Magnesium-aluminum alloy polishing solution and its preparation method and polishing method

A magnesium-aluminum alloy and polishing liquid technology, which is applied in the field of alloy polishing, can solve the problems of unsatisfactory surface quality in microscopic inspection, low polishing efficiency, and poor surface quality, and achieve reduced scratches, good chemical stability, and roughness. and waviness reduction effect

Active Publication Date: 2013-10-02
INNER MONGOLIA BAOTOU STEEL UNION
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are problems with the polishing solution for magnesium and aluminum alloys. First, there are relatively few types. Second, the surface quality after polishing is poor, there are many scratches, and the polishing efficiency is low, which cannot meet the requirements of microscopic inspection for surface quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Add the following raw materials to 1000g of polishing liquid, and the specific contents are shown in Table 1.

[0034] Table 1 Details of polishing liquid raw materials

[0035] serial number

Embodiment 2

[0037] Add the following raw materials to 1000g of polishing liquid, and the specific contents are shown in Table 2.

[0038] Table 2 Details of polishing liquid raw materials

[0039] serial number

Embodiment 3

[0041] Add the following raw materials to 1000g of polishing liquid, and the specific contents are shown in Table 3.

[0042] Table 3 Details of polishing liquid raw materials

[0043] serial number

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a magnesium-aluminum alloy polishing solution. Each 1000g of the magnesium-aluminum alloy polishing solution comprises 5 to 12g of sodium coco-sulfate, 1 to 8g of sodium tripolyphosphate, 1 to 2.5g of sodium hydroxide, 4 to 11g of fatty alcohol polyoxyethylene ether, 0.4 to 2.5g of sodium citrate and the balance distilled water. The invention also discloses a preparation method of the magnesium-aluminum alloy polishing solution and a polishing method of the surface of a magnesium-aluminum alloy material. The magnesium-aluminum alloy polishing solution can improve surface brightness of a polished magnesium-aluminum alloy material.

Description

technical field [0001] The invention relates to the technical field of alloy polishing, in particular to a magnesium-aluminum alloy polishing liquid, a preparation method and a polishing method thereof. Background technique [0002] With the development of mechanical equipment, automobiles, precision parts and other related industries, the demand for magnesium alloy materials is increasing. Due to its excellent high temperature resistance, ablation resistance and molten metal corrosion resistance, it has a wide range of application prospects; in addition, due to its relatively light specific gravity, high strength, easy processing, stable dimensions, and excellent casting process performance, magnesium alloy Good corrosion resistance, low cost, and renewable utilization, etc., are known as "green engineering metals in the 21st century" and can replace steel alloys in many places. Therefore, the requirements for the brightness of the magnesium-aluminum alloy surface are cons...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F3/02
Inventor 徐强
Owner INNER MONGOLIA BAOTOU STEEL UNION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com