Metal rustproof wax using emulsifying wax as main body and preparation method thereof

A technology for metal rust prevention and emulsifying wax, applied in wax coatings, anti-corrosion coatings, coatings, etc., can solve the problems of large amount of direct economic loss, loss of use value, easy corrosion of parts, etc., to achieve convenient use, good fluidity and The effect of salt spray resistance and good rust resistance

Active Publication Date: 2013-06-26
FULAIYIN AUTOMOBILE PARTS
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Under natural storage conditions, steel and iron metals are easy to rust due to environmental and other factors, thereby reducing or losing t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Embodiment 1: the metal antirust wax that takes emulsified wax as the main body, the parts by weight (kg) of its composition raw materials are: emulsified wax 55, 70# microcrystalline wax 40, ferrocene 1, film-forming resin 5, modified silicon Algae earth 4, glycerol triacetate 16, isoglycol monobutyl ether 0.7, modified pure acrylic emulsion 2, aluminum hydroxide 0.5, di-n-octyl tin dithioglycolate 0.6, octadecylamine 1.4, propylene glycol 0.8 , zirconia 6, alkylphenol polyoxyethylene ether 3, antioxidant 168 1 and sodium tripolyphosphate 2.

[0021] The preparation method of the metal antirust wax taking emulsified wax as the main body comprises the following steps:

[0022] (1) Preparation of film-forming resin:

[0023] The formula (kg) of film-forming resin is PVC resin 2, rosin 8, vinyl tris(β-methoxyethoxy) silane 1, polyvinyl acetate emulsion 4, zinc oxide 0.2, dioctyl maleate 5 , m-xylene 3, ethylene bisstearamide 3, potassium persulfate 0.2, polyacryl alcoho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a metal rustproof wax using emulsifying wax as a main body and a preparation method thereof. The metal rustproof wax consists of the following raw materials in parts by weight: 50-60 parts of emulsifying wax, 37-43 parts of 70# microcrystalline wax, 0.8-1.2 parts of ferrocene, 4-6 parts of film-forming resin, 3-5 parts of modified kieselguhr, 15-18 parts of vanay, 0.6-0.8 part of glycol monobutyl ether, 1-3 parts of modified pure acrylic emulsion, 0.4-0.6 part of aluminum hydroxide, 0.5-0.7 part of dimercaptoacetic acid isooctyl diisooctyl tin, 1.2-1.5 parts of octadecylamine, 0.7-0.9 part of propylene glycol, 5-7 parts of zirconia, 2-4 parts of alkylphenol polyoxyethylene ether, 0.9-1.1 parts of antioxygen 168 and 1-3 parts of sodium tripolyphosphate. By using the emulsifying wax as a main raw material, the metal rustproof wax disclosed by the invention has good rustproof performance and is convenient to use, and moreover modified kieselguhr and modified pure acrylic emulsion are added in the raw materials, so the rustproof wax disclosed by the invention has temperature resistance and surface smoothness which are better than those of the similar products, and has good flowability, salt fog resistance and humidity resistance.

Description

technical field [0001] The invention relates to a metal antirust wax mainly composed of emulsified wax and a preparation method thereof, belonging to the technical field of metal antirust. Background technique [0002] Under natural storage conditions, steel and iron metals are prone to corrosion due to environmental and other factors, thereby reducing or losing their use value, resulting in safety accidents and economic losses. The direct economic losses caused by metal corrosion in my country are huge every year. [0003] Metal corrosion is mainly divided into chemical corrosion and electrochemical corrosion in terms of mechanism. There are many reasons for corrosion, such as mechanical damage, surface defects, internal defects, environmental factors, etc. Common corrosion factors include contact with air, surface pollution, and electrochemical corrosion. and surface scratches. Contents of the invention [0004] The object of the present invention is to provide a ki...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D191/06C09D133/04C09D7/12C09D5/08
Inventor 姜国松
Owner FULAIYIN AUTOMOBILE PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap