw materials including a lithium source, a germanium source, a barium source, an iron source and a phosphate source according to the proportion of 1mol:(0.00002-0.00005)mol:(0.0003-0.003)mol:1mol:1mol; then, performing high-speed ball milling at the rotation speed of 200r / minm for 20h in an absolute ethyl alcohol medium; drying at 105-120 DEG C to obtain a precursor; placing the precursor obtained through drying in a high-temperature furnace; and calcinating for 24h at the high temperature of 500-750 DEG C in a nitrogen atmosphere to obtain the germanium and barium activated lithium iron phosphate as the cathode material. Because a small amount of substitutive germanium and barium are doped, the shape and the particle size of a product are favorably controlled to obtain a stable lithium iron phosphate compound, of which the crystal lattice is activated, the lithium ion diffusion coefficient is increased, and the initial discharge capacity of the obtained cathode material reaches 160.52mAh / g; a charge-discharge platform of the cathode material is about 3.5V relative to a lithium electrode potential, the initial discharge capacity exceeds 168mAh / g, and the capacity is attenuated by about 1.2% after 100times of charge-discharge cycles; and compared with a control embodiment, namely undoped LiFePO4, the cathode material is greatly improved in specific capacity and cyclic stability.

Description

technical field [0001] The method for preparing a germanium and barium activated lithium iron phosphate positive electrode material of the invention belongs to a method for preparing a lithium battery positive electrode material, and in particular relates to a preparation method for a lithium iron phosphate battery positive electrode material. Background technique [0002] At present, the research status of lithium iron phosphate doping modification: lithium iron phosphate LiFePO4 is non-toxic, environmentally friendly, high in safety, rich in raw materials, high in specific capacity, stable in cycle performance, and low in price. The stable discharge platform with a theoretical capacity of 3.5V, the lithium iron phosphate material has high energy density, low price, and excellent safety, and is especially suitable for power batteries. But it has a higher resistivity. Due to lithium iron phosphate, the kinetics of LiFePO4 is not good at room temperature, and the rate perfor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/58C01B25/45
CPCY02E60/12Y02E60/10
Inventor 张健张新球吴润秀王晶张雅静李杰李安平李先兰严积芳黄景诚
Owner 浙江远志新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products