High-temperature resistant aluminium alloy and preparation method thereof

A technology of aluminum alloy and high temperature resistance, applied in the field of high temperature resistant aluminum alloy and its preparation, can solve problems such as deformation and easy occurrence of bubbles, and achieve the effects of reasonable formula, high density, and simple and convenient production.

Inactive Publication Date: 2013-01-09
浙江艾默樱零部件有限公司
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, manufacturers of stoves and radiators use conventional aluminum alloys to manufacture aluminum bu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0009] Example 1: Put 800 kg of aluminum ingots into the furnace according to the weight ratio; add 130 kg of silicon and 3 kg of iron in sequence; when the furnace temperature rises to 780°C, add 12 kg of nickel, 15 kg of manganese, 38 kg of copper and Magnesium 2 kg; after smelting and stirring uniformly, the gas and impurities in the aluminum liquid are precipitated; the furnace is kept at 675°C; the cold chamber die-casting machine with three-stage injection is used for die-casting; the mold design cavity uses the center feed; the die-casting The formed aluminum alloy workpiece is placed in an oven for heat treatment: firstly adjust the oven temperature to 200°C, bake for 2.1 hours, then increase the oven temperature to 390°C, bake for 1 hour, and finally increase the oven temperature to 430°C, bake for 2.3 Hours, after 2.4 hours of heat preservation, open the oven and cool to room temperature naturally. The heat-resistant aluminum alloy parts made by heat treatment have go...

Example Embodiment

[0010] Example 2: a. Put 790 kilograms of aluminum ingots into a furnace for melting, b. Add 123 kg of silicon, 5 kg of iron and 0.5 kg of zinc in sequence. When the furnace temperature rises to 785°C, add 15 kg of nickel, 12 kg of manganese, 50 kg of copper and 1.5 kg of magnesium, followed by 1.8 kg of trace element chromium. 0.1 kg of zirconium, 0.4 kg of titanium, 0.7 kg of antimony; c. After smelting and stirring uniformly, the gas and impurities in the aluminum liquid are separated out, d. Keep the furnace constant at 680°C, e. Die casting using a cold chamber die casting machine with three-stage injection, f. Mold design cavity adopts center feeding, g. Put the die-casting aluminum alloy workpiece into an oven for heat treatment. First, adjust the oven temperature to 205°C, bake for 2.3 hours, then increase the oven temperature to 380°C, bake for 1.5 hours, and finally increase the oven temperature to 440°C, and bake After making it for 2.4 hours and keeping it warm ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-temperature resistant aluminium alloy and a preparation method thereof. The high-temperature resistant aluminium alloy comprises 75.0-82.0 wt% of Al, 11.0-14.0wt% of Si, 3.0-7.0wt% of Cu, 0.9-1.9wt% of Mn, 0-0.5wt% of Fe, 0.8-2.1wt% of Ni, 0-0.25wt% of Mg, 0-0.1wt% of Zn, and 0-0.50 wt% of impurities. The preparation method comprises the following steps: melting, charging, stirring for precipitation, keeping a constant temperature, casting, feeding, conducting heat treatment, and baking. According to the invention, the problem that conventional aluminium alloy is easy to foam, deform, and the like in the case of high temperature can be effectively solved, the formula is reasonable, and the preparation method is simple.

Description

Technical field [0001] The invention relates to an aluminum alloy and a preparation method thereof, in particular to a high temperature resistant aluminum alloy and a preparation method thereof. Background technique [0002] At present, manufacturers of cooktops and radiators use conventional aluminum alloys to manufacture cooktop aluminum burners, components, radiator fins and other components, which are prone to bubbles and deformation during use. Summary of the invention [0003] The purpose of the present invention is to provide a high-temperature resistant aluminum alloy and a preparation method thereof that can effectively solve the phenomenon that conventional aluminum alloys are easily foamed and deformed at high temperature, have a reasonable formula, and a simple manufacturing method. [0004] In order to achieve the above objective, the present invention is achieved through the following technical solutions. High temperature resistant aluminum alloy, its weight percentag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C21/02C22C1/02
Inventor 陈雪峰郑奇龙张顺德
Owner 浙江艾默樱零部件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap