Radial tire crown rubber for high-speed passenger car

A radial tire and crown rubber technology, applied in the field of tire manufacturing, can solve the problems of poor wet skid resistance, poor puncture resistance, low loss factor, etc., and achieve good wet skid resistance, good wear performance and durability. High performance and high speed performance

Inactive Publication Date: 2013-12-11
SHANDONG YONGTAI CHEM GROUP
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its loss factor is also low above 30°C, indicating that BR is the best raw material for tires with low rolling resistance and low heat generation, but its wet skid resistance and puncture resistance are poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Radial tire crown rubber for high-speed passenger car
  • Radial tire crown rubber for high-speed passenger car
  • Radial tire crown rubber for high-speed passenger car

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0072] High-speed car radial tire crown rubber, comprising the following components in parts by weight:

[0073] Solution Polystyrene Butadiene Rubber 40 Butadiene Rubber 20

[0074] Silica 40 Carbon Black 15

[0075] Sulfur 10 Aromatic oil 6

[0076] Nano-zinc oxide 5 N-phenyl-N'-isopropyl-p-phenylenediamine 5

[0077] High wear-resistant furnace black 10 Silane coupling agent 15

[0078] Salicylic Acid 1 Gas Carbon Black 12

[0079] Accelerator NOBS 8 Stearic acid 12

[0080] Bis(γ-3-triethoxysilylpropyl) tetrasulfide 10

[0081] Cobalt naphthenate 6

[0082] The particle size of the white carbon black is 400 mesh, which is the white carbon black after ultrafine pulverization.

Embodiment 2

[0114] High-speed car radial tire crown rubber, comprising the following components in parts by weight:

[0115] Solution Polystyrene Butadiene Rubber 40 Butadiene Rubber 20

[0116] Silica 40 Carbon Black 15

[0117] Sulfur 10 Aromatic oil 6

[0118] Nano zinc oxide 5 6-ethoxy-2,2,4-trimethyl-1,2 dihydroquinoline 5

[0119] High wear-resistant furnace black 10 Silane coupling agent 15

[0120]Benzoic acid 1 Gas carbon black 12

[0121] Accelerator NOBS 8 Stearic acid 12

[0122] Hexamethylene-1,6-dithiosulfate disodium salt 10

[0123] The particle size of the white carbon black is 400 mesh, which is the white carbon black after ultrafine pulverization.

Embodiment 3

[0125] High-speed car radial tire crown rubber, comprising the following components in parts by weight:

[0126] Solution Polystyrene Butadiene Rubber 40 Butadiene Rubber 20

[0127] Silica 40 Carbon Black 15

[0128] Sulfur 10 Aromatic oil 6

[0129] Nano zinc oxide 5 6-ethoxy-2,2,4-trimethyl-1,2 dihydroquinoline 5

[0130] High wear-resistant furnace black 10 Silane coupling agent 15

[0131] Benzoic acid 1 Gas carbon black 12

[0132] Accelerator NOBS 8 Stearic acid 12

[0133] Hexamethylene-1,6-dithiosulfate disodium salt 10

[0134] The particle size of the white carbon black is 400 mesh, which is the white carbon black after ultrafine pulverization.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides radial tire crown rubber for a high-speed passenger car, and belongs to the technical field of tire manufacture and particularly relates to automotive tire crown rubber. The automotive tire crown rubber comprises the following components: solution polymerized styrene-butadiene rubber, butadiene rubber, white carbon black, carbon black, sulfur, aromatic hydrocarbon, nano-zinc oxide antiager, high abrasion furnace black, silane coupling agent, scorch retarder, gas carbon black, accelerant, stearic acid and anti-reversion agent, wherein the particle size of the white carbon black is 400-600 meshes, and the white carbon black is smashed in a superfine manner. With the adoption of the formula with the components in parts by weight, the tire crown rubber has the advantages of excellent wear resistance, high rubber hardness, high stress at definite elongation and tear strength, good wet slip resistance, and also relatively good wear resistance performance, and both the endurance quality and the high speed performance of the finished product tire reach a relatively high level.

Description

technical field [0001] The invention belongs to the technical field of tire manufacture, and in particular relates to an automobile tire crown rubber. Background technique [0002] Tires are one of the important parts of the car. They are in direct contact with the road surface, and work together with the car suspension to ease the impact of the car while driving, ensuring that the car has good seating comfort and smooth driving; ensuring that the wheels and the road are in good condition The adhesion of the tire improves the traction, braking and passability of the car; bearing the weight of the car, the important role played by the tire on the car has attracted more and more attention. Automobile tires are especially important in the use of automobiles. Automobile tires are related to the safety performance of automobiles. [0003] In 1895, with the appearance of automobiles, pneumatic tires were widely developed. The first samples of automobile tires appeared in France i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/06C08L9/00C08K13/02C08K3/36C08K3/04C08K3/06C08K3/22C08K5/54C08K5/09C08K5/18C08K5/098
Inventor 尤晓明张国栋王显涛延云峰魏文祥
Owner SHANDONG YONGTAI CHEM GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap