High-temperature resistant self-adhesive polymer modified asphalt waterproofing membrane and preparation method thereof

A technology for modifying asphalt and waterproofing membranes, applied in the direction of asphalt material binders, non-polymer binder additives, binder types, etc., can solve the problems of inability to adapt to high temperature, poor heat resistance, etc. Efficiency, good water impermeability, scientific process formula effect

Inactive Publication Date: 2012-06-13
TANGSHAN DESHENG WATERPROOF
View PDF5 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004]The purpose of this invention is to solve the problem that the existing self-adhesive waterproof membrane has poor heat resistance and cannot adapt to high temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Raw material components and parts by weight are as follows:

[0031] 55 parts of No. 100 asphalt, 7 parts of softening oil, 25 parts of pulverized recycled rubber powder, 8 parts of rubber powder modifier, 25 parts of heavy calcium powder, and 2 parts of pure polypropylene.

[0032] In this example, the softening oil is the third-line oil produced by Qinhuangdao Zhongyou Petrochemical; the pulverized regenerated rubber powder is PS rubber powder produced by Guangxi Yuanjing; the rubber powder modifier is a mixture of fine rubber powder produced by Xinle Yilong; Calcium powder is commercially available 300-400 mesh heavy calcium powder; pure polypropylene is brand 2535A pure polypropylene produced by Formosa Plastics USA.

[0033] Carry out small-scale production by the parts by weight of formula, its production method is as follows:

[0034] 1. Take 55 parts of No. 100 asphalt and 7 parts of softening oil according to the parts by weight, mix and stir the two...

Embodiment 2

[0044] Raw material components and parts by weight are as follows:

[0045] 54 parts of No. 100 asphalt, 8 parts of third-line oil, 25 parts of desulfurized rubber powder, 10 parts of rubber powder modifier, 25 parts of heavy calcium powder, and 3 parts of pure polypropylene.

[0046] In this embodiment, No. 100 asphalt is No. 100 road petroleum asphalt produced by Qinhuangdao PetroChina Petrochemical Co., Ltd.

[0047] The softening oil is the third-line oil produced by Qinhuangdao PetroChina Petrochemical Co., Ltd.

[0048] Pulverized recycled rubber powder is desulfurized rubber powder produced by Guangxi Yuanjing.

[0049] Rubber powder modifier is a mixture of fine rubber powder produced by Xinle Yilong.

[0050] Heavy calcium powder is commercially available 300-400 mesh heavy calcium powder.

[0051] Pure polypropylene is M1600 pure polypropylene produced by Hyundai in Korea.

[0052] Its production method is as follows:

[0053] Take 54 parts o...

Embodiment 3

[0061] Raw material components and parts by weight are as follows:

[0062] 60 parts of No. 100 asphalt, 10 parts of third-line oil, 30 parts of desulfurized rubber powder, 12 parts of rubber powder modifier, 30 parts of heavy calcium powder, and 3 parts of pure polypropylene.

[0063] No. 100 asphalt is No. 100 road petroleum asphalt produced by Qinhuangdao PetroChina Petrochemical Co., Ltd.

[0064] The softening oil is the third-line oil produced by Qinhuangdao PetroChina Petrochemical Co., Ltd.

[0065] Pulverized recycled rubber powder is desulfurized rubber powder produced by Guangxi Yuanjing.

[0066] Rubber powder modifier is a mixture of fine rubber powder produced by Xinle Yilong.

[0067] Heavy calcium powder is commercially available 300-400 mesh heavy calcium powder.

[0068] Pure polypropylene is M1600 pure polypropylene produced by Hyundai in Korea.

[0069] Get 60 parts of No. 100 bitumen according to the weight part of above-mentioned for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-temperature resistant self-adhesive polymer modified asphalt waterproofing membrane and a preparation method thereof. The high-temperature resistant self-adhesive polymer modified asphalt waterproofing membrane comprises the following raw materials by weight: 50 to 60 parts of No. 100 asphalt, 5 to 10 parts of softening oil, 20 to 30 parts of pulverization reclaimed rubber powder, 6 to 12 parts of rubber powder modifier, 20 to 30 parts of coarse whiting powder, and 2 to 3 parts of pure polypropylene. The preparation method comprises the following steps: taking the No. 100 asphalt and softening oil according to the parts by weight; stirring and mixing the No. 100 asphalt and the softening oil; adding the pure polypropylene when the temperature reaches 190 to 200 DEG C; adding the pulverization reclaimed rubber powder when the pure polypropylene is completely melted; keeping stirring for 120 min when the temperature reaches 200 minus or plus 5 DEG C; adding the rubber powder modifier when the temperature falls to 170 minus or plus 5 DEG C; mixing and stirring uniformly when the coarse whiting powder is added, so as to obtain a finished mixture; and making the finished mixture into modified asphalt waterproofing membranes according to the manufacture procedure. As asphalt is modified to bear temperature higher than 120 DEG C, the invention has the advantages that no sliding phenomenon is generated under a high temperature; the viscosity is higher; and the suitability to construction environments is high.

Description

technical field [0001] The invention relates to a waterproof coiled material and a preparation method thereof. In particular, it relates to a high-temperature-resistant self-adhesive polymer modified asphalt waterproof coiled material made by using modifier modified asphalt mixture and a preparation method thereof. Background technique [0002] Self-adhesive waterproof membrane is a new type of waterproof material with great development prospects. Its application in our country began in the early 1990s. Its standards have gone through self-adhesive rubber asphalt waterproofing membrane (JC 840-1999), self-adhesive polymer modified asphalt polyester tire waterproofing membrane (JC 898- 2002) industry standard to the later waterproof membrane with self-adhesive layer (GB / T 23260-2009), pre-paved / wet-laid waterproof membrane (GB / T 23457-2009), self-adhesive polymer modified bitumen waterproof membrane Material (GB 23441-2009) and other national standards, the variety has grad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/00C09J195/00C09J117/00C09J123/12C09J11/04C09J7/04E04D5/10
Inventor 彭贺民张书言
Owner TANGSHAN DESHENG WATERPROOF
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com