Polyamide-based cooling fiber and yarn

A nylon base and fiber technology, applied in fiber treatment, fiber chemical characteristics, yarn and other directions, can solve problems such as rising and difficulty in maintaining cooling characteristics, and achieve the effects of improving the quality of finished products, optimizing the spinning process, and strengthening control

Active Publication Date: 2013-05-08
ZHEJIANG LANTIANHAI FAB TECHNOLAGY CO LTD
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although jade fiber has cooling properties, the temperature of the fabric made of this fiber will continue to rise as it contacts the skin after being worn for a long time, making it difficult to maintain a lasting cooling property

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyamide-based cooling fiber and yarn
  • Polyamide-based cooling fiber and yarn
  • Polyamide-based cooling fiber and yarn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] The cooling masterbatch formula is: 65 parts by weight of PA6, 10 parts by weight of jade powder, 3 parts by weight of zirconia powder, 8 parts by weight of silicon dioxide powder, 1 part by weight of stearic acid dispersant, modified polyphenylene 2 parts by weight of ethylene dispersant, 2 parts by weight of low-molecular wax dispersant, and 1 part by weight of titanate coupling agent.

[0049] Nylon-based cooling fiber, made by the following methods:

[0050] (1) Use cooling masterbatch as raw material to make slices;

[0051] (2) Dry the slices: the drying temperature is 150°C, the drying time is 10 hours, and the dew point of the compressed air during drying is -58°C, so that the water content of the slices is reduced to below 30PPM;

[0052] (3) Spin the slices through the spinning box to make nylon-based cooling fibers: the slices are heated in the spinning box to form a thin stream of spinning melt, which is sprayed out from the spinneret of the spinning box ,...

Embodiment 2

[0056] The cooling masterbatch formula is: 66 parts by weight of PA6, 12 parts by weight of jade powder, 4 parts by weight of zirconia powder, 4 parts by weight of silicon dioxide powder, 2 parts by weight of stearic acid dispersant, modified polyphenylene 3 parts by weight of ethylene dispersant, 3 parts by weight of low molecular weight wax dispersant, and 2 parts by weight of titanate coupling agent.

[0057] Nylon-based cooling fiber, made by the following methods:

[0058] (1) Use cooling masterbatch as raw material to make slices;

[0059] (2) Dry the slices: the drying temperature is 160°C, the drying time is 12 hours, and the dew point of the compressed air is -60°C during drying, so that the water content of the slices is reduced to below 30PPM;

[0060] (3) Spin the slices through the spinning box to make nylon-based cooling fibers: the slices are heated in the spinning box to form a thin stream of spinning melt, which is sprayed out from the spinneret of the spinni...

Embodiment 3

[0064] The cooling masterbatch formula is: 70 parts by weight of PA6, 15 parts by weight of jade powder, 5 parts by weight of zirconia powder, 10 parts by weight of silicon dioxide powder, 3 parts by weight of stearic acid dispersant, modified polyphenylene 4 parts by weight of ethylene dispersant, 4 parts by weight of low molecular wax dispersant, and 3 parts by weight of titanate coupling agent.

[0065] Nylon-based cooling fiber, made by the following methods:

[0066] (1) Use cooling masterbatch as raw material to make slices;

[0067] (2) Dry the slices: the drying temperature is 170°C, the drying time is 14 hours, and the dew point of the compressed air during drying is -62°C, so that the water content of the slices is reduced to below 30PPM;

[0068] (3) Spin the slices through the spinning box to make nylon-based cooling fibers: the slices are heated in the spinning box to form a thin stream of spinning melt, which is sprayed out from the spinneret of the spinning box...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to functional fiber and particularly relates to polyamide-based cooling fiber and yarn. The polyamide-based cooling fiber is prepared by the following method: (1) taking cooling masterbatch as a raw material, and cutting the cooling masterbatch into slices; (2) drying the slices; and (3) spinning the slices through a spinning box to produce the polyamide-based cooling fiber, wherein a formula for the cooling masterbatch comprises the following components: PA6, jade powder, zirconium dioxide powder, silica powder, stearic acid dispersant, polystyrene dispersant, low molecular wax dispersant and titanate coupling agent. The polyamide-based cooling fiber and yarn have the functions of fast heat absorption and fast heat dissipation so as to ensure lasting cooling characteristic.

Description

technical field [0001] The invention relates to functional fibers, in particular to a nylon-based cooling fiber and yarn. Background technique [0002] With the continuous refinement of the social division of labor, many production areas have higher and higher requirements for clothing. In addition to the dust-free production workshop, operators are also required to wear tight clothes from head to toe, which will inevitably bring new benefits to the comfort of operators. Inconvenient, especially in hot summer, this problem is more obvious. In order to improve the wearing comfort of clothing, people have carried out a lot of comfort research on fabrics, among which the research on cooling fabrics applied to protective clothing is undoubtedly a hot topic in recent years. In order to solve the above problems, people have thought of developing a fiber material with a cooling function——jade fiber. Jade in jade fiber is rich in minerals. Long-term application on human skin can i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/90D01F1/10D01D5/088D02G3/04
Inventor 张港
Owner ZHEJIANG LANTIANHAI FAB TECHNOLAGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com