Alkenyl succinic anhydride sizing agent emulsion and preparation method thereof

一种烯基琥珀酸酐、烯基琥珀酸的技术，应用在憎水剂添加、纺织品和造纸、造纸等方向，能够解决无机纳米材料成本高、资源化、白泥废渣污染等问题，达到提高企业竞争力、乳化成本低、实现回收利用的效果

Inactive Publication Date: 2014-08-13
QILU UNIV OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the pollution and recycling of white mud waste residue, and at the same time aiming at the deficiency of the existing ASA emulsification technology and the relatively high cost of inorganic nanomaterials, this paper The invention provides an alkenyl succinic anhydride sizing agent emulsion using white mud waste residue as an emulsifier

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Disperse 0.05 parts of papermaking white mud waste residue powder into 100 parts of deionized water, then disperse into 100 parts of commercial ASA at a stirring speed of 10,000 rpm, and continue stirring for 6 minutes to prepare a stable O / W type ASA emulsion , within 24 hours the emulsion was uniform, stable and non-separated.

[0024] Take 100 parts of poplar BCTMP pulp with a beating degree of about 42°SR and add it to 9900 parts of water. 2 (SO 4 ) 3 , mixed evenly to form a paper material, and passed through a rapid Kaiser method paper sheet former to a quantitative value of 60g / m 2 The hand-made sheet was dried in a drying cylinder at 105°C for 10 minutes, and the sizing degree of the hand-made sheet was measured to be 98s by liquid penetration method (GB / T5405-2002).

[0025] After the prepared emulsion was left to stand for 1 hour, the same operation was carried out according to the above steps, and the sizing degree of the hand-made sheet was measured to be...

Embodiment 2

[0027] Disperse 0.1 part of papermaking white mud waste residue powder into 100 parts of deionized water, then disperse into 100 parts of commercial ASA at a stirring speed of 7000 rpm, and continue stirring for 3 minutes to prepare a stable O / W type ASA emulsion .

[0028] Take 100 parts of poplar BCTMP pulp with a beating degree of about 42°SR and add it to 9900 parts of water. 2 (SO 4 ) 3 , mixed evenly to form a paper material, and passed through a rapid Kaiser method paper sheet former to a quantitative value of 60g / m 2 The hand-made sheet was dried in a drying cylinder at 105°C for 10 minutes, and the sizing degree of the hand-made sheet was measured to be 116s by liquid penetration method (GB / T5405-2002).

Embodiment 3

[0030] Disperse 0.16 parts of papermaking white mud waste residue powder into 100 parts of deionized water, then disperse into 100 parts of commercial ASA at a stirring speed of 6000 rpm, and continue stirring for 4 minutes to prepare a stable O / W type ASA emulsion .

[0031] Take 100 parts of poplar BCTMP pulp with a beating degree of about 42°SR and add it to 9900 parts of water. 2 (SO 4 ) 3 , mixed evenly to form a paper material, and passed through a rapid Kaiser method paper sheet former to a quantitative value of 60g / m 2 The hand-made sheet was dried in a drying cylinder at 105°C for 10 minutes, and the sizing degree of the hand-made sheet was measured to be 135s by liquid penetration method (GB / T5405-2002).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of sizing agents in the papermaking industry, in particular to an alkenyl succinic anhydride sizing agent emulsion, which contains white mud waste residue, alkenyl succinic anhydride and water, and the mass ratio of alkenyl succinic anhydride to water is 1:1~4 ; The mass ratio of white mud waste residue to alkenyl succinic anhydride is 1:20~1000. The preparation method is to disperse the white mud waste residue into alkenyl succinic anhydride, and then add water to mix evenly; or disperse white mud waste residue into water, and then mix evenly with alkenyl succinic anhydride to prepare a stable O / W type ASA emulsion . Realize the recycling of industrial waste residues, and realize a virtuous economic cycle; the amount of emulsifier used when white mud is used as an emulsifier is lower than that of inorganic nanomaterials, and it can achieve good results at a lower amount of emulsifier. sizing effect, so the cost of emulsification is lower, and it also has the advantages of simple emulsification process and high concentration of the prepared emulsion. After diluting and emulsifying with water, it is added to the paper material for in-pulp sizing, and the sizing efficiency is high.

Description

[0001] technical field [0002] The invention relates to the field of sizing agents in the papermaking industry, in particular to an alkenyl succinic anhydride sizing agent emulsion, and also relates to a preparation method of the alkenyl succinic anhydride sizing agent emulsion. [0003] Background technique [0004] According to a report by China Industry News in 2008, the world's soda ash production capacity is mainly distributed in China, North America and Europe, accounting for 85% of the global total production capacity. By the end of 2006, China's soda ash production capacity reached 17.2 million tons, accounting for 34% of the world's total production capacity, ranking first in the world, while Europe and North America accounted for 29% and 23% respectively. About 0.3~0.6t of soda slag is discharged per 1t of soda ash produced, commonly known as "soda white mud". According to this calculation, the "white mud" produced by the soda making industry in my country is as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H21/16D21H17/68D21H17/14
Inventor 王哲魏明志刘温霞薛菁雯王慧丽王兴琪王晓卫
Owner QILU UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com