Fixture for forming proton exchange membrane fuel cell membrane electrode and preparation method of proton exchange membrane fuel cell membrane electrode

A fuel cell membrane and proton exchange membrane technology, applied in battery electrodes, circuits, electrical components, etc., can solve the problems of poor bonding strength of membrane electrodes, unfavorable electrochemical performance of proton exchange membrane fuel cells, affecting discharge performance, etc. The effect of excellent discharge performance, improved electrochemical performance and extended cycle life

Active Publication Date: 2015-09-16
CHANGZHOU INST OF ENERGY STORAGE MATERIALS &DEVICES
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] However, the existing technology is to directly use the traditional hot pressing method to prepare the membrane electrode. If a high-precision molding machine is not introduced, the obtained membrane electrode will have poor bonding strength, which will affect its discharge performance and is not conducive to further improving the proton Electrochemical Performance of Exchange Membrane Fuel Cells

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fixture for forming proton exchange membrane fuel cell membrane electrode and preparation method of proton exchange membrane fuel cell membrane electrode
  • Fixture for forming proton exchange membrane fuel cell membrane electrode and preparation method of proton exchange membrane fuel cell membrane electrode
  • Fixture for forming proton exchange membrane fuel cell membrane electrode and preparation method of proton exchange membrane fuel cell membrane electrode

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0056] The invention provides a method for preparing a membrane electrode of a proton exchange membrane fuel cell, comprising:

[0057] The anode diffusion layer, the anode catalyst layer, the proton exchange membrane layer, the cathode catalyst layer, and the cathode diffusion layer are sequentially placed between the first flat plate and the second flat plate placed in parallel, and the first flat plate and the second flat plate are provided with through hole, the screw rod connects the first plate and the second plate through the through hole;

[0058] The torque of the screw rod is set to 0.5N·m~5N·m, the first plate is provided with a screw hole, and the set screw rod tightens the second plate through the screw hole to complete the fixation;

[0059] The fixed first plate, the second plate, and the anode diffusion layer, anode catalyst layer, proton exchange membrane layer, cathode catalyst layer, and cathode diffusion layer placed between the first plate and the second p...

Embodiment 1

[0085] Spray 5mg / cm on a piece of 2cm×7cm anode carbon paper 2 Platinum ruthenium black catalyst to obtain catalyst anode layer; Spray coating 5mg / cm2 on another 2cm×7cm cathode carbon paper 2 Platinum black catalyst, to obtain the catalyst cathode layer; these two carbon papers are placed on both sides of a 3cm × 10cm Nafion115 membrane (purchased from DuPont), the catalyst is in contact with the Nafion115 membrane respectively, and then these membrane electrode assemblies are placed At figure 1 Between the first flat plate and the second flat plate of the clamp shown, both flat plates are made of steel plates;

[0086] The torque of the screw that connects and fixes the two plates is set to 1N·m~1.3N·m, the first plate is provided with a screw hole, and the set screw rod tightens the second plate through the screw hole, complete fixation;

[0087] Place the clamps with each assembly of the membrane electrode on a flat plate molding machine, heat at 200°C for 10 minutes, t...

Embodiment 2

[0090] Spray 2mg / cm on a piece of 2cm×2cm anode carbon paper 2 Platinum ruthenium black catalyst to obtain catalyst anode layer; spray 2mg / cm2 on another 2cm×2cm cathode carbon paper 2 Platinum black catalyst, to obtain the catalyst cathode layer; these two carbon papers are placed on both sides of a 3cm × 3cm Nafion117 membrane (purchased from DuPont), the catalyst is in contact with the Nafion117 membrane respectively, and then these membrane electrode assemblies are placed At figure 1 Between the first flat plate and the second flat plate of the fixture shown, both flat plates are made of alloy aluminum plates;

[0091] The torque of the screw rod that connects and fixes the two plates is set to 0.8N·m~1N·m, the first plate is provided with a screw hole, and the set screw rod tightens the second plate through the screw hole, complete fixation;

[0092] Place the fixed clamps with the membrane electrode components on a flat plate molding machine, heat at 240°C for 5 minut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
torqueaaaaaaaaaa
torqueaaaaaaaaaa
torqueaaaaaaaaaa
Login to View More

Abstract

The invention provides a fixture used for moulding of a proton exchange membrane fuel cell membrane electrode and a preparation method for the proton exchange membrane fuel cell membrane electrode. The preparation method comprises the following steps: membrane electrode components are placed between a first flat plate and second flat plate of the fixture in sequence; torque of a lead screw of the fixture is set as 0.5 Nm to 5Nm and a fastening lead screw abuts against the second flat plate through a screw hole in the first flat plate; and the fixture is heated at a temperature from 140 DEG C to 250 DEG C for 2 min to 30 min so that the proton exchange membrane fuel cell membrane electrode is obtained. According to the fixture used for moulding of the proton exchange membrane fuel cell membrane electrode and the preparation method for the proton exchange membrane fuel cell membrane electrode, the fixture is formed by the first flat plate and the second flat plate and the like and a mould pressing method for preparation of the membrane electrode is regulated, so that the discharging performance of the membrane electrode is good and electrochemical performance of a fuel cell can be improved. The preparation method for the proton exchange membrane fuel cell membrane electrode is simple and easy to operate, low in cost due to the fact that expensive mould pressing equipment is not needed and beneficial to popularization.

Description

technical field [0001] The invention relates to the field of fuel cells, in particular to a fixture for forming a membrane electrode of a proton exchange membrane fuel cell and a method for preparing the membrane electrode of a proton exchange membrane fuel cell. Background technique [0002] A fuel cell is a power generation device that converts chemical energy directly into electrical energy through an electrochemical reaction. Compared with traditional energy conversion systems, fuel cells have many advantages: for example, they are not limited by the Carnot cycle, and the energy conversion efficiency is high; the product is usually water, which has little environmental pollution. Therefore, fuel cells have received increasing attention in recent years. [0003] Among fuel cells, a proton exchange membrane fuel cell is a device that uses fuels such as methanol, hydrogen, and formic acid to generate electricity through a membrane electrode composed of an ion exchange memb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B25B11/00H01M4/88
CPCY02E60/50
Inventor 邢巍廖建辉张弘严亮李晨阳司凤占
Owner CHANGZHOU INST OF ENERGY STORAGE MATERIALS &DEVICES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com