Microencapsulation red phosphorus fire retardation antistatic polyethylene pipe composition

A technology for microencapsulating red phosphorus and polyethylene pipes, applied in the field of plastic processing, can solve problems such as poor flame retardant effect, and achieve the effects of good physical and mechanical properties, low raw material cost and low density

Inactive Publication Date: 2013-05-08
山东远洋塑胶工业有限公司
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] According to the deficiencies in the prior art, the technical problem to be solved by the present invention is to provide a microencapsulated red phosphorus flame-retardant antistatic polyethylene pipe composition to solve the problem that the flame-retardant effect of microencapsulated red phosphorus alone is not good. problems, the flame retardant system is used in combination with antistatic masterbatch to obtain a pipe composition with excellent flame retardant properties, antistatic properties and good mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microencapsulation red phosphorus fire retardation antistatic polyethylene pipe composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～3

[0032] Table 1 is the embodiment of the present invention and comparative example

[0033] raw material

Example 1

Example 2

Example 3

Comparative example 4

Comparative example 5

High-density polyethylene

53.2

54.2

43.2

100

100

Linear Low Density Polyethylene

10

20% conductive carbon black masterbatch

30

30

30

30

30

Microencapsulated red phosphorus

6

7

9

12

14

MCA

8

10

6

Dispersant

1.5

1.5

1.5

1.5

1.5

Titanate coupling agent

1.0

1.0

1.0

1.0

Aluminate coupling agent

1.0

Antioxidant 1010

0.15

0.15

0.15

0.15

0.15

Antioxidant 168

0.15

0.15

0.15

0.15

0.15

[0034] The sample preparation method of embodimen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a microencapsulation red phosphorus fire retardation antistatic polyethylene pipe composition, and belongs to the technical field of plastic processing. The composition comprises the following raw materials, by weight, 45-60 parts of a polyethylene resin, 30 parts of an electric conduction carbon black master batch, 6-10 parts of microencapsulation red phosphorus, 6-10 parts of a melamine isocyanurate, 1.0-3.0 parts of a coupling agent, 0.1-0.3 part of an antioxidant, and 1.0-3.0 parts of a dispersing agent. With the present invention, the problem of not good fire retardation effect during fire retardation of polyethylene through single microencapsulation red phosphorus is solved; a synergetic fire retardation agent MCA is added so as to reduce the amount of the red phosphorus and improve a fire retardation effect of the composition; the microencapsulation red phosphorus fire retardation antistatic polyethylene pipe composition is an environmental protection type material, and has characteristics of good extrusion processability and good mechanical property; and compared with the bromine-antimony fire retardation system, the composition has characteristics of low raw material cost, low density, good economic benefits, and good market application prospects.

Description

technical field [0001] The invention relates to a microencapsulated red phosphorus flame-retardant antistatic polyethylene pipe material composition, which belongs to the technical field of plastic processing. Background technique [0002] Polyethylene pipes have the advantages of low cost, light weight, convenient installation, and environmental protection. With the promotion of national policies, they are widely used in various fields. Among them, in addition to the physical and mechanical properties of general plastic pipes, polyethylene pipes for mining should also meet the special requirements of coal mines, that is, they must have antistatic properties and self-extinguishing properties, and the combustion products must not be toxic. Polyethylene is an organic polymer material with a very high volume resistivity of 10 16-20 Ω / cm, static electricity will be generated by friction, and it will accumulate on the plastic surface, which may cause fire and gas explosion. Ther...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08K13/06C08K9/10C08K3/02C08K3/04C08K5/3492F16L9/12
Inventor 朱新华陈勇周金勇
Owner 山东远洋塑胶工业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap