Preparation method of extracted high-purity molybdenum trioxide

A high-purity molybdenum trioxide technology, which is applied in the field of preparation of high-purity molybdenum trioxide extraction, can solve the problems of environmental protection difficulty, high cost, and large amount of waste gas and waste residue, and achieve environmental friendliness, low energy consumption, and high recovery rate Effect

Inactive Publication Date: 2013-12-18
HUBEI ZHONGAO NANO MATERIAL TECH CO LTD
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the amount of waste gas, waste water and waste residue in the production process is large, and the environmental protection is difficult and expensive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] 1. Industrial molybdic acid pretreatment. The treatment temperature is 750°C to remove moisture and oil in the material, as well as to remove other trace impurities in the material whose volatilization point is below 750°C. The content of molybdenum trioxide in the treated material is above 98%; the impurities in the material are accurately detected;

[0009] 2. According to the sublimation rate, the material is sent into the sublimation furnace. If the material contains calcium metal, the temperature of the sublimation furnace is controlled at 1100°C.

[0010] 3. Choose clean air cooling or liquid nitrogen cooling according to user requirements, and the temperature before the primary dust collection and recovery device is controlled at 250°C or 50°C;

[0011] 4. After primary and secondary gas-solid separation and recovery, the product (nano-scale) high-purity molybdenum trioxide is collected;

[0012] 5. The residue of the sublimation furnace is calculated according ...

Embodiment 2

[0014] 1. Industrial molybdic acid pretreatment. The treatment temperature is 750°C to remove moisture and oil in the material, as well as to remove other trace impurities in the material whose volatilization point is below 750°C. The content of molybdenum trioxide in the treated material is above 98%; the impurities in the material are accurately detected;

[0015] According to the sublimation rate, the material is sent into the sublimation furnace. If the material does not contain metallic calcium, the temperature of the sublimation furnace is controlled at 1160°C.

[0016] 2. Choose clean air cooling or liquid nitrogen cooling according to user requirements, and the temperature before the primary dust collection and recovery device is controlled at 250°C or 50°C;

[0017] 3. After primary and secondary gas-solid separation and recovery, the product (nano-scale) high-purity molybdenum trioxide is collected;

[0018] 4. The residue of the sublimation furnace is calculated ac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of molybdenum trioxide, and specifically relates to a preparation method of extracted high-purity molybdenum trioxide. The preparation method is characterized by comprising the following steps: treating industrial molybdic acid to remove moisture, oil and various trace impurities with a volatilization point lower than 750 DEG C in materials; metering according to sublimation speed for feeding the materials into a subliming furnace, and controlling the temperature of the subliming furnace to 1100 DEG C-1160 DEG C; selectively adopting clean air coiling or liquid nitrogen cooling according to the requirements of the grain size, and controlling the temperature to 250 DEG C or 50 DEG C; collecting the dust by a primary metal membrane for recycling with a yield of 99%, and collecting the dust by a secondary cloth bag with the yield of 1% to recycle high-purity molybdenum trioxide. The technical scheme is adopted, and the subliming furnace is used as a carbon rod for directly heating up, and therefore, the heating efficiency is high, the temperature is controlled by using a computer, and a temperature fluctuation range is +/-1 DEG C. Residues at the furnace bottom are calculated according to material balance and exhausted regularly, and waste of the residues is used as steel-making ferro-molybdenum after being cooled or used as the material for producing sodium molybdate after being crushed. The preparation method disclosed by the invention is safe and reliable in process, high in recovery rate and high in quality, thereby improving production efficiency and relieving labor intensity of operation personnel.

Description

technical field [0001] The invention relates to the field of molybdenum trioxide, and relates to a preparation method for extracting high-purity molybdenum trioxide. Background technique [0002] The method commonly used now is: make fine-quality ammonium molybdate from molybdenum-containing raw materials, and heat and refine ammonium molybdate to produce high-purity molybdenum trioxide. Ammonium molybdate is made from molybdenum concentrate with a molybdenum content of more than 40% through roasting, leaching, impurity removal, concentration, acid precipitation, filtration and other processes. The yield of molybdenum is about 95%. Therefore, the amount of waste gas, waste water and waste residue in the production process is large, and the environmental protection is difficult and expensive. Contents of the invention [0003] The object of the present invention is to propose a method for preparing high-purity molybdenum trioxide with simple process, short time consumption...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01G39/02
CPCY02P20/10
Inventor 陈方吾
Owner HUBEI ZHONGAO NANO MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap