Manufacture method of carbonized particle nutrition soil for culturing arethusa plants
A manufacturing method and technology of carbonizing granules, applied in fertilizer mixtures, fertilization devices, applications, etc., can solve the problem that nutrient soil cannot fully meet the requirements of normal growth and nutrient elements required by orchid plants, and achieve water storage Moisturizing, improving the degree of standardization and scientificity, and the effect of more living space
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0041] Respectively, after drying the weed grass and the clay, pulverize them into powder with a pulverizer, the length of the weed grass powder is less than 5 mm; the clay powder can pass through an 80 mesh sieve, and the weight percentage is 2% of the weed grass powder and 98% of the clay powder are mixed evenly to obtain a mixed powder Then, the amount of macroelements and microelements in the formula of B5 medium is prepared according to the total weight ratio of the carbonized granule nutrient soil, then concentrated 10 times, directly added to the above mixed powder, and then added with clean water and mixed thoroughly , to obtain nutritional powder; the water content in the nutritional powder is controlled at about 12%, and after further mixing evenly, the nutritional powder is prepared into solid particles with a particle feed machine, and the diameter of the particles is about 5mm. After the solid particles are naturally air-dried , placed in a closed dry distillation ...
Embodiment 2
[0043] Respectively dry wheat straw and clay and pulverize them into powder with a pulverizer, the length of the wheat straw powder is less than 7mm; the clay powder can pass through an 80 mesh sieve, and mix 98% wheat straw powder and 2% clay powder evenly by weight to obtain a mixed powder Then the amount of macroelements and microelements in the formula of MS culture medium is prepared according to the total weight ratio of the carbonized granule nutrient soil, then concentrated 10 times, directly added to the above mixed powder, and then added with clean water and mixed thoroughly , to obtain nutritional powder; the water content in the nutritional powder is controlled at about 15%, and after further mixing evenly, the nutritional powder is prepared into solid particles with a diameter of about 20 mm using a pellet feed machine, and after the solid particles are naturally air-dried, Put it in a closed carbonization furnace for carbonization. After the temperature in the car...
Embodiment 3
[0045] Respectively dry the edible fungi cultivation waste and clay and pulverize them into powder with a pulverizer. The length of the edible fungi cultivation waste powder is below 10mm; Mix evenly with 50% clay powder to obtain mixed powder; then prepare the amount of macroelements and microelements in the formula of B5 medium according to the total weight ratio of the prepared carbonized granulated nutrient soil, and then concentrate the amount by 10 times. Add directly to the above mixed powder, then add clean water and mix thoroughly to obtain nutritional powder; the water content in the nutritional powder is controlled at about 13%, and after further mixing evenly, the nutritional powder is prepared into a solid by using a pellet feed machine Granules, the diameter of which is about 8mm. After the solid particles are naturally air-dried, they are placed in a closed carbonization furnace for carbonization. The temperature is about 200°C, and the airtight carbonization ti...
PUM
Property | Measurement | Unit |
---|---|---|
Particle diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com