Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Quick mending agent

A repairing agent and fast technology, applied in the direction of adhesive, adhesive type, adhesive additive, etc., can solve the problems of difficult to achieve strength and temperature resistance, large foreign exchange consumption, unsatisfactory performance, etc. The effect of fast repair speed and high bond strength

Inactive Publication Date: 2013-07-03
北京天诚宇新材料技术有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, although some domestic units have developed some metal fillers and wear-resistant adhesives, their performance cannot meet the requirements for equipment maintenance.
Although the performance of the above-mentioned foreign-developed repair materials is higher than that of domestic products, Germany’s Diamant products were used for tank track hangers in my country in the 1980s, but the strength and temperature resistance are still difficult to meet the demanding performance requirements for repairing military equipment or strength. equipment requirements, and the price of imported repair agents is extremely expensive, consuming a large amount of foreign exchange, resulting in the company's consumption of huge funds in equipment maintenance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quick mending agent
  • Quick mending agent
  • Quick mending agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3

[0069] Component A is 3600g of 711 epoxy resin, 3601g of epoxy resin E51, 537g of aluminum oxide, 1428g of iron powder, 894g of stainless steel powder, 358.5g of graphite powder and 120g of white carbon black; component B is 810 underwater epoxy curing agent 714g, low molecular weight polyamide 650 537g, DMP-30 (2,4,6-tris(dimethylaminomethyl)phenol) 54g, white carbon black 660g; Weigh it according to the ratio of 3:1~5:1 by weight, and mix evenly. The concrete proportioning ratio of each embodiment is shown in Table 1.

[0070] Table 1

[0071] Example 1 2 3 Grade TG517 TG518 TG519 A, B ratio 4:1 5:1 6:1

[0072] Tensile strength, tensile shear strength, compressive strength, hardness, wear resistance, corrosion resistance and temperature resistance are tested according to the Ministry of Chemical Industry and national standards. The test methods and test results are as follows:

[0073] 3.1 Tensile strength

[0074] (1) Test method:

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a quick mending agent and a preparation method thereof. The mending agent is a normal-temperature curing dual-component reactive mending agent, and has better comprehensive performances than those of epoxy, anaerobic and other common adhesives; a cured adhesive layer is grey and has the bonding strength of 43MPa; and the temperature for using the mending agent is between 60and 180 DEG C. The quick mending agent is mainly used for sealing and blocking oil tanks, water tanks and gas transmission pipelines.

Description

technical field [0001] The invention relates to a fast repairing agent, in particular to an epoxy-modified normal-temperature curing two-component reactive fast adhesive. Background technique [0002] As an important means of maintenance, surface engineering has been paid more and more attention. As an important part of the surface engineering discipline n9 surface technology, surface repair technology includes electroplating, electro-brush plating, thermal spraying, adhesive bonding, etc. These repair methods complement each other and become the necessary emergency measures for equipment maintenance. The old parts have been brought back to life, saving huge economic losses for the enterprise, and equipment maintenance has become an integral part of productivity. [0003] As one of the modern surface technologies, surface adhesive coating technology has played an important role in the field of equipment maintenance in recent years and achieved good social and huge economic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J163/00C09J11/04C09J11/06
Inventor 梁欣
Owner 北京天诚宇新材料技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com