High and low-temperature resistant porcelain glaze for enamel

A high-low temperature, enamel technology, applied in the field of enamel, can solve the problems of poor high temperature resistance, ceramics are easy to be frozen and cracked, high and low temperature resistance, etc., to achieve good glaze slurry performance, good glaze smoothness, The effect of excellent high and low temperature resistance

Inactive Publication Date: 2014-06-04
XIANGFENG ZHEJIANG METAL PROD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Enamel products are widely used in all aspects of life, but the enamel of the prior art is a kind of environmental protection ceramic glaze disclosed in the invention patent application of CN102372501A as the application publication number, which includes the following composition, and its mass fraction is: SiO 2 50-60%, A1 2 o 3 5-10%, CaO3-8%, ZnO5-10%, K 2 O2-4%, Na 2 O1-4%, B 2 o 3 2-7%, La 2 o 3 0.3-2%, also contains MgO, BaO and ZrO 2 , its total addition amount is ≤15%. This kind of ceramic glaze has poor performance in high and low temperature resistance. In winter, ceramics are easy to be frozen and cracked, and their high temperature resistance is also poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: a kind of high and low temperature resistant enamel material that is used for enamel, it is made by mixing the powder granular raw material of following parts by weight at a temperature of 1350 degrees: 22 parts of sodium silicate with a modulus of 2, oxidized 11 parts of aluminum, 10 parts of manganese dioxide, 6 parts of palladium oxide, 6 parts of high borate calcium borate, 23 parts of lead sulfate, 2 parts of talc; 7 parts of calcium carbonate, 8 parts of barium sulfate, 12 parts of zinc sulfate, 2 parts of titanium oxide .

[0011] The particle size of all raw materials is 30-32 mesh.

[0012] After testing, the performance of this embodiment is as follows: thermal expansion coefficient 50, conversion point (degrees) 580, expansion softening point (degrees) 660, sintering point (degrees) 680, softening point (degrees) 950, ball point (degrees) 1120, Hemisphere point (degrees) 1310; According to GB / T 7989-2003 "Determination of Boiling Hydrochloric A...

Embodiment 2

[0013] Embodiment 2: a kind of high and low temperature resistant enamel material that is used for enamel, it is made by mixing and melting the granular raw materials of following parts by weight at a temperature of 1300 degrees: 38 parts of sodium silicate with a modulus of 3.8, oxidized 19 parts of aluminum, 20 parts of manganese dioxide, 9 parts of palladium oxide, 9 parts of high borate calcium borate, 29 parts of lead sulfate, 4 parts of talc; 13 parts of calcium carbonate, 12 parts of barium sulfate, 19 parts of zinc sulfate, 9 parts of titanium oxide .

[0014] All raw materials had a particle size of 35-38 mesh.

[0015] After testing, the performance of this embodiment is as follows: thermal expansion coefficient 53, conversion point (degrees) 589, expansion softening point (degrees) 666, sintering point (degrees) 675, softening point (degrees) 948, ball point (degrees) 1130, Hemisphere point (degrees) 1330; According to GB / T 7989-2003 "Determination of Boiling Hydro...

Embodiment 3

[0016] Embodiment 3: a kind of high and low temperature resistant enamel material that is used for enamel, it is mixed and melted and stirred at the temperature of 1400 degrees by the powder granular raw material of following parts by weight and is made: modulus is 2.5 sodium silicate 25 parts, oxidized 15 parts of aluminum, 13 parts of manganese dioxide, 7 parts of palladium oxide, 6 parts of high borate calcium borate, 25 parts of lead sulfate, 2 parts of talc; 8 parts of calcium carbonate, 10 parts of barium sulfate, 15 parts of zinc sulfate, 3 parts of titanium oxide .

[0017] The particle size of all raw materials was 32-36 mesh.

[0018] After testing, the performance of this embodiment is as follows: coefficient of thermal expansion 48, conversion point (degrees) 600, expansion softening point (degrees) 685, sintering point (degrees) 692, softening point (degrees) 945, ball point (degrees) 1120, Hemisphere point (degrees) 1310; According to GB / T 7989-2003 "Determinati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to porcelain glaze and in particular relates to high and low-temperature resistant porcelain glaze for enamel. According to the technical scheme, the highnd low-temperature resistant porcelain glaze for enamel is prepared from the following raw materials in parts by weight: 22-38 parts of sodium silicate with the modulus of 2-3.8, 11-19 parts of aluminum oxide, 10-20 parts of manganese dioxide, 6-9 parts of palladium oxide, 6-9 parts of high-boron calcium borate, 23-29 parts of lead sulfate, 2-4 parts of talc, 7-13 parts of calcium carbonate, 8-12 parts of barium sulfate, 12-19 parts of zinc sulfate and 2-9 parts of titanium oxide. The high and low-temperature resistant porcelain glaze has excellent ultralow-temperature resistance and high-temperature resistance.

Description

technical field [0001] The invention relates to a ceramic glaze, in particular to a high and low temperature resistant enamel material for enamel. Background technique [0002] Enamel products are widely used in all aspects of life, but the enamel of the prior art is a kind of environmental protection ceramic glaze disclosed in the invention patent application of CN102372501A as the application publication number, which includes the following composition, and its mass fraction is: SiO 2 50-60%, A1 2 o 3 5-10%, CaO3-8%, ZnO5-10%, K 2 O2-4%, Na 2 O1-4%, B 2 o 3 2-7%, La 2 o 3 0.3-2%, also contains MgO, BaO and ZrO 2 , and its total addition amount is ≤15%. This kind of ceramic glaze has poor resistance to high and low temperatures. In winter, ceramics are easily cracked by freezing and have poor high-temperature resistance. Contents of the invention [0003] The object of the present invention is to provide a high and low temperature resistant enamel material for en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00
Inventor 王如松
Owner XIANGFENG ZHEJIANG METAL PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com