Mosquito-dispelling polyamide 6 fiber and preparation method thereof

A technology of nylon and mosquito repellent, which is applied in the field of mosquito repellent nylon 6 fiber and its preparation, which can solve the problems of poor slow-release effect of mosquito repellent, large amount of volatilization of mosquito repellent, easy falling off of mosquito repellent coating, etc., and achieves low price , low cost, small effect under high temperature conditions

Inactive Publication Date: 2012-08-01
HANGZHOU XINFU TEXTILE
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the existing methods for preparing mosquito repellent textiles have problems such as that the mosquito repellent is easy to volatilize in large quantities during the processing, the loss is large, the mosquito repellent coating is easy to fall off, the process is complicated, the slow release effect of the mosquito repellent is poor during use, and the mosquito repellent effect is not good. ideal
And the mosquito repellants used are mostly insect repellents, pyrethroids, etc., which are highly toxic, and long-term inhalation will affect human health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) Preparation of mosquito repellent nylon 6 masterbatch

[0024] The weight percent of each composition in the masterbatch is:

[0025] Fiber grade polyamide 6:60%;

[0026] Attapulgite: 25%

[0027] Mosquito repellent: 14%;

[0028] Antioxidant MD697: 0.5%;

[0029] Light stabilizer 783: 0.5%.

[0030] The preparation method is:

[0031] Roast attapulgite at 200°C for 4 hours, add attapulgite and mosquito repellent uniformly according to the proportion of the above formula, then add the antioxidant and light stabilizer in the weight percentage of the formula into the kneading pot, knead to the coating state, After granulation, it is made into a compound, and then mixed evenly with polyamide 6, put into a twin-screw extruder for mixing, extruding, and granulating to obtain mosquito repellent nylon 6 masterbatch. The temperature of the twin-screw extruder is 270°C.

[0032] (2) The preparation method of mosquito repelling nylon 6 fiber

[0033] Mix nylon 6 slic...

Embodiment 2

[0035] (1) Preparation of mosquito repellent masterbatch

[0036] The weight percent of each composition in the masterbatch is:

[0037] Fiber grade polyamide 6: 65%;

[0038] Attapulgite: 15%

[0039] Mosquito repellent: 19%;

[0040] Antioxidant MD697: 0.5%

[0041] Light stabilizer 783: 0.5%;

[0042] Roast attapulgite at 300°C for 3 hours, add attapulgite and mosquito repellent evenly according to the proportion of the above formula, then add the antioxidant and light stabilizer in the weight percentage of the formula into the kneading pot, knead to the coating state, After granulation, it is made into a compound, and then mixed evenly with polyamide 6, put into a twin-screw extruder for mixing, extruding, and granulating to obtain mosquito repellent nylon 6 masterbatch.

[0043] (2) The preparation method of mosquito repelling nylon 6 fiber

[0044] Mix nylon 6 slices with the above-mentioned mosquito repellent nylon 6 masterbatch in a weight ratio of 80:20, and use...

Embodiment 3

[0046] (1) Preparation of mosquito repellent masterbatch

[0047] The weight percent of each composition in the masterbatch is:

[0048] Fiber grade polyamide 6: 70%;

[0049] Attapulgite: 15%

[0050] Mosquito repellent: 14%;

[0051] Antioxidant MD697: 0.5%

[0052] Light stabilizer 783: 0.5%;

[0053] Preparation:

[0054] Roast attapulgite at 400°C for 2 hours, add attapulgite and mosquito repellent evenly according to the proportion of the above formula, then add the antioxidant and light stabilizer in the weight percentage of the formula into the kneading pot, knead to the coating state, After granulation, it is made into a compound, and then mixed evenly with polyamide 6, put into a twin-screw extruder for mixing, extruding, and granulating to obtain mosquito repellent nylon 6 masterbatch.

[0055] (2) The preparation method of mosquito repellent nylon 6 fiber is: mix nylon 6 slices with the above-mentioned mosquito repellent nylon 6 masterbatch according to the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
Login to view more

Abstract

The invention provides a mosquito-dispelling polyamide 6 fiber and a preparation method thereof. The preparation method comprises the following steps of: after adsorbing mosquito-dispelling ester to attapulgite, adding an additive and polyamide 6 resin; extruding in a double-screw extruder and granulating to prepare mosquito-dispelling polyamide 6 master batch, wherein the mosquito-dispelling polyamide master batch comprises the following materials in percentage by weight: 60-70 percent of fiber-scale polyamide 6 resin, 15-30 percent of attapulgite, 0.1-1 percent of antioxidant, 0.1-1 percent of light stabilizer 78300 and 5-15 percent of mosquito-dispelling ester, wherein the antioxidant is a composition of MD 697 and one of a hindered phenolic antioxidant, a phosphite ester antioxidant and thiodipropionate antioxidant; and performing blended spinning on polyamide 6 slices and the mosquito-dispelling polyamide 6 master batch according to the weight ratio of80-90:10-20 to prepare the mosquito-dispelling polyamide 6 fiber. The mosquito-dispelling polyamide 6 fiber has the advantages of lasting mosquito-dispelling effect, simple process, low cost, wide application and the like.

Description

technical field [0001] The invention relates to the technical field of modified fibers, in particular to a mosquito-repelling nylon 6 fiber and a preparation method thereof. Background technique [0002] Nylon 6 fiber has the characteristics of high breaking strength, excellent wear resistance, small specific gravity, good elasticity and hygroscopicity, excellent chemical stability, and anti-mold and moth resistance. Therefore, it is widely used in socks, underwear, clothing fabrics, non-woven fabrics, especially Especially in the fields of clothing, hosiery and nonwoven fabrics. With the rapid increase of domestic nylon production, the market competition for conventional products has intensified. The development of high-tech and high value-added products has become an urgent problem to be solved in the nylon industry. [0003] Preparation of textiles with mosquito repellent effect has been reported in patents, such as patents CN1468983A and CN1468984 using DEET and PP melt ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/90D01F1/10D01D5/08D01D5/253
Inventor 尹翠玉李金福刘校奎仵君粉
Owner HANGZHOU XINFU TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap