Environmentally-friendly multifunctional metal surface treating fluid

A metal surface treatment, multi-functional technology, applied in the field of treatment liquid, can solve the problems of low anti-rust ability, poor quality of transformation, complicated operation procedures, etc., and achieve the effect of excellent effect and simple operation.

Inactive Publication Date: 2013-10-02
杭州聚城环保科技有限公司
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention provides an environment-friendly multi-functional metal surface treatment liquid, which mainly solves the problems in the prior art that the treatment liquid needs to be degreased, derusted, cleaned, and heated in advance when treating the metal surface. It is more complex, and the quality of the transformation is poor, and the technical problems such as low anti-rust ability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: the environmental protection type multifunctional metal surface treatment liquid of this example, prepares 100 kilograms of environmental protection type multifunctional metal surface treatment liquids:

[0011] Tools: mixer, heater, 50L, 100L, 250L plastic barrels.

[0012] In three steps:

[0013] 1. Add 15kg of deionized water to a plastic bucket with a volume of 50L, add 3kg of zinc skin or zinc blocks, and zinc granules, and stir until completely dissolved to prepare a solution for use.

[0014] 2. Add 20kg of deionized water into a 100L plastic bucket, then add 30Kg of phosphoric acid, 1.3kg of acid manganese phosphate, 0.12kg of calcium nitrate, 1kg of tartaric acid, and 0.8kg of citric acid and stir until completely dissolved.

[0015] 3. Add 25kg of deionized water into a plastic bucket with a volume of 250L, and heat it to 25 degrees, then add 0.58kg of thiourea, 0.1kg of polyethylene glycol, 2.3kg of sodium dodecylbenzenesulfonate, and analytic...

Embodiment 2

[0016] Embodiment 2: the environmental protection type multifunctional metal surface treatment liquid of this example, prepares 100 kilograms of environmental protection type multifunctional metal surface treatment liquids:

[0017] Tools: mixer, heater, 50L, 100L, 250L plastic barrels.

[0018] In three steps:

[0019] 1. Add 20kg of deionized water to a plastic bucket with a volume of 50L, add 2.5kg of zinc skin or zinc blocks, and zinc particles, stir thoroughly for 20 minutes, then add 1.3kg of acid manganese phosphate until completely dissolved to prepare a solution for later use .

[0020] 2. Add 18kg of deionized water into a 100L plastic bucket, followed by 28Kg of phosphoric acid, 0.14kg of calcium nitrate, 1kg of tartaric acid, and 0.7kg of citric acid, and stir until completely dissolved.

[0021] 3. Add 25kg of deionized water into a plastic bucket with a volume of 250L, and heat it to 15 degrees, then add 0.6kg of thiourea, 0.16kg of polyethylene glycol, 1.8kg o...

Embodiment 3

[0022] Embodiment 3: the environmental protection type multifunctional metal surface treatment liquid of this example, prepares 100 kilograms of environmental protection type multifunctional metal surface treatment liquids:

[0023] Tools: Blender, 50L, 100L, 250L plastic buckets.

[0024] In three steps:

[0025] 1. Add 22kg of deionized water to a plastic bucket with a volume of 50L, add 2.8kg of zinc skin or zinc blocks, and zinc particles, stir thoroughly for 20 minutes, then add 1.2kg of acid manganese phosphate until completely dissolved to prepare a solution for later use .

[0026] 2. Add 20kg of deionized water to a 100L plastic bucket, followed by adding 24Kg of phosphoric acid, 0.15kg of calcium nitrate, 0.84kg of tartaric acid, and 0.8kg of citric acid, and stir until completely dissolved.

[0027] 3. Add 25kg of deionized water into a plastic bucket with a volume of 250L, and then add 0.7kg of thiourea, 0.11kg of polyethylene glycol, 1.6kg of sodium dodecylbenze...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to treating fluid, and particularly relates to environmentally-friendly multifunctional metal surface treating fluid. The environmentally-friendly multifunctional metal surface treating fluid is mainly used for solving the technical problems in the prior art that when the treating fluid is used for treating metal surfaces, oil removal, dust removal and cleaning need to be carried out in advance, heating is also needed, operation working procedures are complicated, the conversion quality is low, the rust prevention capacity is low and the like. The treating fluid comprises the following components in percentage by mass: 25%-40% of phosphoric acid, 0.25%-0.32% of sheet zinc or zinc slab, zinc granules, 1%-1.5% of acid type manganese phosphate, 0.1%-0.15% of calcium nitrate, 0.8%-1% of tartaric acid, 0.2%-0.8% of phytic acid, 0.5%-0.7% of thiourea, 0.11%-0.16% of polyethylene glycol, 1.5%-2.5% of sodium dodecylbenzene sulfonate, 0.08%-0.12% of analytically pure ammonium molybdate and the balance of water.

Description

technical field [0001] The invention relates to a treatment liquid, in particular to an environment-friendly multifunctional metal surface treatment liquid. Background technique [0002] Coating is an anti-corrosion method widely used in metal surface treatment. Pre-painting treatment is an essential pre-painting process. Its function is to establish a non-metallic protective layer on the protected metal workpiece, so that the metal workpiece has good adhesion to the paint film, so that both Stronger adhesion, thus improving the corrosion resistance of the coating. Chinese patent discloses an environment-friendly multifunctional steel surface treatment solution (publication number: CN102839365 A), which is composed of phosphoric acid, film forming agent, organic acid, dispersant, oxidation accelerator, complexing agent, surfactant and other raw materials Composition, its specific raw material ratio is as follows: phosphoric acid (85%) 28-35% (percentage by weight), zinc di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/42
Inventor 李连生韩小娟
Owner 杭州聚城环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap