High-oil-absorbency resin

An oleoresin, high-absorption technology, applied in the field of resin, can solve the problems that hinder the development of industrialization, product application expansion, low oil absorption ratio, poor reversibility of oil absorption and discharge, etc., and achieve the effect of enhanced reversibility of oil absorption and discharge, and increased oil absorption ratio

Inactive Publication Date: 2013-11-20
南京市荣达树脂有限公司
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, this single chemical cross-linked oil-absorbing resin has low oil absorption ratio and poor oil

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] High oil-absorbing resin composition: 100 parts of butyl acrylate, 1 part of polyethylene glycol, 1 part of benzoyl peroxide, 4 parts of ethylene glycol dimethacrylate, 6 parts of polybutadiene;

[0021] The preparation method of above-mentioned high oil-absorbing resin, its preparation comprises the steps:

[0022] (1) Weigh the raw material components according to the formula ratio, put polyethylene glycol into the reaction vessel, add a certain amount of deionized water, and stir to fully dissolve;

[0023] (2) Mix the butyl acrylate, benzoyl peroxide, ethylene glycol dimethacrylate and polybutadiene in the amount of the formula evenly at room temperature, and then add them together into the reaction vessel;

[0024] (3) Nitrogen, stirring, heating to 65°C, and reacting for 8 hours;

[0025] (4) Cooling, discharging, washing and drying to obtain the product.

[0026] The high oil-absorbing resin prepared in this example, compared with a single chemically cross-link...

Embodiment 2

[0028] High oil-absorbing resin composition: 100 parts of butyl methacrylate, 0.5 parts of methyl cellulose, 0.5 parts of lauroyl peroxide, 3 parts of ethylene glycol diacrylate, 4 parts of polyethylene;

[0029] The preparation method of above-mentioned high oil-absorbing resin, its preparation comprises the steps:

[0030] (1) Weigh the raw material components according to the formula ratio, put the methyl cellulose into the reaction container, add a certain amount of deionized water, stir to fully dissolve;

[0031] (2) Mix the butyl methacrylate, lauroyl peroxide, ethylene glycol diacrylate and polyethylene in the recipe amount at room temperature, and then add them together into the reaction vessel;

[0032] (3) Nitrogen flow, stirring, heating to 70°C, and reacting for 7 hours;

[0033] (4) Cooling, discharging, washing and drying to obtain the product.

[0034] The high oil-absorbing resin prepared in this example, compared with single chemically cross-linked oil-abso...

Embodiment 3

[0036] High oil-absorbing resin composition: 100 parts of lauryl methacrylate, 1.5 parts of polyvinyl alcohol, 1.5 parts of di-tert-butyl peroxide, 5 parts of divinylbenzene, and 8 parts of polypropylene;

[0037] The preparation method of above-mentioned high oil-absorbing resin, its preparation comprises the steps:

[0038] (1) Weigh the raw material components according to the formula ratio, put polyvinyl alcohol into the reaction container, add a certain amount of deionized water, and stir to fully dissolve;

[0039] (2) Mix the lauryl methacrylate, di-tert-butyl peroxide, divinylbenzene and polypropylene in the recipe amount at room temperature, and then add them together into the reaction vessel;

[0040] (3) Nitrogen flow, stirring, heating to 60°C, and reacting for 9 hours;

[0041] (4) Cooling, discharging, washing and drying to obtain the product.

[0042] The high oil-absorbing resin prepared in this example, compared with a single chemically cross-linked oil-abso...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-oil-absorbency resin which is mainly prepared from the following ingredients in parts by weight: 100 parts of a acrylic monomer, 0.5-1.5 parts of a dispersing agent, 0.5-1.5 parts of an initiating agent, 3-5 parts of a chemical cross-linking agent and 4-8 parts of a physical cross-linking agent. Compared with other oil-absorbency resins prepared in a single chemical cross-linking mode in the prior art, the high-oil-absorbency resin has the advantages that oil absorption multiplying power for diesel oil is improved by 18-20%, the oil absorption multiplying power for engine oil is increased by 14-16%, the oil absorption multiplying power is remarkably increased, and the oil absorption reversibility is remarkably improved.

Description

technical field [0001] The invention relates to a resin, in particular to a high oil-absorbing resin, which can be used in environmental protection aspects such as oil recovery and water purification. Background technique [0002] In recent years, the environmental pollution caused by a large amount of oily wastewater caused by leakage accidents of oil tankers and oil tanks has attracted much attention. Traditional oil-absorbing materials cannot meet the requirements of waste oil recovery and environmental treatment in terms of performance and output. In the face of deteriorating environmental pollution, the research and development of effective oil recovery technology and oily wastewater purification materials is imperative. As a self-swelling oil-absorbing material, super oil-absorbing resin has many advantages such as various types of oil-absorbing, no water absorption during oil-absorbing, small size and convenient recycling. Oil slicks and treatment of industrial oily ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F220/18C08F222/14C08F212/36C08F220/28C08F120/18C08F2/44C09K3/32
Inventor 刘荣春
Owner 南京市荣达树脂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap