A kind of rapid vulcanization low-smoke halogen-free flame-retardant rubber cable material and its preparation method

A technology of rapid vulcanization and flame-retardant rubber, which is applied in the field of cable materials and its preparation, can solve problems such as poor low-temperature flexibility, decreased cold resistance, and decreased mechanical properties and processing properties of cable materials, and achieves good low-temperature flexibility, easy processing, and extrusion packaging good workmanship

Inactive Publication Date: 2016-01-06
GUILIN UNIV OF ELECTRONIC TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems that the addition of a large amount of flame retardant and smoke suppressant to the thermoplastic polyolefin low-smoke halogen-free flame-retardant cable material leads to a significant decrease in the mechanical properties and processing properties of the cable material, poor low-temperature flexibility, and a decrease in cold resistance, and provides a Rapidly vulcanized low-smoke halogen-free flame-retardant rubber cable compound and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) A rapidly vulcanized low-smoke, halogen-free, flame-retardant rubber cable material, consisting of the following raw materials in parts by weight:

[0031] Smoked sheet glue 20 parts;

[0032] 80 parts of styrene-butadiene rubber;

[0033] 140 parts of aluminum hydroxide;

[0034] 10 parts of white carbon black;

[0035] 1.5 parts of vinyltriethoxysilane;

[0036] 2 parts of zinc dimethyl dithiocarbamate;

[0037] 1.5 parts of sulfur;

[0038] 7 parts of zinc oxide;

[0039] 2 parts stearic acid;

[0040] Antioxidant 10101 parts;

[0041] (2) The mixing process of low-smoke, halogen-free and flame-retardant rubber cable materials is as follows:

[0042] First prepare the above-mentioned raw materials by weight, put the smoked sheet rubber masticated according to the conventional method into the roll gap of the started open rubber mixer, put in styrene-butadiene rubber after wrapping the rolls to make the rubber wrap the rolls, and then put in zinc oxide in t...

Embodiment 2

[0050] (1) A rapidly vulcanized low-smoke, halogen-free, flame-retardant rubber cable material, consisting of the following raw materials in parts by weight:

[0051] 20 parts crepe glue;

[0052] 80 parts of styrene-butadiene rubber;

[0053] 70 parts of aluminum hydroxide;

[0054] 70 parts of magnesium hydroxide;

[0055] 10 parts of zinc stannate;

[0056] 1.5 parts of γ-aminopropyltriethoxysilane;

[0057] 2 parts of zinc dimethyl dithiocarbamate;

[0058] 1.5 parts of macromolecular cross-linking agent;

[0059] 5 parts of zinc oxide;

[0060] 2 parts stearic acid;

[0061] Antioxidant 10101 parts;

[0062] (2) The mixing process of low-smoke, halogen-free and flame-retardant rubber cable materials is as follows:

[0063] First prepare the above raw materials by weight, put the crepe rubber masticated according to the conventional method into the roll gap of the open rubber mixer, and put in styrene-butadiene rubber after wrapping the rolls to make the rubber wr...

Embodiment 3

[0071] (1) A rapidly vulcanized low-smoke, halogen-free, flame-retardant rubber cable material, consisting of the following raw materials in parts by weight:

[0072] Smoked sheet glue 20 parts;

[0073] 80 parts of styrene-butadiene rubber;

[0074] 70 parts of magnesium hydroxide;

[0075] 70 parts of magnesium aluminum double hydroxide;

[0076] 10 parts of zinc borate;

[0077] 1.5 parts of vinyltriethoxysilane;

[0078] 2 parts of zinc dimethyl dithiocarbamate;

[0079] 1.5 parts of sulfur;

[0080] 5 parts of zinc oxide;

[0081] 2 parts stearic acid;

[0082] Antioxidant 10101 parts;

[0083] (2) The mixing process of low-smoke, halogen-free and flame-retardant rubber cable materials is as follows:

[0084] First prepare the above-mentioned raw materials by weight, put the smoked sheet rubber masticated according to the conventional method into the roll gap of the open rubber mixer, and put in styrene-butadiene rubber to wrap the rubber after wrapping the rolls, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
limiting oxygen indexaaaaaaaaaa
limiting oxygen indexaaaaaaaaaa
limiting oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a rapid-vulcanized low-smoke halogen-free flame retardant rubber cable material. The rapid-vulcanized low-smoke halogen-free flame retardant rubber cable material mainly comprises the following raw materials in parts by weight: 20-80 parts of natural rubber, 20-80 parts of butadiene-styrene rubber, 130-150 parts of flame retardant smoke suppression agent, 4-10 parts of flame retardant smoke suppression synergist, 1-3 parts of coupling agent, 1-3 parts of zinc dimethyldithiocarbamate, 1-5 of vulcanizing agent, 6-8 parts of zinc oxide, 1-3 parts of stearic acid and 1-2 parts of antioxidant. The rapid-vulcanized low-smoke halogen-free flame retardant rubber cable material has the beneficial effects that the cable material is easy to machine, an extruded wrapping technology is good, and products have good mechanical property and good low-temperature flexibility.

Description

technical field [0001] The invention relates to a cable material and a preparation method thereof, in particular to a rapidly vulcanized low-smoke halogen-free flame-retardant rubber cable material and a preparation method thereof. Background technique [0002] In order to reduce fire accidents caused by cable heating and burning, the use of flame-retardant cables is becoming more and more common; traditional halogen-containing flame-retardant cables will produce a lot of smoke and toxic, irritating and corrosive hydrogen halides in the event of a fire. Gas; smog can cause death and hinder firefighting and evacuation, hydrogen halide gas can corrode equipment and endanger human health. Therefore, it is mandatory to use halogen-free flame-retardant cables in places where many people gather, and the production of halogen-free flame-retardant cable materials is the key. [0003] For thermoplastic polyolefin low-smoke, halogen-free, flame-retardant cable materials, a large amou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L9/00C08L9/06C08K13/02C08K5/39C08K3/22C08K5/09C08K3/36C08K3/38C08K3/24
Inventor 戴培邦马传国何玉汝卢悦群
Owner GUILIN UNIV OF ELECTRONIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com