Manufacturing method of beaded polytrifluorochloroethylene resins

A technology of polychlorotrifluoroethylene and chlorotrifluoroethylene, which is applied in the field of polymer production, can solve problems such as difficulty in popularization, and achieve the effects of low cost, convenient washing and drying

Inactive Publication Date: 2013-09-18
山东森福新材料有限公司
View PDF11 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] U.S. Patent US3045000 uses solvents and strong oxidants to carry out terminal group tre

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of beaded polytrifluorochloroethylene resins

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1

[0028] After the 2 liter high-pressure reactor with electromagnetic stirring is deoxidized, 1000g of high-purity water, 100g of diisopropyl ether, 0.4g of isobutyl peroxydicarbonate and 0.6g of N,N-dimethylaniline are added, and the stirring rate is 400rmp. Bottom, filled with 100g of chlorotrifluoroethylene, reacted at 30°C for 4 hours, adjusted the stirring rate to 100rmp, and heated to 50°C. Continue the reaction for 2 hours. Open the reactor and, while stirring, wash the obtained resin with distilled water at 80°C and then with distilled water at room temperature. Finally, it was dried at 170°C for 12 hours to obtain a polychlorotrifluoroethylene resin in the form of beads with a diameter of 1 mm to 3 mm.

Example Embodiment

[0029] Example 2

[0030] Except that the added amount of diisopropyl ether is 150 g, the rest is the same as in Example 1, and the polymerization reaction is performed to obtain a polychlorotrifluoroethylene resin in the form of beads of 1 mm to 3 mm.

Example Embodiment

[0031] Example 3

[0032] Use n-hexane instead of diisopropyl ether, add 150g, and use dibenzoyl peroxide instead of isobutyl peroxide. The same polymerization reaction as in Example 1 is carried out to obtain beads of 0.8mm-3mm. Fluorochloroethylene resin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a manufacturing method of beaded polytrifluorochloroethylene resins, which comprises the following steps of: taking trifluorochlor oethylene, high-purity water, an organic dispersant and an initiator under the condition that the mass ratio of the trifluorochlor oethylene, the high-purity water, the organic dispersant and the initiator is 100:(500-1000): (50-200): (0.1-1); placing the high-purity water, the organic dispersant and the initiator in a reaction kettle, and at a stirring speed of 400-500 rmp, feeding the trifluorochlor oethylene into the reaction kettle; carrying out reaction on the obtained mixture for 4-6 hours under the conditions of 0.2-1 Mpa and 20-30 DEG C; and then continuing to react for 2-4 hours at a temperature of 50 DEG C and at a stirring speed of 100-200 rmp; and carrying out washing and drying on the obtained product so as to obtain a beaded polytrifluorochloroethylene resin with a diameter of 0.5-5 mm. The method disclosed by the invention is stable in polymerization rate and narrow in molecular weight distribution, no dust flying occurs in the process of production, and no further granulation treatment is required; the obtained polytrifluorochloroethylene resin is excellent in performances, and can be prepared into tubes, bars and profiles with more complicated shapes through melt injection molding; and no yellowing phenomenon occurs, therefore, the method has good social, economic and environmental benefits.

Description

technical field [0001] The invention relates to a production method of bead-shaped polychlorotrifluoroethylene resin. The invention belongs to the technical field of high molecular polymer production. Background technique [0002] Polychlorotrifluoroethylene (PCTFE) has high transparency, excellent cold flow resistance, wear resistance, and stable size. It is often used in extreme climate conditions where other materials cannot adapt, especially in high-tech manufacturing and military aerospace. PCTFE is non-hygroscopic, radiation-resistant, and has excellent gas barrier properties. It can be used as a sealing material and an observation window for spacecraft in high-pressure or negative-pressure systems. [0003] PCTFE can be processed into various profiles, such as components in compressors and mechanical pumps, food and drug packaging films, gaskets and bearings, through conventional techniques such as injection molding, spelling out, and compression molding. Because of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F114/24C08F214/24C08F214/22C08F214/26C08F216/12C08F2/18C08F4/34C08F4/32C08F4/38
Inventor 程昊杨勇杨涛毕翔宇
Owner 山东森福新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap