Coating white cardboard and production process thereof

A technology of cloth white cardboard and production technology, which is applied in the field of papermaking, can solve the problems of high cost, impossibility of popularization and implementation, easy failure of anti-counterfeiting measures, etc., and achieve the effect of easy identification

Active Publication Date: 2013-09-25
ZHUHAI S E Z HONGTA RENHENG PAPER +1
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the anti-counterfeiting technology on packaging paper generally adopts barcode anti-counterfeiting, printing anti-counterfeiting, etc.; but with the development of various new technologies, such as high-precision scanning and printing, computer graphics processing technology, digital printing technology, etc., the anti-counterfeiting technology on packaging paper Anti-counterfeiting measures are easily invalidated and imitated
If the anti-counterfeiting technology is improved by transforming papermaking and printing equipment, the cost is too high to be widely implemented

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating white cardboard and production process thereof
  • Coating white cardboard and production process thereof
  • Coating white cardboard and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Surface pulp: wood pulp (weight percentage: 70% bleached hardwood kraft pulp, 30% bleached softwood kraft pulp), crushed and mixed by a pulper, refined by a disc refiner, and enter the surface of the paper machine net filter;

[0036] Core layer pulp: wood pulp (percentage by weight: bleached hardwood kraft pulp 50%, bleached softwood kraft pulp 25%, broken paper 25%), crushed and mixed by pulper, refined by disc refiner , into the paper machine core mesh filter;

[0037]Bottom pulp: wood pulp (percentage by weight: 5% natural fiber, 85% bleached hardwood kraft pulp, 10% bleached softwood kraft pulp), crushed and mixed by a pulper, refined by a disc refiner, Enter the paper machine surface screen filter;

[0038] Then, a three-layer laminated wire is formed by a paper machine to produce a wet paper sheet with a surface layer 103, a core layer 102 and a bottom layer 101 distributed with natural fibers. After coating and drying, it enters the coiling section, coils, re...

Embodiment 2

[0050] The production process of this embodiment is the same as that of the above-mentioned embodiment 1, the difference lies in: the slurry ratio of the surface layer slurry, the core layer slurry, and the bottom layer slurry, and the coating ratio of the pre-coating and core coating.

[0051] Surface pulp (percentage by weight): bleached hardwood kraft pulp 85%, bleached softwood kraft pulp 15%;

[0052] Core layer pulp (weight percentage): bleached hardwood kraft pulp 53%, bleached softwood kraft pulp 17%, broken paper 30%;

[0053] Bottom pulp (weight percent): natural fiber 8%, bleached hardwood kraft pulp 72%, bleached softwood kraft pulp 20%;

[0054] The coating ratio of precoating and core coating is (parts by weight): 100 parts of calcium carbonate, 8 parts of latex, 3 parts of soybean protein, 0.4 parts of carboxymethyl cellulose, 0.09 parts of dispersant, 0.8 parts of water repellent, lubricating 0.3-1.2 parts of antifoaming agent and 0.035 parts of antifoaming ag...

Embodiment 3

[0063] Surface pulp (percentage by weight): bleached hardwood kraft pulp 90%, bleached softwood kraft pulp 10%;

[0064] Core pulp (weight percent): 55% bleached hardwood kraft pulp, 5% bleached softwood kraft pulp, 40% broken paper;

[0065] Bottom pulp (weight percent): natural fiber 10%, bleached hardwood kraft pulp 60%, bleached softwood kraft pulp 30%;

[0066] The coating ratio of pre-coating and core coating is (parts by weight): 100 parts of calcium carbonate, 10 parts of latex, 1.0 parts of soybean protein, 0.6 parts of carboxymethyl cellulose, 0.12 parts of dispersant, 1.0 parts of water-resistant agent, lubricating 1.2 parts of agent, 0.035 parts of defoamer.

[0067] The coating amounts of the precoat layer 104, the core coat layer 105, and the top coat layer 106 were applied at 10 g / m2, 12 g / m2, and 12 g / m2, respectively.

[0068] The produced coated white cardboard is compared with FBB ordinary white cardboard of the same grammage on the market, and its physica...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a coating white cardboard comprising a raw paper and a coating layer, wherein the raw paper comprises a surface layer, a core layer and a bottom layer which are orderly overlaid, the bottom layer is distributed with natural color fibers accounting for 5-10% by weight of the bottom layer, and the coating layer is coated on the surface layer. Because the natural color fibers which are distributed on the bottom layer form textures, the coating white cardboard is easy to be distinguished and recognized from conventional white cardboards. The natural color fibers do not need to be bleached through chemical processing, thereby influence of environment from bleaching chemicals is reduced, and COD emission load when in pulping is effectively reduced. The flexible performance and the bond strength of the coating white cardboard are increased by adopting a fiber structure, binding force between layers is increased, and therefore packaging strength is increased.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a coated white cardboard and a production process thereof. Background technique [0002] At present, the anti-counterfeiting technology on packaging paper generally adopts barcode anti-counterfeiting, printing anti-counterfeiting, etc.; but with the development of various new technologies, such as high-precision scanning and printing, computer graphics processing technology, digital printing technology, etc., the anti-counterfeiting technology on packaging paper Anti-counterfeiting measures are easy to fail and be imitated. If the anti-counterfeiting technology is improved by transforming papermaking and printing equipment, the cost will be too high to be popularized and implemented. Based on the fact that the packaging base materials currently used in the market are generally ordinary coated white cardboard, if we start from the packaging base material and provide a packagi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/82D21H19/38D21H19/44D21H19/50D21H19/52D21H21/06D21H21/08D21H21/12D21H21/14D21H15/10
Inventor 季向东杨玺李赓仇如全
Owner ZHUHAI S E Z HONGTA RENHENG PAPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com