Preparation method of domestic ceramic dish

A manufacturing method and a technology for ceramic discs, which are applied in the field of ceramics, can solve the problems of insufficient gloss, insufficient thermal stability, waste of energy, etc. of daily-use ceramics, and achieve the effects of good gloss, increased fluidity, and uniform mud.

Inactive Publication Date: 2013-07-17
林潮清
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, daily-use ceramics are produced, but the gloss of the produced daily-use ceramics is not good enough, the thermal stability is not good enough, and the current production of daily-use ceramics is a serious waste of energy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of domestic ceramic dish
  • Preparation method of domestic ceramic dish
  • Preparation method of domestic ceramic dish

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for manufacturing a daily-use ceramic dish, the method comprising the following steps:

[0019] (1) Put the white mud and black mud in the ceramic clay for making ceramic raw materials into the beater according to the weight ratio of 2:1, and beat the ceramic clay into mud with the beater. The properties of white mud and black mud are different. Yes, the toughness of white mud is not as good as that of black mud. In this way, mixing white mud with black mud in a certain proportion will help to improve the quality of ceramic clay based on ceramic principles, and it will also help improve the quality of daily-use ceramic plates.

[0020] (2) Add a certain amount of water glass to the mud made in step (1), the weight of the mud and water glass is 2000:1, and then pour it into the mixer for stirring and mixing evenly.

[0021] (3) Inject the mud produced in step (2) into the ceramic plate mold, dry it automatically, evaporate the water evenly, demould after drying,...

Embodiment 2

[0030] A method for manufacturing a daily-use ceramic dish, the method comprising the following steps:

[0031] (7) Put the white mud and black mud in the ceramic clay for making ceramic raw materials into the beater according to the weight ratio of 2:1, and beat the ceramic clay into mud with the beater. The properties of white mud and black mud are different. Yes, the toughness of white mud is not as good as that of black mud. In this way, mixing white mud with black mud in a certain proportion will help to improve the quality of ceramic clay based on ceramic principles, and it will also help improve the quality of daily-use ceramic plates.

[0032] (8) Add a certain amount of water glass to the mud made in step (1). The weight of the mud and water glass is 2000:1, and then pour it into the mixer for stirring and mixing evenly.

[0033] (9) Inject the mud produced in step (2) into the ceramic plate mold, dry it automatically, evaporate the water evenly, demould after drying,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to the field of ceramic technology. The invention discloses a preparation method of a domestic ceramic dish, including the following steps of charging white and black clay in ceramic raw materials of ceramic clay at weight ratio of 2:1 into a beater, beating the ceramic clay into slurry with the beater, adding a certain amount of sodium silicate and then pouring into a blender, blending and mixing evenly to obtain a ceramic clay blank, coating coloured glaze on the prepared ceramic dish clay blank and placing the blank into a kiln for firing at a temperature of between 1250 and 1300 DEG C for 7.5-9.0 hours to obtain the domestic ceramic dish. The domestic ceramic dish prepared by the method has high luster and excellent thermal stability.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a ceramic manufacturing method. Background technique [0002] The Chinese invention patent number is: 201110416597.4 discloses a high-gloss daily-use ceramic glaze and its preparation method. The high-gloss daily-use ceramic glaze is composed of the following components calculated by weight percentage: 37-38% of potassium feldspar, 15-16% of kaolin, 4.5-6% of barium carbonate, 1.5-2% of lanthanum carbonate, and 1.6% of lithium carbonate. ~1.8%, zinc oxide 8~10%, zirconia 3~4%, phosphorus pentoxide 3~4%, quartz 22~24%. The preparation method of the high-gloss daily-use ceramic glaze comprises the following steps: mixing and pulverizing each raw material according to the proportion of the component formula, performing wet ball milling to obtain glaze slurry; then removing iron, sieving, and decomposing to obtain. The high-gloss daily-use ceramic glaze contains rare earth metal l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/00C04B41/86
Inventor 林潮清
Owner 林潮清
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com