Highlight scratch resistance agent and process for preparing highlight scratch resistance transparent PVC thin film by applying same

A technology of PVC film and anti-scratch agent, which is applied in the direction of surface coating liquid devices, coatings, and pre-treated surfaces, etc., which can solve the problem that the anti-scratch performance and impact resistance of PVC films cannot meet the needs and cannot meet the needs of consumers. Requirements, film can not protect and other problems, to achieve good decorative effect, high production efficiency, improve the effect of scratch resistance

Inactive Publication Date: 2013-05-01
DONGGUAN GUODING OPTICAL MEMBRANE TECH
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the existing film materials are made of PVC film, but the scratch resistance of this type of film is poor. Damaged, the damaged film not only cannot protect the above-mentioned door panels, partition walls, wardrobes, etc., but also seriously affects the aesthetics of the above-mentioned products, loses its decorative effect, and cannot meet the requirements of consumers; The surface of the PVC film is coated with a surface treatment agent to improve the scratch resistance and water resistance of the film, but the curing degree of the existing surface treatment agent on the surface of the PVC film is low, resulting in the scratch resistance and impact resistance of the PVC film. Sex, etc. are still not enough to meet the needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A high-gloss anti-scratch agent, which consists of the following components by weight:

[0043] 95 parts of oily polyurethane, 15 parts of isocyanate, 0.8 part of cobalt soap drier, 0.1 part of erucamide, 37 parts of methyl ethyl ketone, and 38 parts of ethyl ester.

[0044] The process of preparing a high-gloss scratch-resistant transparent PVC film using the high-gloss anti-scratch agent of this embodiment includes the following process steps:

[0045] Step (1): Take the base film, which is a PVC film;

[0046] Step (2): Mix and stir oily polyurethane, isocyanate, cobalt soap drier, erucamide, butanone, and ethyl ester according to the proportion, and prepare a high-gloss anti-scratch agent. The viscosity of the high-gloss anti-scratch agent is 35cps .

[0047] Step (3): Put the high-gloss anti-scratch agent prepared in step (2) into the coating trough of the coater.

[0048] Step (4): In the coating trough, select an anilox roller engraved with mesh wires interwov...

Embodiment 2

[0053] A high-gloss anti-scratch agent, which consists of the following components by weight:

[0054] 97 parts of oily polyurethane, 17 parts of isocyanate, 0.9 part of cobalt soap drier, 0.3 part of erucamide, 39 parts of butanone, and 38 parts of ethyl ester.

[0055] The process of preparing a high-gloss scratch-resistant transparent PVC film using the high-gloss anti-scratch agent of this embodiment includes the following process steps:

[0056] Step (1): Take the base film, which is a PVC film;

[0057] Step (2): Mix and stir oily polyurethane, isocyanate, cobalt soap drier, erucamide, methyl ethyl ketone, and ethyl ester in proportion to prepare a high-gloss anti-scratch agent. The viscosity of the high-gloss anti-scratch agent is 45cps .

[0058] Step (3): Put the high-gloss anti-scratch agent prepared in step (2) into the coating trough of the coater.

[0059] Step (4): In the coating trough, select an anilox roller engraved with mesh wires interwoven into a patter...

Embodiment 3

[0064] A high-gloss anti-scratch agent, which consists of the following components by weight:

[0065] 100 parts of oily polyurethane, 20 parts of isocyanate, 1 part of cobalt soap drier, 0.5 parts of erucamide, 40 parts of butanone, and 40 parts of ethyl ester.

[0066] The process of preparing a high-gloss scratch-resistant transparent PVC film using the high-gloss anti-scratch agent of this embodiment includes the following process steps:

[0067] Step (1): Take the base film, which is a PVC film;

[0068] Step (2): Mix and stir oily polyurethane, isocyanate, cobalt soap drier, erucamide, methyl ethyl ketone, and ethyl ester in proportion to prepare a high-gloss anti-scratch agent. The viscosity of the high-gloss anti-scratch agent is 40cps .

[0069] Step (3): Put the high-gloss anti-scratch agent prepared in step (2) into the coating trough of the coater.

[0070] Step (4): In the coating trough, select an anilox roller engraved with mesh wires interwoven into a patter...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of a decorative film material, in particular to a highlight scratch resistance agent and a process for preparing a highlight scratch resistance transparent PVC (Poly Vinyl Chloride) thin film by applying the same. The highlight scratch resistance agent consists of the following components in part by weight: 95 to 105 parts of oil polyurethane, 15 to 25 parts of curing agent, 0.8 to 1.2 parts of drier, 0.1 to 1 part of smooth agent and 75 to 85 parts of organic solvent. The highlight scratch resistance agent disclosed by the invention has the characteristics of good toughness, high hardness, strong scratch resistance and high brightness; the process for preparing the highlight scratch resistance transparent PVC thin film by applying the highlight scratch resistance agent adopts a method of directly coating a highlight scratch resistance coating on a PVC thin film, adopts a simple preparation process, has high production efficiency, requires a small quantity of production equipment, can reduce cost and is beneficial to general popularization and application; and the prepared highlight scratch resistance transparent PVC thin film has the advantages of high hardness, good scratch resistance, flat surface, high brightness and stable quality.

Description

technical field [0001] The invention relates to the technical field of decorative film materials, in particular to a high-gloss anti-scratch agent and a process for preparing a high-gloss anti-scratch transparent PVC film using the same. Background technique [0002] With the development of the economy and the improvement of people's living standards, people have higher and higher requirements for building materials and furniture such as interior door panels, partition walls, and wardrobes. Damaged by various mechanical forces such as collisions, depressions, and scratches. In recent years, the practice of attaching various membrane materials on the surface of building material panels has gradually emerged in the above-mentioned industries. It can not only protect the surface of the above-mentioned building material panels For protection, but also to achieve a good decorative effect. [0003] Most of the existing film materials are made of PVC film, but the scratch resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D7/12C08J7/04C08L27/06B05D3/02B05D3/00
Inventor 林丽芬
Owner DONGGUAN GUODING OPTICAL MEMBRANE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com