Production technology of preprocessing copper-clad steel wire matrix

A production process and technology of copper-clad steel, applied in metal material coating process, manufacturing tools, metal processing equipment and other directions, can solve the problems of poor bonding force and produce a large amount of acid mist waste liquid, etc., and achieve good anti-oxidation effect. Solve the effect of poor adhesion and easy cleaning

Active Publication Date: 2012-10-10
ZHEJIANG PUJIANG BAICHUAN IND
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the problems that the copper layer of the copper-clad steel wire produced in the traditional process is not well bonded to the substrate, and a large amount of acid mist and waste liquid are generated in the producti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The present invention is further described below.

[0016] A production process for the pretreatment of a copper-clad steel wire substrate, comprising the following steps in sequence.

[0017] (1) Peeling: Oxidation of the steel wire under natural conditions will generate an excessively thick oxide layer. Because the oxide layer is brittle and has low extensibility, it needs to be peeled off. The steel wire is derusted and peeled by machinery to remove the oxide layer on the surface of the steel wire. , Specifically, the steel wire is processed into a steel wire matrix with a diameter of 6.5mm or 5.5mm.

[0018] (2) Steel wire brush to remove rust, after mechanical shelling, use a steel wire brush to wipe off the residual oxide layer on the surface of the steel wire substrate.

[0019] (3) Pickling, pickling with a hydrochloric acid solution with a volume ratio of 50%, further removing the oxide layer remaining on the surface of the steel wire substrate due to incomple...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention, relating to a production technology of copper-clad steel, particularly discloses a production technology of preprocessing a copper-clad steel wire matrix, successively comprising the following steps: husking, derusting with a wire brush, pickling, washing, boronizing, drawing, secondary washing, drying and spooling, and ammonia decomposition tempering. The technology has the following advantages: little pollution in the production process, complete treatment of the surface oxidation layer of the steel wire, bright surface of the steel wire, good anti-oxidation effect, and good binding force between the processed steel wire and the copper layer in the subsequent electroplating process.

Description

technical field [0001] The invention relates to a production process of copper-clad steel, in particular to a production process of pre-treatment of copper-clad steel wire matrix. Background technique [0002] Copper-clad steel wire is a new type of composite wire made of a steel core with a layer of copper on its surface and then drawn. This product not only has the strength and toughness of steel, but also has the good conductivity and corrosion resistance of copper. It has become an updated product of traditional pure copper single wire and is widely used in communications, transportation, metallurgy, electronic instruments, machinery, power transmission etc. However, copper-clad steel wire has always had a common industry problem of poor bonding force, which has not been effectively solved for a long time. After analysis and research, it is found that the pre-treatment of copper-clad steel substrate-steel wire has a great influence on the bonding force. [0003] The tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C8/40C21D1/18C21D1/76C21D8/06C23F17/00B24B27/033
Inventor 张鸿翔陈金兰杨相艳潘超鹰方彪董毓敏
Owner ZHEJIANG PUJIANG BAICHUAN IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap