Metal antirust wax with liquid paraffin as main body and preparation method thereof

A liquid paraffin, metal anti-rust technology, applied in wax coatings, anti-corrosion coatings, coatings and other directions, can solve the problems of large amount of direct economic loss, loss of use value, easy corrosion of parts, etc., to achieve convenient use, good fluidity and The effect of salt spray resistance and good rust resistance

Active Publication Date: 2013-06-26
FULAIYIN AUTOMOBILE PARTS
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Under natural storage conditions, steel and iron metals are easy to rust due to environmental and other factors, thereby reducing or losing their use value, resulting in safety accidents and economic losses. The direct economic losses caused by metal corrosion in my country are huge every year

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1: The metal antirust wax mainly taking liquid paraffin as the main body, the parts by weight (kg) of its raw materials are: liquid paraffin 98, kanaba wax 8, ferrocene 2, film-forming resin 2, modified pottery clay 3 , dibutyl phthalate 20, sodium lauryl ether sulfate 0.8, tung oil 0.3, dipentylamine 0.8, 2,6-di-tert-butyl-p-cresol 3, zinc oxide 1 and polyvinylpyrrolidone 1.5.

[0020] The preparation method of the metal antirust wax taking liquid paraffin as the main body comprises the following steps:

[0021] (1) Preparation of film-forming resin:

[0022] The formula (kg) of film-forming resin is 5 urea, 1 anilinomethyltriethoxysilane, 3 tributyl citrate, 6 citric acid, 0.3 iron oxide, 3 epoxy linseed oil, 2 xylene, liquid Paraffin wax 3, potassium persulfate 0.2, polyacryl alcohol 0.3, dibutyl phthalate 0.3; the preparation method is as follows:

[0023] a: Add tributyl citrate, citric acid, anilinomethyltriethoxysilane, epoxy linseed oil, xylene, dib...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a metal antirust wax with liquid paraffin as a main body and a preparation method of the metal antirust wax. The metal antirust wax comprises the following ingredient raw materials in parts by weight: 95-100 parts of liquid paraffin, 5-10 parts of carnauba wax, 1-3 parts of ferrocene, 1-3 parts of binder resin, 2-4 parts of modified kaolin, 18-22 parts of dibutyl phthalate, 0.7-0.9 parts of sodium lauryl ether sulfate, 0.2-0.4 parts of Chinese wood oil, 0.7-0.9 parts of diamylamine, 2-4 parts of 2,6-ditert-butyl-4-methyl phenol, 0.8-1.2 parts of zinc oxide, and 1-2 parts of polyvinylpyrrolidone. The metal antirust wax disclosed by the invention takes the liquid wax as the main raw material, has good antirust performance and is convenient in use, the modified kaolin is added in the raw materials, the metal antirust wax disclosed by the invention is more excellent in temperature resistance performance and in surface smoothness when compared with like product, and has excellent fluidity, salt fog resistance, and heat and humidity resistance.

Description

technical field [0001] The invention relates to a metal antirust wax mainly composed of liquid paraffin and a preparation method thereof, belonging to the technical field of metal antirust. Background technique [0002] Under natural storage conditions, steel and iron metals are prone to corrosion due to environmental and other factors, thereby reducing or losing their use value, resulting in safety accidents and economic losses. The direct economic losses caused by metal corrosion in my country are huge every year. [0003] Metal corrosion is mainly divided into chemical corrosion and electrochemical corrosion in terms of mechanism. There are many reasons for corrosion, such as mechanical damage, surface defects, internal defects, environmental factors, etc. Common corrosion factors include contact with air, surface pollution, and electrochemical corrosion. and surface scratches. Contents of the invention [0004] The object of the present invention is to provide a m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D191/06C09D7/12C09D5/08
Inventor 姜国松
Owner FULAIYIN AUTOMOBILE PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com