Deoxidizing agent for steelmaking of electric converter and preparation method thereof

A deoxidizer and electric converter technology, which is applied in the field of electric converter steelmaking, can solve the problems of not being able to improve the quality of steel products, difficult removal of impurities in finished products, and problems affecting product quality, so as to achieve good deoxidation effect, improve processing and mechanical properties, and be economical. significant effect

Active Publication Date: 2012-08-01
芜湖县天海耐火炉料有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the deoxidizer used in the steelmaking process of the domestic metallurgical industry is mainly aluminum or aluminum alloy, which is directly used for deoxidation treatment, but it produces The impurity left in the finished product is not easy to remove, which seriously

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] Example 1: Electric converter steelmaking deoxidizer, the weight parts of its raw materials are: 30 parts of calcium carbide, 30 parts of calcium oxide, 3 parts of calcium difluoride, 3 parts of coke, 5 parts of magnesium oxide, 3 parts of zinc oxide, 5 parts of straw ash , 10 parts of kaolin, 3 parts of silicon dioxide, 8 parts of lapis lazuli, 5 parts of attapulgite and 3 parts of barium carbonate.

[0010] The component raw materials are weighed according to the weight portion of the constituent raw materials, and the large granular raw materials are pulverized and ball-milled, and then mixed uniformly to obtain.

[0011] The deoxidizer of the present invention was tested on Q235B steel type in a certain steel factory, and the average value of the detected oxygen content was 49.4PPM.

Embodiment 2

[0012] Example 2: Electric converter steelmaking deoxidizer, the weight parts of its raw materials are: 40 parts of calcium carbide, 40 parts of calcium oxide, 8 parts of calcium difluoride, 8 parts of coke, 10 parts of magnesium oxide, 5 parts of zinc oxide, 10 parts of straw ash , 15 parts of kaolin, 8 parts of silicon dioxide, 12 parts of lapis lazuli, 10 parts of attapulgite and 5 parts of barium carbonate.

[0013] The component raw materials are weighed according to the weight portion of the constituent raw materials, and the large granular raw materials are pulverized and ball-milled, and then mixed uniformly to obtain.

[0014] A steel factory produces 20Mn steel in a 300-ton electric converter. The former deoxidizes with ferroalmanganese, and adds 1 ton to each furnace, 8 tons per ton of steel. With the electric converter steelmaking deoxidizer of the present invention, adds 500 kg to each furnace, and 4 tons per ton of steel , The average oxygen content detected is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a deoxidizing agent for the steelmaking of an electric converter and a preparation method thereof. The deoxidizing agent is obtained by uniformly mixing raw materials according to certain parts by weight, wherein the raw materials are calcium carbide, calcium oxide, calcium difluoride, coke, magnesium oxide, zinc oxide, straw ashes, kaoline, silicone dioxide, celestite, attapulgite and barium carbonate. The deoxidizing agent is used for the steelmaking of the electric converter, does not contain aluminium and can increase the physical, mechanical and processing properties of steel; and simultaneously, the deoxidizing agent can remove gases, changes a nonmetallic inclusion and can increase the quality and the mechanical property of the steel made by the electric converter.

Description

technical field [0001] The invention relates to the technical field of electric converter steelmaking, in particular to an electric converter steelmaking deoxidizer and a preparation method thereof. Background technique [0002] At present, the deoxidizers used in the steelmaking process of the domestic metallurgical industry are mainly aluminum or aluminum alloys. Aluminum or aluminum alloys are directly used for deoxidation treatment, but the impurities produced are not easy to remove in the finished product, which seriously affects the quality of the product. , its role is to improve the quality of steel, but its method can not solve the removal of sulfur in the steelmaking process, can not improve the quality of steel products, an urgent need for a product and method of steelmaking deoxidation. Contents of the invention [0003] In order to alleviate the deficiencies and defects of the prior art, the object of the present invention is to improve a deoxidizer for elect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21C7/06
Inventor 吴大宏童振兰
Owner 芜湖县天海耐火炉料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap