Non-halogen red phosphorus flame-retardant heat shrinking tube and preparation method thereof

A technology of heat-shrinkable tube and red phosphorus, which is applied in the field of heat-shrinkable tube and its preparation, can solve the problems of environmental and product hazards, and achieve the effect of smooth surface and excellent processing performance

Active Publication Date: 2013-10-02
CHANGYUAN GRP
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is: to overcome the defect that the use of red phosphorus as a flame retardant in the existing heat shrinkable tubes is harmful to the environment and products, and to provide a halogen-free, red phosphorus-free flame-retardant heat-shrinkable tube that does not cont...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Take 100 parts of ethylene-hexene acetate copolymer, 90 parts of magnesium hydroxide, 20 parts of polyphosphazene, 3 parts of composite antioxidant, and 5 parts of lubricant.

[0037] The above materials are mixed and granulated by banburying, and extruded into pipes by a single-screw extruder. The pipes are cross-linked by cobalt 60 or electron accelerator 100KGy radiation, and the pipes after radiation cross-linking are expanded by 2 times at a temperature of 120°C to obtain The properties of the halogen-free and red phosphorus-free flame retardant heat shrinkable tube are as follows:

[0038] Flame retardancy: VW-1 passed, tensile strength: 12.8Mpa, elongation at break: 376%, and the product surface is smooth.

Embodiment 2

[0040] Take 100 parts of ethylene-hexene acetate copolymer, 110 parts of magnesium hydroxide, 5 parts of polyphosphazene, 1 part of composite antioxidant, and 2 parts of lubricant.

[0041] The above materials are mixed and granulated by banburying, and extruded into pipes by a single-screw extruder. The pipes are cross-linked by cobalt 60 or electron accelerator 100KGy radiation, and the pipes after radiation cross-linking are expanded by 2 times at a temperature of 120°C to obtain The properties of the halogen-free and red phosphorus-free flame retardant heat shrinkable tube are as follows:

[0042] Flame retardancy: VW-1 passed, tensile strength: 11.3Mpa, elongation at break: 235%, and the product surface is smooth.

Embodiment 3

[0044] Take 100 parts of ethylene-hexene acetate copolymer, 100 parts of magnesium hydroxide, 12 parts of polyphosphazene, 2 parts of composite antioxidant, and 3.5 parts of lubricant.

[0045] The above materials are mixed and granulated by banburying, and extruded into pipes by a single-screw extruder. The pipes are cross-linked by cobalt 60 or electron accelerator 100KGy radiation, and the pipes after radiation cross-linking are expanded by 2 times at a temperature of 120°C to obtain The properties of the halogen-free and red phosphorus-free flame retardant heat shrinkable tube are as follows:

[0046] Flame retardancy: VW-1 passed, tensile strength: 11.8Mpa, elongation at break: 246%, and the product surface is smooth.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a non-halogen red phosphorus flame-retardant heat shrinking tube. The heat shrinking tube comprises the following components in parts by weight: 100 parts of ethylene-acetate hexane copolymer, 90 to 110 parts of magnesium hydroxide, 5 to 20 parts of polyphosphazene, 1 to 3 parts of complex antioxidant, and 2 to 5 parts of lubricant, wherein the acetate hexane content of the ethylene-acetate hexane copolymer is 14-28 percent; the average grain size of the magnesium hydroxide is less than 4 mu m; the anti-oxidant is compounded of 2,2'-methylene-bis(6-tert-butyl-para-cresol) and 2-hydroxy-4-(octyloxy)benzophenone which are in a ratio of 5:1; and the lubricant is one or more of the following substances: polyethylene wax, zinc stearate and stearic acid. The non-halogen red phosphorus flame-retardant heat shrinking tube does not contain halogen, red phosphorous, lead, mercury, cadmium, hexavalent chromium or other toxic and harmful substances, the flame retardance can pass VW-1 test, the tensile strength is more than 10.9MPa, the elongation at break is more than 260 percent, the product surface is smooth, and the processing performance is excellent.

Description

technical field [0001] The invention relates to a heat-shrinkable pipe material and a preparation method thereof. Background technique [0002] On July 1, 2006, the EU RoHS directive came into effect, and in November 2006, my country's electronic industry standard SJ / T 11363-2006 "Limit Requirements for Toxic and Hazardous Substances in Electronic Information Products" came into effect, prohibiting the use of lead and mercury in electronic information products , cadmium, hexavalent chromium, polybrominated biphenyls (PBB) and polybrominated diphenyl ethers (PBDE). PBDE), to manufacture flame retardant heat shrink tubing. [0003] However, when red phosphorus burns, it will release toxic and irritating smoke, corrode human skin and mucous membranes, and endanger human health. The silver reacts electrochemically and connects the positive and negative poles of the circuit board, causing the circuit board to fail. So in June 2007, Apple released the "Apple Halogen Free Specific...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08L85/02C08K13/02C08K3/22C08K5/5399C08J3/28C08J3/24
Inventor 赵成刚尹沾松谢世平刘军
Owner CHANGYUAN GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products