High-performance epoxy resin asphalt warm mixing agent and preparation method thereof

A technology of epoxy resin and warm mix agent, which is applied in building insulation materials, building components, climate change adaptation, etc.

Inactive Publication Date: 2013-05-22
NANJING UNIV
View PDF5 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, domestic warm mix asphalt mixture technology has not been

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance epoxy resin asphalt warm mixing agent and preparation method thereof
  • High-performance epoxy resin asphalt warm mixing agent and preparation method thereof
  • High-performance epoxy resin asphalt warm mixing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0054] Example 1: Weigh 100 parts (parts by mass, the same below) epoxy resin bisphenol A glycidyl ether epoxy resin (E51) (provided by Wuxi Bluestar Petrochemical Co., Ltd.), and add 0.1 part of carbon black (N660) (Provided by Cabot, USA) and 0.2 parts of γ-(2,3 glycidoxy)propyltrimethoxysilane (KH-560) (provided by Nanjing Yudeheng Fine Chemical Co., Ltd.), heated to 80°C, Mechanically stirred for 30 minutes and cooled to room temperature to obtain component A of high-performance warm-mix epoxy resin asphalt warm-mixing agent.

Example Embodiment

[0055] Example 2: Weigh 100 parts of epoxy resin bisphenol A type glycidyl ether epoxy resin (E51), add 0.3 parts of carbon black (N660) and 0.5 parts of γ-(3,4 epoxy cyclohexane) ethyl Trimethoxysilane (KH-530) (provided by Nanjing Wanda Silicon Industry Co., Ltd.), heated to 80°C, mechanically stirred for 30 minutes, and cooled to room temperature to obtain component A of the high-performance warm-mix epoxy resin asphalt warm-mixing agent.

[0056] The preparation method of component B of high-performance warm-mix epoxy resin asphalt warm-mix agent is as follows:

Example Embodiment

[0057] Example 3: 119 parts of hexadecenyl succinic anhydride (HDSA) (provided by Dixie Chemical Company, USA), 1 part of mixed fatty acid amide (Licomont BS 100) (provided by Swiss Klein Company), and 3 parts of nonylphenol Provided by Huntsman), 5 parts of titanium dioxide (provided by Shanghai Jianghu Titanium White Chemical Products Co., Ltd.), 20 parts of liquid polysulfide rubber (provided by Toray Company of Japan) and 0.1 part of polysiloxane defoamer (BYK-A530) ) (Provided by Xiamen Kangdilong Trading Co., Ltd.), heat to 100°C, mix with a colloid mill for 30 minutes, and cool to room temperature to obtain component B of high-performance epoxy resin asphalt warm mix.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-performance epoxy resin asphalt warm mixing agent comprising a component A and a component B, wherein the component A is composed of epoxy resin, a reinforcing agent and a coupling agent; the component B mainly comprises a flexible curing agent, an accelerant, a reinforcing agent, a toughening agent and a defoaming agent; and the mass proportion of the component A to the component B is equal to (100:250)-(100:300). High-performance warm mixing epoxy resin asphalt prepared by using the high-performance epoxy resin asphalt warm mixing agent provided by the invention has the characteristics of lower mixing temperature, high strength, better high-temperature ductility resistance and low-temperature fracture resistance, longer construction time, simple construction process, low-carbon and environment friendliness and the like and is suitable for paving pavements of roads, bridges, tunnels, airfield runways and the like. The invention discloses a preparation method of the high-performance epoxy resin asphalt warm mixing agent.

Description

technical field [0001] The invention relates to an asphalt warm mix agent and a preparation method thereof. Background technique [0002] At present, the asphalt pavement in road construction basically adopts the traditional Hot Mixture Asphalt (HMA). HMA is a hot-mixed asphalt mixture. It heats the asphalt from normal temperature to about 140°C, heats the mineral material from normal temperature to 160-180°C, and then mixes the asphalt and mineral material at a high temperature of 160°C. , the HMA temperature after stirring is not lower than 150°C. The temperature during paving and rolling shall not be lower than 120°C. Heating asphalt and mineral materials to such a high temperature not only consumes a lot of energy, but also emits a lot of waste gas and dust during production and construction, which seriously affects the quality of the surrounding environment and the health of construction workers. Therefore, it is very necessary to study a green and environment-friend...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00C08L63/02C08K13/02C08K5/5435C08K5/1539C08K5/13C08K3/04C08K3/22C04B26/26
CPCY02A30/30
Inventor 谢鸿峰尹海燕王睿王治流程镕时
Owner NANJING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka