Novel process for preparing peony porcelain

A production process, peony porcelain technology, applied in the field of ornamental peony porcelain production, to achieve the effect of lifelike image, regional culture promotion and quality of finished products

Active Publication Date: 2012-07-11
李学武
View PDF4 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] It can be seen from the above that ceramics, as a kind of utensils that can be preserved for a long time, can keep flowers blooming forever if they are combined with flower making. After searching, no combination of ceramics and flowers has been found.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A new manufacturing process of peony porcelain,

[0044] Alumina, iron oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, titanium dioxide and quartz are used as china clay base materials, and the weight percentage of each raw material is: alumina 20%, iron oxide 0.3%, calcium oxide 0.01% , magnesium oxide 0.01%, potassium oxide 2.5%, sodium oxide 0.14%, titanium dioxide 0.04% and quartz 77%;

[0045] Using white feldspar, quartz, calcite, kaolin, alumina, white clay, porcelain stone and potassium feldspar as glaze raw materials, the weight ratio of each raw material is: white feldspar 6%, quartz 10%, calcite 4%, kaolin 15% %, alumina 5%, white clay 30%, porcelain stone 15%, potassium feldspar 15%, the production method is:

[0046] Step 1, mud making: After pulverizing the china clay base material, mix it into the mill according to the above ratio, add water with a total weight of 29% of the mixed raw material, start the machine for wet grinding for...

Embodiment 2

[0054] A new manufacturing process of peony porcelain,

[0055] Alumina, iron oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, titanium dioxide and quartz are used as china clay base materials, and the weight percentage of each raw material is: aluminum oxide 30%, iron oxide 0.3%, calcium oxide 0.01% , magnesium oxide 0.01%, potassium oxide 2.4%, sodium oxide 0.14%, titanium dioxide 0.04% and quartz 67%;

[0056] Using white feldspar, quartz, calcite, kaolin, alumina, white clay, porcelain stone and potassium feldspar as glaze raw materials, the weight ratio of each raw material is: white feldspar 10%, quartz 4%, calcite 6%, kaolin 17% %, alumina 3%, white clay 25%, porcelain stone 17%, potassium feldspar 18%, the production method is:

[0057] Step 1, mud making: After pulverizing the china clay base material, mix it into the mill according to the above ratio, add water with 33% of the total weight of the mixed raw material, start the wet grinding for 14...

Embodiment 3

[0065] A new manufacturing process of peony porcelain,

[0066] Aluminum oxide, iron oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, titanium dioxide and quartz are used as china clay base materials, and the weight percentages of each raw material are: aluminum oxide 26.7%, iron oxide 0.36%, calcium oxide 0.01% , magnesium oxide 0.01%, potassium oxide 2.7%, sodium oxide 0.18%, titanium dioxide 0.04% and quartz 70%;

[0067] Using white feldspar, quartz, calcite, kaolin, alumina, white clay, porcelain stone and potassium feldspar as glaze raw materials, the weight ratio of each raw material added is: white feldspar 4%, quartz 6%, calcite 10%, kaolin 20% %, alumina 4%, white clay 18%, porcelain stone 18%, potassium feldspar 20%, the production method is:

[0068] Step 1, mud making: After pulverizing the china clay base material, mix it into the mill according to the above ratio, add water with 30% of the total weight of the mixed raw material, start the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel process for preparing peony porcelain. Porcelain prepared by the process can be fired for second time to form the peony porcelain. Aluminum oxide, ferric oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, titanium dioxide, and quartz are used as porcelain clay base stick; and the process comprises the following steps of: a, preparing mud blank; 2, preparing glaze slip; 3, preparing a green body; 4, firing to obtain biscuit for later use; 5, applying glaze slip, namely placing the biscuit prepared in the step 4 in the glaze slip prepared in the step 2 to obtain a green body for later use; 6, calcining, namely placing the green body which is obtained in the step 5 and to which the glaze slip is applied in a kiln and calcining, and after firing is completed, drawing to obtain a green body for later use; and 7, painting colored drawing, namely drawing dermatoglyphic patterns on the green body prepared in the step 6 and dyeing by using pigment to obtain the colored green body, firing for 4 to 6 hours, taking out, and cooling to room temperature to obtain a finished product.

Description

technical field [0001] The invention relates to a method for making porcelain, in particular to a method for making ornamental peony porcelain. Background technique [0002] As we all know, peonies, roses, chrysanthemums, peonies and other ornamental flowers have a short flowering period, but the flowers are very bright, which can add a lot of bright spots to indoors or celebrations, but as the saying goes: "Flowers don't always bloom, youth doesn't always exist" , which means that although flowers are good, they only bloom for a limited time, and the flowering period is very short; flowers need corresponding ecological conditions to grow and open. [0003] It is known that ceramics, as a common utensil "including daily necessities such as cups, teapots, and bowls", have existed for thousands of years. In my country, pottery was invented as early as about 8000-2000 BC (Neolithic Age). . The main components of ceramic materials are silicon oxide, aluminum oxide, potassium ox...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/18C04B41/86
Inventor 李学武
Owner 李学武
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com