Plastic floor substrate and making method thereof

A technology of plastic floor and base material, applied in the field of interior decoration materials, can solve the problems of people's health and environmental hazards, and achieve the effect of good bacteriostatic and bactericidal effect.

Active Publication Date: 2013-11-27
吴江汾湖科技创业服务有限公司
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the floor will deposit a large amount of bacteria on the floor surface during long-term use, especially when walking barefoot for a long time, and it is difficult to completely remove it, it will bring harm to people's health and the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plastic floor substrate and making method thereof
  • Plastic floor substrate and making method thereof
  • Plastic floor substrate and making method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A plastic floor substrate, comprising by weight components:

[0015] 80 parts of polyvinyl chloride, the degree of polymerization is 600, 20 parts of dioctyl phthalate, 60 parts of calcium carbonate, 6 parts of titanium dioxide, 2 parts of epoxy soybean oil, 1 part of magnesium stearate, 2 parts of phosphite, 12 parts of plasticizer DPO, 0.5 parts of polyvinyl alcohol, 0.3 parts of chitin, 0.5 parts of nano-zinc oxide powder, and 0.5 parts of nano-silver powder.

[0016] Above-mentioned floor substrate is prepared by following steps:

[0017] (1) Put each component into the mixer according to the weight part for stirring and mixing, the stirring speed is 60 rpm, and the stirring time is 10 minutes.

[0018] (2) Send the mixed material into a twin-screw extruder for extrusion, and the temperature of the extruder is 150°C.

[0019] (3) The extruded material is calendered with a three-roll calender, wherein the temperature of the upper roll is 165°C, the temperature of t...

Embodiment 2

[0021] A plastic floor substrate, comprising by weight components:

[0022] 83 parts of polyvinyl chloride, the degree of polymerization is 620, 22 parts of dioctyl phthalate, 68 parts of calcium carbonate, 8 parts of titanium dioxide, 3 parts of epoxy soybean oil, 2 parts of magnesium stearate, 3 parts of phosphite, 14 parts of plasticizer DPO, 0.8 parts of polyvinyl alcohol, 0.5 parts of chitin, 0.6 parts of nano-zinc oxide powder, and 0.6 parts of nano-silver powder.

[0023] Above-mentioned floor substrate is prepared by following steps:

[0024] (1) Put each component into the mixer according to the weight part for stirring and mixing, the stirring speed is 65 rpm, and the stirring time is 12 minutes.

[0025] (2) Send the mixed material into a twin-screw extruder for extrusion, and the temperature of the extruder is 160°C.

[0026] (3) The extruded material is calendered with a three-roll calender, wherein the temperature of the upper roll is 168°C, the temperature of ...

Embodiment 3

[0028] A plastic floor substrate, comprising by weight components:

[0029] 86 parts of polyvinyl chloride, the degree of polymerization is 650, 26 parts of dioctyl phthalate, 70 parts of calcium carbonate, 8 parts of titanium dioxide, 4 parts of epoxy soybean oil, 4 parts of magnesium stearate, 3 parts of phosphite, 15 parts of plasticizer DPO, 1.2 parts of polyvinyl alcohol, 0.5 parts of chitin, 0.7 parts of nano-zinc oxide powder, and 0.8 parts of nano-silver powder.

[0030] Above-mentioned floor substrate is prepared by following steps:

[0031] (1) Put each component into the mixer according to the weight part for stirring and mixing, the stirring speed is 70 rpm, and the stirring time is 15 minutes.

[0032] (2) Send the mixed material into a twin-screw extruder for extrusion, and the temperature of the extruder is 165°C.

[0033] (3) The extruded material is calendered with a three-roll calender, wherein the temperature of the upper roll is 168°C, the temperature of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention provides a plastic floor substrate and a making method thereof. The plastic floor substrate comprises, by weight, 80-90 parts of polyvinyl chloride, 20-30 parts of dioctyl phthalate, 60-80 parts of calcium carbonate, 6-12 parts of titanium dioxide, 2-6 parts of epoxy soybean oil, 1-5 parts of magnesium stearate, 2-5 parts of phosphate, 12-18 parts of a plasticizer DPO, 0.5-2 parts of polyvinyl alcohol, 0.3-0.7 parts of chitin, 0.5-1 part of nano-ZnO powder, and 0.5-1 part of nano-Ag powder. The plastic floor substrate has good performances in antibiotic tests, and has an Escherichia coli inhibition rate of above 99.7% during the 24th month in long-term tests, and a Staphylococcus aureus inhibition rate of above 99.6%.

Description

technical field [0001] The invention belongs to the field of interior decoration materials, in particular to a plastic floor base material and a preparation method thereof. Background technique [0002] At present, PVC flooring is a new type of light-weight floor decoration material that is very popular in the world today, also known as "light-weight floor material". It is a popular product in Europe, America and Asia. Plastic flooring has entered the Chinese market since the 1980s, and has been widely recognized in domestic large and medium-sized cities, and is widely used, such as indoor homes, hospitals, schools, office buildings, factories, public places, supermarkets, businesses, sports venues, etc. PVC floor can be divided into block material (floor tile) and roll material (floor leather) according to its use state. Its main advantage is that it is light in weight, 10 times lighter than wooden floors and 20 times lighter than ceramic tiles, and it is easy to carry; du...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L29/04C08L5/08C08K13/02C08K5/12C08K3/26C08K3/22C08K5/1515C08K5/098C08K5/524C08K3/08B29C69/02B29C47/00B29C43/24
Inventor 陈健张建光杨文乾
Owner 吴江汾湖科技创业服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap