Method for preparing magnetic/hollow double-shell layer print adsorbent by emulsion polymerization

A technology of emulsion polymerization and imprinting adsorption, which is applied in chemical instruments and methods, alkali metal compounds, alkali metal oxides/hydroxides, etc., can solve problems affecting the human central nervous system, endocrine disturbance, and disturbance of consciousness, and achieve significant Effects of recognition performance, reduction of non-specific adsorption, and good magnetic response properties

Inactive Publication Date: 2013-07-17
JIANGSU UNIV
View PDF4 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But some studies suggest that pyrethroid insecticides may predispose to disturbance of consciousness and seizu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing magnetic/hollow double-shell layer print adsorbent by emulsion polymerization
  • Method for preparing magnetic/hollow double-shell layer print adsorbent by emulsion polymerization
  • Method for preparing magnetic/hollow double-shell layer print adsorbent by emulsion polymerization

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 1, a kind of Pickering emulsion polymerization prepares the method for magnetic / hollow double-shell imprinted adsorbent, it is characterized in that carrying out according to the following steps:

[0039] (1) Hydrophilic Fe 3 o 4 Synthesis of Nanoparticles

[0040] 4. Mix 5380g of tetramethylammonium hydroxide and 22ml of deionized water into a solution, and stir mechanically at 70°C. Subsequently, 1.3gFeCl 3 ·6H 2 O and 0.5gFeCl 2 4H 2 O was dissolved in 6.0ml of water and transferred to a solution of tetramethylammonium hydroxide. After the mixture was stirred for 30 minutes, the prepared Fe was collected with a permanent magnet. 3 o 4 Nanoparticles. Wash several times with deionized water and ethanol. The prepared hydrophilic Fe 3 o 4 The nanoparticles were vacuum dried at 60°C.

[0041] (2) Synthesis of magnetic / hollow double-shell imprinted adsorbents

[0042] First, 0.05g of hydrophilic Fe 3 o 4 Nanoparticles, 0.286g NaCl and 0.15g attapulgite were ...

Embodiment 2

[0059] 1, a kind of Pickering emulsion polymerization prepares the method for magnetic / hollow double-shell imprinted adsorbent, it is characterized in that carrying out according to the following steps:

[0060](1) Hydrophilic Fe 3 o 4 Synthesis of Nanoparticles

[0061] 5. Mix 4369g of tetramethylammonium hydroxide and 22ml of deionized water into a solution, and stir mechanically at 70°C. Subsequently, 1.5gFeCl 3 ·6H 2 O and 0.5gFeCl 2 4H 2 O was dissolved in 6.0ml of water and transferred to a solution of tetramethylammonium hydroxide. After the mixture was stirred for 30 minutes, the prepared Fe was collected with a permanent magnet. 3 o 4 Nanoparticles. Wash several times with deionized water and ethanol. The prepared hydrophilic Fe 3 o 4 The nanoparticles were vacuum dried at 60°C.

[0062] (2) Synthesis of magnetic / hollow double-shell imprinted adsorbents

[0063] First, 0.08 g of prepared hydrophilic Fe 3 o 4 Nanoparticles, 0.355g NaCl and 0.2g attapulgi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Saturated adsorption capacityaaaaaaaaaa
Saturated adsorption capacityaaaaaaaaaa
Adsorption capacityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing magnetic/hollow double-shell layer print adsorbent by emulsion polymerization and belongs to the technical field of the preparation of environment function materials. Attapulgite is used as stabilizer; a few Fe3O4 nanometer particles are used as a magnetic separation carrier; a dispersion solution of hydrophilic Fe3O4 nanometer particles and attapulgite is used as a water phase; and a mixture of organic solvent hexadecane, cross-linking agent styrene, template molecule cyhalothrin, initiator azo isobutyric dimethyl ester and functional monomers acrylamide and tetra-vinyl pyridine is used as an oil phase. The water phase and the oil phase are mixed to prepare stable oil-in-water emulsion in an ultrasonic manner; and the magnetic hollow double-shell layer print polymer is prepared by emulsion polymerization. The magnetic hollow double-shell layer print polymer can be applied to selective recognition and separation of cyhalothrin in an aqueous solution. The magnetic hollow double-shell layer print polymer has a hollow double-layer structure, wherein the hollow structure can be used for effectively increasing adsorption capacity; the strength of the obtained printer polymer is enabled to be high by the inorganic particle layer in the shell layer; and the recognition points are unlikely to be damaged.

Description

technical field [0001] The invention relates to a method for preparing a magnetic hollow double-shell imprinted adsorbent by using Pickering emulsion polymerization, which belongs to the technical field of preparation of environmental functional materials. Background technique [0002] Pyrethroids are synthetic analogs of the natural insecticide permethrin. Due to its high efficacy at low doses, pyrethroids are used in agriculture instead of organochlorine and organophosphorus insecticides. In recent years, pyrethroids have been found in surface water and sediments. Although compared with organochlorine and organophosphorus pesticides, pyrethroid pesticides exhibit relatively low toxicity to mammals. However, some studies have shown that pyrethroid insecticides may easily cause disturbance of consciousness and seizures, affect the human central nervous system, and are also suspected of having endocrine disrupting effects. Therefore, it is necessary to selectively remove p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F212/08C08F220/56C08F2/44C08F2/22C08K3/22C08K3/34C08J9/28B01J20/26B01J20/30B01J20/28
Inventor 潘建明李林子戴江栋孟敏佳卫潇
Owner JIANGSU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap