A technology of broken glass and beer bottles, which is applied in the field of making beer bottles by using broken glass, can solve the problems of unqualified pressure resistance and impact resistance, complicated types of waste broken glass, different colors and components, etc., and achieve improved impact resistance and Effects of compressive strength, production cost reduction, and utilization improvement

Inactive Publication Date: 2012-07-18
WUHAN HUAXIA GLASSWORK
View PDF3 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the various types of waste and old broken glass in the society at present, and the colors and components are not the same
If these problems cannot be solved, qualified beer bottles cannot be produced
[0004] In addition, beer bottles produced purely from waste cullets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: 55-57 kg of quartz sand, 15-19 kg of soda ash, 15-19 kg of calcite, 3-6 kg of dolomite, 6-8 kg of feldspar, 3-5 kg ​​of mirabilite, and 5-7 kg of fluorite , 1-2 kilograms of sodium nitrate (or 0.5-1.5 kilograms of cerium dioxide), add into the mixing machine and mix evenly to make powder, so that the uniformity of the powder reaches ≥ 95%, and then add the crushed powder that meets the requirements for preparing white beer bottles. 1000 kg of glass, fully mixed with powder again, the moisture content of the mixture is ≤8%; and then made into white beer bottles according to the processing technology of glass bottles.

[0018] The 1000 kg cullet for preparing white beer bottles includes 70-100% plain white glass and 0-30% white flat glass, the particle size of the cullet is 10-40 mm, and the water content of the cullet is ≤5%.

Embodiment 2

[0019] Example 2: Add 57 kg of quartz sand, 17 kg of soda ash, 17 kg of calcite, 4 kg of dolomite, 7 kg of feldspar, 5 kg of mirabilite, 6 kg of fluorite, and 1.5 kg of sodium nitrate into a mixing machine and mix evenly to prepare Powder, so that the uniformity of the powder reaches ≥95%, then add 1,000 kg of broken glass that meets the requirements of white beer bottles, and then fully mix with the powder again, the moisture content of the mixture is ≤8%; then make according to the processing technology of glass bottles into white beer bottles.

[0020] The 1000 kg cullet for preparing white beer bottles includes 70-100% plain white glass and 0-30% white flat glass, the particle size of the cullet is 10-40 mm, and the water content of the cullet is ≤5%.

[0021] 2) Prepare green beer bottle:

[0022] Embodiment 1: 53-57 kg of quartz sand, 17-21 kg of soda ash, 7-10 kg of calcite, 3-5 kg ​​of dolomite, 4-6 kg of feldspar, 4-6 kg of mirabilite, and 5-7 kg of fluorite , Chrom...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to view more

Abstract

A method for manufacturing beer bottles through broken glass includes the steps of adding powder materials in 1000 kilograms of broken glass. For manufacturing white beer bottles, the composition and weight of the powder materials are that: 55-57 kilograms of quartz sand, 15-19 kilograms of sodium carbonate, 15-19 kilograms of calcite, 3-6 kilograms of dolomite, 6-8 kilograms of feldspar, 3-5 kilograms of mirabilite, 5-7 kilograms of fluorite and 1-2 kilograms of sodium nitrate or 0.5-1.5 kilograms of cerium dioxide. For manufacturing green beer bottles, the composition and weight of the powder materials are that: 53-57 kilograms of quartz sand, 17-21 kilograms of sodium carbonate, 7-10 kilograms of calcite, 3-5 kilograms of dolomite, 4-6 kilograms of feldspar, 4-6 kilograms of mirabilite, 5-7 kilograms of fluorite and 0.5-1.5 kilograms of chromium mineral powder. For manufacturing brown beer bottles, the composition and weight of the powder materials are that: 52-56 kilograms of quartz sand, 17-20 kilograms of sodium carbonate, 12-15 kilograms of calcite, 3-5 kilograms of dolomite, 4-6 kilograms of feldspar, 5-7 kilograms of mirabilite, 5-7 kilograms of fluorite and 0.3-1.0 kilogram of carbon powder. The method for manufacturing beer bottles through broken glass can improve utilization rate of broken glass, ensures quality of glass and is suitable for manufacturing of beer bottles.

Description

technical field [0001] The invention relates to the production and manufacture of glass bottles, in particular to a method for preparing beer bottles from broken glass. Background technique [0002] How to effectively reuse the large amount of waste cullet generated in people's daily production and life is one of the urgent issues to be solved by glass workers in China and even around the world. In the prior art, the recycling of waste (or waste) glass is mainly used for low-grade flat-drawn flat glass, mosaic glass, etc., which have lower requirements on quality indicators such as glass impurities. For glass varieties with high quality requirements, such as float glass, waste glass is generally not added as raw materials. "Recycling and Utilization of Waste Glass" (Jiang Wenjiu "Shanghai Building Materials" No. 3, 2003) discloses the application of the prior art to waste cullet, and its disclosed content is quoted here. [0003] As a renewable raw material, cullet can red...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C6/06C03C6/02
Inventor 谈宇宏赵新江冯爱霞王海军徐汉尧刁国贤徐德华
Owner WUHAN HUAXIA GLASSWORK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap