Metal antirust paint for ships and its preparation method

A metal antirust and marine technology, applied in the field of metal antirust paint, can solve the problems of harsh environment, easy peeling off of antirust paint, poor weather resistance, etc., and achieve the effect of high hardness and strong adhesion

Active Publication Date: 2013-11-20
寿县风顺船舶修造有限责任公司
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Due to the harsh environment of ships traveling in rivers or seas for many years, the anti-rust paint on the outside of the hull is easy to fall off, and it needs to be repainted frequently, which increases the cost and is not conducive to the protection of the hull
The existing marine metal antirust paint generally has poor weather resistance, is easy to fall off, and is not suitable for complex and harsh environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] A kind of marine metal antirust paint, is made from the raw material component of following component parts by weight (kg):

[0013] Zinc powder 8, ferroferric oxide 5, methyl ethyl ketone 20, medium oil alkyd resin 30, HDl biuret 2, dicyclopentenyl ethoxy methacrylate 5, hexanediol butyl ether acetate 10, hydroxide Magnesium 6, nano attapulgite 5, stannous pyrophosphate 1, sodium tripolyphosphate 5, polysiloxane defoamer 2, triethylenediamine 2, propylene glycol 5, tung oil 10, xylene 15, diisoperoxide Propylbenzene DCP 2, silane coupling agent KH550 5, crosslinking agent TAC 2, maleic anhydride 16, styrene 8, p-benzoquinone 2, p-tert-butylcatechol 2, aluminum nitride 1, aluminum hydroxide Powder3.

[0014] The preparation method comprises the following steps:

[0015] (1) Add xylene, maleic anhydride, styrene, p-benzoquinone, and p-tert-butylcatechol into the reaction kettle, heat to 70-80°C, stir, and add dicumyl peroxide DCP, under stirring, then add aluminum nit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a metal antirust paint for ships. The metal antirust paint is composed of the following raw materials by weight part: 5-8 of zinc powder, 5-8 of ferroferric oxide, 20-30 of methyl ethyl ketone, 30-40 of medium oil alkyd resin, 1-2 of HDl biuret, 5-10 of dicyclopentenyl ethoxyl methacrylate, 5-10 of hexanediol butyl ether acetate, 4-6 of magnesium hydroxide, 3-5 of nano-attapulgite clay, 1-2 of stannous pyrophosphate, 3-5 of sodium tripolyphosphate, and 1-2 of a polysiloxane defoaming agent, etc. The preparation method of the antirust paint involved in the invention is designed as a two-step process. In the first step, the zinc powder reacts with other ingredients to form a grid structure. The formed paint film has high hardness, scratch resistance and strong adhesion, and resists salt fog, saline, acid and base, water as well as oil. No damage can be caused to the paint film. The paint film also has super strong flexibility, and a general service life of 6-8 years.

Description

technical field [0001] The invention relates to a metal antirust paint, in particular to a marine metal antirust paint and a preparation method thereof. Background technique [0002] Ships have been driving in rivers or seas for many years, and the environment is harsh, so the anti-rust paint on the outside of the hull is easy to fall off, and it needs to be repainted frequently, which increases the cost and is not conducive to the protection of the hull. The existing marine metal antirust paint generally has poor weather resistance, is easy to fall off, and is not suitable for complex and harsh environments. Contents of the invention [0003] The invention provides a marine metal antirust paint and a preparation method thereof, which have good mechanical stability, flexibility and surface hardness, and good weather resistance. [0004] Technical scheme of the present invention is: [0005] A kind of antirust paint for marine metal is characterized in that it is made of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D135/00C09D5/10C09D7/12C08F222/06C08F212/08
Inventor 徐兆堂
Owner 寿县风顺船舶修造有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products