Flame-retardant polymer cement waterproof mortar

A waterproof mortar and polymer technology, applied in the field of building materials, can solve problems such as unrealistic, and achieve the effects of firm bonding, simple production and good flame retardant effect

Active Publication Date: 2012-06-20
JIANGSU WONIUSHAN THERMAL INSULATION & WATERPROOF TEHNOLOGY
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, it is unrealistic for all roofing materials to be composed of non-combustible materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant polymer cement waterproof mortar
  • Flame-retardant polymer cement waterproof mortar
  • Flame-retardant polymer cement waterproof mortar

Examples

Experimental program
Comparison scheme
Effect test

no. 1 example

[0023] Based on the above range, the first embodiment provided by the present invention, the specific weight ratio of each component is as follows:

[0024] 1) Liquid material part

[0025] Propylbenzene emulsion 55%;

[0026] Preservatives 0.2%;

[0027] Polyacrylic acid sodium salt dispersant 0.3%;

[0028] Mineral oil defoamer 0.2%;

[0029] Water 44.2%;

[0030] 2) Powder part:

[0031] Ordinary Portland cement 45.00%;

[0032] Quartz sand 53.90%;

[0033] Cellulose ether 0.10%;

[0034] Water reducer 0.20%;

[0035] Magnesium hydroxide 2%;

[0036] 3) The weight proportion of each component:

[0037] Liquid material: Powder = 1:4

[0038] Based on the above range, the second embodiment provided by the present invention, the specific weight ratio of each component is as follows:

[0039] 1) Liquid material part

[0040] Propylbenzene emulsion 50%;

[0041] Preservatives 0.2%;

[0042] Polyacrylic acid sodium salt dispersant 0.3%;

[0043] Mineral oil defoam...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a flame-retardant polymer cement waterproof mortar which comprises liquid and powder in a weight ratio of 1.0:(3.5-4.5). The liquid comprises the following raw materials in percentage by weight: 50-60% of styrene-acrylate emulsion, 0.10-0.20% of preservative, 0.20-0.30% of dispersant, 0.10-0.20% of defoaming agent and 40-50% of water. The powder comprises the following raw materials in percentage by weight: 40-45% of ordinary Portland cement, 50-55% of quartz sand, 0.02-0.05% of cellulose ether, 0.4-0.5% of water reducing agent and 1.0-3.0% of flame retardant. The flame-retardant polymer cement waterproof mortar can be used for waterproof and moistureproof treatment, effectively solves the problem of waterproofing on the building waterisde or landside, has the advantages of favorable flame retardancy and high binding firmness, is simple and convenient for production, and has favorable flame retardancy and waterproof property when the construction thickness is 1-2mm.

Description

technical field [0001] The invention relates to a building material, in particular to a flame-retardant polymer cement waterproof mortar widely used in toilets, bathrooms, kitchens, balconies and exterior walls. Background technique [0002] In recent years, fires caused by building materials have occurred frequently in our country, especially the huge fires in the CCTV Building, Jinan Olympic Sports Center, Peking University Table Tennis Hall and Taiyuan Iron and Steel Plant have attracted great attention from the competent government departments. [0003] The Fire Department of the Ministry of Public Security organizes the Tianjin Fire Research Institute of the Ministry of Public Security, the Sichuan Fire Research Institute of the Ministry of Public Security and other relevant units to integrate the "Code for Fire Protection Design of Buildings" (GB50016-2006) and "Code for Fire Protection Design of High-rise Civil Buildings" (GB50045-95) revised. A few days ago, the rev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
Inventor 冯春鹏熊卫锋
Owner JIANGSU WONIUSHAN THERMAL INSULATION & WATERPROOF TEHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com