Grinding and polishing synthetic fiber material preparation method

A technology of synthetic materials and fiber materials, applied in abrasives, manufacturing tools, metal processing equipment, etc., can solve problems such as no more detailed discussion, no clear solution, etc., and achieve the effect of low cost, flexibility and simple process

Active Publication Date: 2013-08-14
WUHAN INST OF GEOLOGICAL MINERALS
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The methods proposed in these patent documents have been greatly improved compared with the previous methods, but there are still certain limitations, especially for the polishing of heterogeneous substances, there is no clear solution in the literature, for example Naturally formed rock and ore aggregates have not been discussed in detail and solved in many literatures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for preparing a fiber composite material for grinding and polishing, characterized in that it comprises the following steps:

[0029] 1) Processing and treatment of fiber materials: cut the wool felt with a thickness of 10mm into a circle with a diameter of 250mm, and punch it into a honeycomb shape with a honeycomb aperture of 4mm and a hole distance of 8mm, and then place it in a polishing agent solution Soak in water for 3-4 hours, then remove and dry for later use.

[0030] The polishing agent solution is prepared from water, ammonium dichromate and oxalic acid, and the ammonium dichromate is baked at 150°C for 1 hour before the preparation, wherein the weight ratio of water to ammonium dichromate and oxalic acid is 1000:20 : 3, so that it can be fully dissolved at room temperature.

[0031] After soaking for 3-4 hours, the aqueous solution rich in ammonium dichromate and oxalic acid fills all the gaps in the wool felt. On the one hand, the solution reacts...

Embodiment 2

[0037] A method for preparing a fiber composite material for grinding and polishing, characterized in that it comprises the following steps:

[0038] 1) Processing and treatment of fiber materials: Cut the wool felt with a thickness of about 10mm into a circle (Φ=250mm) and punch it into a honeycomb shape. The honeycomb aperture is about 5mm and the hole distance is 9mm. Soak in water for 3-4 hours, then remove and dry for later use.

[0039] Step 1) The leaching solution is prepared from water, ammonium dichromate and oxalic acid, and the ammonium dichromate is baked at 155°C for 1.5 hours before preparation, and the weight ratio of water to ammonium dichromate and oxalic acid is correspondingly 1000:25:4, so that it can be fully dissolved at room temperature.

[0040] After soaking for 3-4 hours, the aqueous solution rich in ammonium dichromate and oxalic acid fills all the gaps in the wool felt. On the one hand, the solution reacts with impurities in the wool felt to reduc...

Embodiment 3

[0046] A method for preparing a fiber composite material for grinding and polishing, characterized in that it comprises the following steps:

[0047] 1) Processing and treatment of fiber materials: Cut the wool felt with a thickness of about 10mm into a circle (Φ=250mm) and punch it into a honeycomb shape with a honeycomb aperture of 6mm and a distance of 10mm, and then place it in the soaking solution Soak for 3-4 hours, then remove and dry for later use.

[0048] Step 1) The leaching solution is prepared from water, ammonium dichromate and oxalic acid, and the ammonium dichromate is baked at 160°C for 3 hours before preparation, and the weight ratio of water to ammonium dichromate and oxalic acid is correspondingly 1000:30:5, so that it can be fully dissolved at room temperature.

[0049] After soaking for 3-4 hours, the aqueous solution rich in ammonium dichromate and oxalic acid fills all the gaps in the wool felt. On the one hand, the solution reacts with impurities in t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apertureaaaaaaaaaa
Pitchaaaaaaaaaa
Apertureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a grinding and polishing synthetic fiber material preparation method. The fiber synthetic material preparation method includes and is characterized by including preliminarily processing fiber materials, penetrating thin glue, pressing a composite material uniformly mixed with polishing agent, strengthening plasticizer and adhesive, and integrally drying at constant temperature to enable the fiber materials, the polishing agent, the strengthening plasticizer and the like to be firmly solidified to form a uniform and elastic integral body. The synthetic materials have the advantages that the synthetic materials are quick polished, low in consumables, durable, wear-resisting, low in production cost, simple in technique, easy to realize industrial lives, and the like.

Description

technical field [0001] The invention relates to a preparation method of a fiber composite material for grinding and polishing. The obtained grinding and polishing fiber material has the advantages of fast glazing speed, less consumables, good friction resistance and the like, and can be widely used in industrial fields. Background technique [0002] Rock mineral aggregates are extremely complex and changeable heterogeneous substances formed by natural crustal changes. In geological prospecting, geotechnical engineering and environmental protection, it is often necessary to grind mineral rock aggregates into a certain thickness of light Slices, thin slices or polished surfaces for genetic analysis, composition research and structural research. The traditional polishing process is to attach a layer of navy, canvas or wool felt to a metal disc to form a polishing disc, and then make the polishing disc rotate at a high speed and continuously add polishing materials, so that the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B24D3/02B24D3/34B24D11/00
Inventor 张树淮牛焕友郑杨武育宁明星
Owner WUHAN INST OF GEOLOGICAL MINERALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap