High-heat-insulation, ultraviolet-isolation and transparent colored master batch and preparation method thereof

An ultraviolet and masterbatch technology, applied in the field of high heat insulation ultraviolet shielding transparent colored masterbatch and its preparation, can solve the problems of difficult adhesion of PET materials, many impurities in coating process particles, uneven color, etc., and achieve uniform color, The effect of good smoothness and high transparency

Inactive Publication Date: 2013-12-11
SUZHOU XILIN OPTOELECTRONICS TECH IND
6 Cites 14 Cited by

AI-Extracted Technical Summary

Problems solved by technology

[0006] The publication number is CN200410014672.4, and the Chinese patent titled nano-transparent heat-insulating composite coating and its heat-insulating effect test device discloses a process of coating a relativ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Abstract

The invention discloses a high-heat-insulation, ultraviolet-isolation and transparent colored master batch which comprises the following components in percentage by weight: 50-70% of resin, 0.5-10% of dispersing agent, 2-10% of heat-insulation ultraviolet-isolation nano material, 10-30% of slipping agent and 0-10% of coloring agent. The invention further discloses a preparation method of the high-heat-insulation, ultraviolet-isolation and transparent colored master batch. According to the master batch and the preparation method, the master batch and a transparent polyester chip are matched at a ratio, and subjected to extrusion and two-way stretch to produce a high-heat-insulation, ultraviolet-isolation and transparent colored film; the high-heat-insulation, ultraviolet-isolation and transparent colored film has excellent heat-insulation and ultraviolet-isolation functions; the heat-insulation and ultraviolet-isolation capacity can be adjusted as required; the color is uniform and consistent; and when the master batch is applied to PET (polyethylene glycol terephthalate) film extrusion or sheet extrusion, the master batch is smog-free, high in transparency and good in smooth effect.

Technology Topic

Image

  • High-heat-insulation, ultraviolet-isolation and transparent colored master batch and preparation method thereof
  • High-heat-insulation, ultraviolet-isolation and transparent colored master batch and preparation method thereof
  • High-heat-insulation, ultraviolet-isolation and transparent colored master batch and preparation method thereof

Examples

  • Experimental program(8)

Example Embodiment

[0023] Example 1: Masterbatch ingredients are shown in Table 1.
[0024]
[0025] 1) Under normal temperature and pressure, in the high-speed mixer, turn on the stirring blade and control the speed to 600r/min, and the heating and mixing temperature to be 85°C;
[0026] 2) After weighing the materials according to the ingredients list, put in 50% of the total amount of PET resin, and then put in the other components according to the proportion of ingredients. After the materials are mixed for 10 minutes, ensure that the slip agent has been completely melted and the materials are formed. Block, add the remaining PET resin after cooling;
[0027] 3) Then control the mixer speed to 480r/min to disperse the materials into granules to complete the preliminary melting and mixing of the materials, and the dispersing time is 1h;
[0028] 4) Put the preliminarily melted and mixed materials into the twin-screw machine for further melting and blending. The melting temperature is controlled at 260℃, the screw speed is 100r/min, and the time is 1h. The shearing and mixing of the screw makes the additives in The carrier resin is thoroughly dispersed uniformly, and then granulated and dried to obtain a transparent colored masterbatch with high heat insulation and ultraviolet radiation.
[0029] The natural color masterbatch can be combined with other heat-insulating UV-cut masterbatches to produce heat-insulating and UV-cutting functional films in appropriate proportions with transparent polyester chips. It is mainly used to adjust the smoothness of the film product and also adjust the color and heat insulation ability of ultraviolet rays.

Example Embodiment

[0030] Example 2: See Table 2 for the ingredients of the masterbatch.
[0031]
[0032] 1) Under normal temperature and pressure, in the high-speed mixer, turn on the stirring paddle and control the speed to 1000r/min, and the heating and mixing temperature to be 100℃;
[0033] 2) After weighing the materials according to the ingredients list, first put in 50% of the total amount of PET resin, and then put in the other components according to the proportion of the ingredients, and wait for the materials to mix for 15 minutes to ensure that the slip agent has been completely melted and the materials are consolidated Block, add the remaining PET resin after cooling;
[0034] 3) Then control the mixer speed to be 250r/min to disperse the materials into granules to complete the preliminary melting and mixing of the materials, and the dispersing time is 10h;
[0035] 4) Put the preliminarily melted and mixed materials into the twin-screw machine for further melting and blending. The melting temperature is controlled at 255℃, the screw speed is 300r/min, and the time is 5h. Through the shearing and mixing of the screw, the additives are The carrier resin is thoroughly dispersed uniformly, and then granulated and dried to obtain a transparent colored masterbatch with high heat insulation and ultraviolet radiation.
[0036] Use heat-insulating UV-cut transparent blue-green masterbatch and transparent polyester chips to produce heat-insulating and UV-cut functional films according to product needs. If it is necessary to adjust the smoothness of the film product, the UV-cut transparent natural color masterbatch of Example 1 can be appropriately added. With this masterbatch, it is possible to produce a heat-insulating film with high light transmittance, high heat insulation and UV cut with a light transmittance of more than 70%, an infrared cut of more than 80%, and an ultraviolet cut of more than 99%. It is suitable for architectural glass and automobile front glass that require high light transmission, high heat insulation and UV protection.

Example Embodiment

[0037] Example 3: See Table 3 for the ingredients of the masterbatch.
[0038]
[0039] 1) Under normal temperature and pressure, in the high-speed mixer, turn on the stirring blade and control the speed to 800r/min, and the heating and mixing temperature to be 95℃;
[0040] 2) After weighing the materials according to the ingredients list, first put in 50% of the total amount of PET resin, and then put in other components according to the proportion of the ingredients, and wait for the materials to mix for 25 minutes to ensure that the slip agent has been completely melted and the materials are consolidated Block, add the remaining PET resin after cooling;
[0041] 3) Control the mixer speed to be 500r/min to disperse the materials into granules to complete the preliminary melting and mixing of the materials, the dispersing time is 5h;
[0042] 4) Put the preliminarily melted and mixed materials into the twin-screw machine for further melting and blending. The melting temperature is controlled at 270℃, the screw speed is 200r/min, and the time is 3h. Through the shearing and mixing of the screw, the additives are The carrier resin is thoroughly dispersed uniformly, and then granulated and dried to obtain a transparent colored masterbatch with high heat insulation and ultraviolet radiation.
[0043] The heat-insulating UV-cut transparent light yellow-green masterbatch and transparent polyester chips are used to produce heat-insulating and UV-cut functional films according to product requirements. If it is necessary to adjust the smoothness of the film product, the UV-cut transparent natural color masterbatch of Example 1 can be appropriately added. With this masterbatch, it is possible to produce a heat-insulating film with high light transmittance, high heat insulation and UV cut with a light transmittance of more than 80%, an infrared cut of more than 80%, and an ultraviolet cut of more than 99%. It is suitable for architectural glass and automobile front glass that require high light transmission, high heat insulation and UV protection.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

no PUM

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Similar technology patents

Pink gold target for vacuum magnetron sputtering and preparation method thereof

ActiveCN103938174AUniform colorGood anti-oxidation and anti-sulfurizationVacuum evaporation coatingSputtering coatingFerrous metallurgyHigh surface
Owner:沈阳东创贵金属材料有限公司

High-performance glass fiber

InactiveCN110407474ASmooth appearanceUniform colorChemical stabilitySodium oxide
Owner:佛山市嘉懿行农业科技有限公司

Double component dyed sealed and hardened terrace material

ActiveCN106747652AFull dense colorUniform colorDyeingHardness
Owner:ZIGONG INNOVATION CENT OF ZHEJIANG UNIV

Polyacrylic film forming compositions

Owner:JOHNSON & JOHNSON CONSUMER COPANIES

Classification and recommendation of technical efficacy words

  • Uniform color
  • High transparency

Production method

ActiveUS20110293906A1Uniform colorControlled colour variationIrregular area designLayered product treatmentSurface plateDry powder
Owner:VÄLINGE INNOVATION AB

Indica rice crust producing process

InactiveCN1344509AUniform colorEnsure the original taste and colorFood preparationNutrient contentRice dishes
Owner:汪林

Health-care preserved kumquat and preparation method thereof

InactiveCN103404683AUniform colorFull of organizationConfectionerySweetmeatsEucommia ulmoidesOsmanthus
Owner:张松波

Ce:YAG microcrystalline glass used for white light LED and preparation method of Ce:YAG microcrystalline glass

ActiveCN103183473AUnique material compositionHigh transparencyFluorescenceGlass matrix
Owner:FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products