A kind of manufacturing method of nylon functional air-cleaning negative ion air-covered yarn

An air-coated yarn and air-cleaning technology is applied in the spinning field to improve production efficiency, odor and smoke.

Active Publication Date: 2016-07-27
ZHEJIANG YAXING FIBER
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, functional fibers have been mostly used in the specifications of polyester production, but the development of nylon functional products is far behind the level of domestic polyester factories. Domestic nylon chemical fiber production or development of nylon functional products The manufacturers of nylon are not common enough, and most of them focus on the production of conventional varieties. In fact, the hydrophilicity of nylon, the abrasion resistance of fibers, and the dyeing fastness are better than polyester, and it is more suitable for use in close-fitting clothing for the human body. Due to this characteristic, the functionality of nylon filaments used in body-fitting fabrics has been more and more developed and researched, hoping to closely combine the long-term health care of the human body and the application of environmentally friendly materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of manufacturing method of nylon functional air-cleaning negative ion air-covered yarn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A kind of manufacture method of nylon functional air clean negative ion air covering silk, comprises the following steps:

[0039] a) Melt high-speed spinning: The precision weight feeding machine imported from Japan is used to add functional anion masterbatch and nylon chips into the extruder. The content of functional anion masterbatch is 6%, and the German Bama The standard extruder is used to make the two kinds of slices fully melt and evenly. The temperature of each section of the extruder is set at 240°C, 250°C, 253°C, 255°C, and 256°C. The temperature of the heating furnace for box insulation is set at 262°C, the spinneret hole of the spinneret assembly is circular, with a diameter of 0.25mm, an aspect ratio of 2.5, and the number of spinneret holes is 34;

[0040] b) Cooling by side blowing: wind temperature 16°C, humidity 90%, wind speed 0.38m / s.

[0041] c) Oiling and clustering: the fibers cooled by side blowing are oiled and clustered through the oil mist n...

Embodiment 2

[0048] A kind of manufacture method of nylon functional air clean negative ion air covering silk, comprises the following steps:

[0049] a) Melt high-speed spinning: The precision weight feeding machine imported from Japan is used to add functional anion masterbatch and nylon chips into the extruder. The content of functional anion masterbatch is 7%, and the German Bama The standard extruder is used to make the two kinds of slices fully melt and uniform. The temperature of each section of the extruder is set at 240°C, 250°C, 253°C, 255°C, and 270°C. The temperature of the heating furnace for box insulation is set at 244°C, the spinneret hole of the spinneret assembly is circular, with a diameter of 0.24mm, an aspect ratio of 2.5, and the number of spinneret holes is 48;

[0050] b) Cooling by side blowing: wind temperature 18°C, humidity 95%, wind speed 0.45m / s;

[0051] c) Oiling and clustering: the fibers cooled by side blowing are oiled and clustered through the oil mist ...

Embodiment 3

[0058] A kind of manufacture method of nylon functional air clean negative ion air covering silk, comprises the following steps:

[0059] a) Melt high-speed spinning: The precision gravimetric feeding machine imported from Japan is used to add functional anion masterbatch and nylon chips into the extruder. The content of functional anion masterbatch is 8%, and German Bama is used. The standard extruder is used to make the two kinds of slices fully melt and evenly. The temperature of each section of the extruder is set at 240°C, 251°C, 252°C, 260°C, and 268°C. The temperature of the heating furnace for box insulation is set at 268°C, the spinneret hole of the spinneret assembly is circular, with a diameter of 0.22mm, an aspect ratio of 2.5, and the number of spinneret holes is 68;

[0060] b) Side blowing cooling: wind temperature 17°C, humidity 92%, wind speed 0.50m / s;

[0061] c) Oiling and clustering: the fibers cooled by side blowing are oiled and clustered through the oil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to view more

Abstract

An embodiment of the invention discloses a production method of functional nylon air cleaning negative ion air coated filaments. The production method includes steps: (a) fusing and high-speed spinning; (b) cross air blasting for cooling; (c) oiling and bundling; (d) winding; (e) lead wire heating; (f) cooling and false twisting and (g) drafting and wire stitching, and finally the functional nylon air cleaning negative ion air coated filaments are obtained. The production method of the functional nylon air cleaning negative ion air coated filaments is formed through appropriate negative ion master batch material selection, a filling machine with excellent performance and adjustment of spinning temperature, cooling conditions, spinning speed, oiling rate, winding speed and the like, and the produced functional nylon air cleaning negative ion air coated filaments can well release negative ions so as to improve the environment and meanwhile have good quality level stability.

Description

technical field [0001] The invention belongs to the technical field of spinning, and in particular relates to a method for manufacturing nylon functional air-cleaning negative ion air-coated yarn. Background technique [0002] In purifying air, the molecular formula of negative air ions is O2-(H2O)n, or OH-(H2O)n or CO4-(H2O)n. The negative air ions with environmental protection function mainly refer to the first two small molecular negative ions. Negative air ions can restore active oxygen (oxygen free radicals) produced by atmospheric pollutants, nitrogen oxides, cigarettes, etc., and reduce the harm of excessive active oxygen to the human body; neutralize positively charged air dust and settle without charge, making The air is purified, and negative ions can also purify odors. [0003] With the development of industry and commerce, the odor emitted from factories, the exhaust gas emitted by automobiles are increasing, and the second-hand smoke exhaled by people's daily s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/38D01D5/08D01F6/90D01F1/10D01F11/08
Inventor 郑期中刘文华陈宜生张岚岚赵欣华
Owner ZHEJIANG YAXING FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap