Steel pipeline anticorrosive material and preparation method of steel pipeline anticorrosive material
A technology for anti-corrosion materials and pipes, applied in anti-corrosion coatings, coatings, etc., can solve problems such as poor low-temperature toughness, insufficient use, and hard-to-find base materials, etc., achieve high-temperature indentation hardness, high impact toughness, and ensure production capacity Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0031] Example 1
[0032] In this embodiment, we adopt the following steps to make:
[0033] 3 parts of high-density polyethylene refined to more than 200 mesh, 26 parts of PPB4228, 25 parts of EPS30R, 2.4 parts of titanium dioxide, 1.2 parts of antioxidants, 1.2 parts of lubricants, 0.6 parts of styrene, 0.6 parts of diisoperoxide After the propylbenzene is uniformly mixed in a high-speed mixer, it is extruded, stretched, air-cooled, and pelletized by a reactive twin-screw extruder with a length-to-diameter ratio of 52:1. per minute, the steel pipeline anti-corrosion material with high Vicat, high hardness and good low temperature toughness can be obtained. 48 kJ / ㎡.
Example Embodiment
[0034] Example 2
[0035] In this embodiment, we adopt the following steps to make:
[0036] 6 parts of high-density polyethylene refined to more than 200 mesh, 50 parts of PPB8101, 2.2 parts of carbon black, 1.0 part of antioxidant, 0.3 part of lubricant, 0.4 part of 2,6-di-tert-butyl-4-cresol, After 0.5 part of benzoyl peroxide was uniformly mixed in a high-speed mixer, it was extruded, stretched, air-cooled, and pelletized by a reactive twin-screw extruder with a length-to-diameter ratio of 52:1, and the temperature was set at 180°C. When the rotation speed is set to 180 rpm, the steel pipeline anti-corrosion material with high Vicat, high hardness and good low temperature toughness can be obtained. mm, low temperature impact strength 50 kJ / ㎡.
Example Embodiment
[0037] Example 3
[0038] In this embodiment, we adopt the following steps to make:
[0039] 8 parts of high-density polyethylene refined to more than 200 mesh, 48 parts of PPK8303, 1.8 parts of carbon black masterbatch, 0.6 parts of antioxidants, 0.6 parts of lubricants, 0.2 parts of turpentine, 0.4 parts of di-tert-butyl peroxide After mixing evenly in a high-speed mixer, it was extruded, stretched, air-cooled, and pelletized by a reactive twin-screw extruder with a length-to-diameter ratio of 52:1. The temperature was set at 220°C and the rotational speed was set at 280 rpm. , the steel pipeline anti-corrosion material of the present invention with high Vicat, high hardness and good low temperature toughness can be obtained, the Vicat indentation hardness at 155°C and 23°C is 0.02 mm, the indentation hardness at 90°C is 0.11 mm, and the low temperature impact strength is 52 kJ / ㎡.
PUM
Property | Measurement | Unit |
---|---|---|
Indentation hardness | aaaaa | aaaaa |
Indentation hardness | aaaaa | aaaaa |
Low temperature impact strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap