Aerated brick containing asbestos fiber carbide slag composite particles

A technology of asbestos fiber and composite particles, which is applied in the field of aerated bricks, can solve the problems of slow development of aerated bricks and the inability to meet diversified market demands, and achieve good thermal insulation performance, high strength, and good thermal insulation performance. Effect

Inactive Publication Date: 2013-12-18
潘逸东
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing technology of aerated bricks is slow to develop and cannot meet the diversified market demands

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] An aerated brick containing asbestos fiber carbide slag composite particles, which is made from the following raw materials in parts by weight (kg): 0.004 oxidized paraffin wax soap, 0.005 calcium acetate, 3 sodium methylene dibenzoate, silane coupling Agent kh570 0.02, hydroxypropyl methylcellulose 0.002, bentonite 8, hydroxypropyl methylcellulose ether 9, pottery sand 20, sodium lignosulfonate 0.5, triethanolamine 0.8, asbestos fiber carbide slag composite particles 16, zinc Powder 0.06, rapeseed cake powder 0.03, cement 12, raw gypsum 4.

[0015] The aerated brick containing asbestos fiber carbide slag composite particles,

[0016] The preparation method is: (1) Take carbide slag and crush it, soak it in 7% sodium hydroxide solution for 15 hours, take it out, wash it with deionized water, dry it, take it out, pass it through a 100-mesh sieve, and mix it with asbestos fiber by weight 1.6% dioctyl ester, 0.4% nano-carbon, 0.5% epoxy linseed oil, and an appropriate amo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aerated brick containing asbestos fiber carbide slag composite particles. The aerated brick is prepared from the following raw materials in parts by weight: 0.002-0.004 part of oxyparaffin soap, 0.003-0.005 part of calcium acetate, 2-3 parts of methylene sodium dibenzoate, 0.01-0.02 part of silane coupling agent kh570, 0.001-0.002 part of hydroxypropyl methyl cellulose, 7-9 parts of bentonite, 7-9 parts of hydroxypropyl methyl cellulose ester, 10-20 parts of pottery sand, 0.5-0.7 part of sodium lignin sulfonate, 0.4-0.8 part of triethanolamine, 13-16 parts of asbestos fiber carbide slag composite particles, 0.04-0.06 part of zinc powder, 0.01-0.03 part of rape seed cake powder, 9-12 parts of cement and 2-4 parts of gypsum.

Description

technical field [0001] The invention relates to the field of aerated bricks, in particular to an aerated brick containing asbestos fiber carbide slag composite particles. Background technique [0002] Aerated bricks are aerated concrete blocks produced by high-temperature autoclaved equipment. "Aerated brick" can be understood as a simplified or a general name. The range of products it covers should be larger, that is, bricks produced by various other processes including autoclaving. [0003] In the past, the wall materials used in the construction market were mainly red bricks, but now many advanced areas have completely banned the use of red bricks. [0004] The existing technology of aerated bricks is slow to develop and cannot meet the diversified market demands. Contents of the invention [0005] The object of the present invention is to provide an aerated brick containing asbestos fiber carbide slag composite particles. [0006] The above purpose is achieved ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B38/02C04B28/14C04B18/04
CPCY02W30/91
Inventor 潘逸东
Owner 潘逸东